Quenched and tempered high-strength alloy steel 06Ni9DR steel plate used for ultralow-temperature pressure container and preparation method of quenched and tempered high-strength alloy steel 06Ni9DR steel plate

A pressure vessel and ultra-low temperature technology, which is applied in the field of steel plates for pressure vessels and its preparation, can solve the problems of dependence on imports and the difficulty of producing 06Ni9DR steel plates, and achieve the effects of avoiding welding magnetic deflection, good low-temperature performance, and good post-weld performance

Active Publication Date: 2016-10-12
NANYANG HANYE SPECIAL STEEL CO LTD
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the purpose of the present invention is to address the deficiencies of the prior art, to provide a quenched and tempered high-strength alloy steel 06Ni9DR steel plate for ultra-low temperature pressure vessels and its preparation method, which solves the difficulty in the production of domestic 06Ni9DR steel plates, and most of them rely on imports The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quenched and tempered high-strength alloy steel 06Ni9DR steel plate used for ultralow-temperature pressure container and preparation method of quenched and tempered high-strength alloy steel 06Ni9DR steel plate
  • Quenched and tempered high-strength alloy steel 06Ni9DR steel plate used for ultralow-temperature pressure container and preparation method of quenched and tempered high-strength alloy steel 06Ni9DR steel plate
  • Quenched and tempered high-strength alloy steel 06Ni9DR steel plate used for ultralow-temperature pressure container and preparation method of quenched and tempered high-strength alloy steel 06Ni9DR steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031]A quenched and tempered high-strength alloy steel 06Ni9DR steel plate for ultra-low temperature pressure vessels, including the following chemical components in mass percentages (unit, wt%): C: 0.01, Si: 0.20, Mn: 0.50, P: 0.006, S: 0.002, Ni : 8.5, Cu: 0.10, Mo: 0.01, V: 0.005, Cr: 0.10, Als: 0.015, N: 0.012, and the balance is Fe and unavoidable impurities.

[0032] Wherein, the carbon equivalent of the alloy steel plate [Ceq=C+Mn / 6+(Cr+V+Mo) / 5+(Cu+Ni) / 15]=0.10%, and the thickness of the steel plate is 12mm.

[0033] Its preparation method comprises the following steps:

[0034] (1) KR hot metal pretreatment: use the ladle to carry the hot metal, remove the former slag from the hot metal at the station, control the content of P and S in the hot metal, after the hot metal is stirred and desulfurized by KR, the hot metal P≤0.1%, S≤0.004%, and the desulfurization cycle≤25min , desulfurization temperature drop ≤ 20 ℃; after desulfurization is completed, the slag layer is ...

Embodiment 2

[0047] A quenched and tempered high-strength alloy steel 06Ni9DR steel plate for ultra-low temperature pressure vessels, including the following chemical components in mass percentages (unit, wt%): C: 0.03, Si: 0.14, Mn: 0.69, P: 0.005, S: 0.001, Ni : 9.4, Cu: 0.01, Mo: 0.01, V: 0.003, Cr: 0.25, Als: 0.020, N: 0.00189, and the balance is Fe and unavoidable impurities.

[0048] Wherein, the carbon equivalent of the alloy steel plate [Ceq=C+Mn / 6+(Cr+V+Mo) / 5+(Cu+Ni) / 15]=0.50%, and the thickness of the steel plate is 40mm.

[0049] Its preparation method comprises the following steps:

[0050] (1) KR hot metal pretreatment: use the ladle to carry the hot metal, remove the former slag from the hot metal at the station, control the content of P and S in the hot metal, after the hot metal is stirred and desulfurized by KR, the hot metal P≤0.1%, S≤0.004%, and the desulfurization cycle≤25min , desulfurization temperature drop ≤ 20 ℃; after desulfurization is completed, the slag layer ...

Embodiment 3

[0063] A quenched and tempered high-strength alloy steel 06Ni9DR steel plate for ultra-low temperature pressure vessels, including the following chemical components in mass percent (unit, wt%): C: 0.03, Si: 0.14, Mn: 0.68, P: 0.005, S: 0.001, Ni : 9.4, Cu: 0.09, Mo: 0.01, V: 0.003, Cr: 0.20, Als: 0.020, N: 0.00195, and the balance is Fe and unavoidable impurities.

[0064] Wherein, the carbon equivalent of the alloy steel plate [Ceq=C+Mn / 6+(Cr+V+Mo) / 5+(Cu+Ni) / 15]=0.15%, and the thickness of the steel plate is 50mm.

[0065] Its preparation method comprises the following steps:

[0066] (1) KR hot metal pretreatment: use the ladle to carry the hot metal, remove the former slag from the hot metal at the station, control the content of P and S in the hot metal, after the hot metal is stirred and desulfurized by KR, the hot metal P≤0.1%, S≤0.004%, and the desulfurization cycle≤25min , desulfurization temperature drop ≤ 20 ℃; after desulfurization is completed, the slag layer is s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a quenched and tempered high-strength alloy steel 06Ni9DR steel plate used for an ultralow-temperature pressure container and a preparation method of the quenched and tempered high-strength alloy steel 06Ni9DR steel plate. The steel plate comprises, by mass percent, 0.01 wt%-0.06 wt% of C, 0.10 wt%-0.20 wt% of Si, 0.50 wt%-0.80 wt% of Mn, smaller than or equal to 0.008 wt% of P, smaller than or equal to 0.002 wt% of S, 8.5 wt%-9.5 wt% of Ni, smaller than or equal to 0.10 wt% of Cu, smaller than or equal to 0.10 wt% of Mo, smaller than or equal to 0.005 wt% of V, smaller than or equal to 0.25 wt% of Cr and the balance Fe and inevitable impurities. According to the quenched and tempered high-strength alloy steel 06Ni9DR steel plate used for the ultralow-temperature pressure container, by means of the reasonable chemical component design, the cleanliness synergistic and effective process of steel is effectively implemented through the RH+LF+RH process, and the prepared steel plate has the beneficial effects of being high in strength, excellent in low-temperature tenacity, good in post-welding performance, and the like.

Description

technical field [0001] The invention relates to a steel plate for pressure vessels and a preparation method thereof, in particular to a quenched and tempered high-strength alloy steel 06Ni9DR steel plate for ultra-low temperature pressure vessels and a preparation method thereof. Background technique [0002] 06Ni9DR steel is commonly known as 9% Ni steel, Ni9 steel, 9Ni steel, etc. It is a quenched and tempered high-strength alloy steel for ultra-low temperature storage tanks and pressure vessels containing 8.5-9.5% Ni. It is an important structural material for ultra-low temperature equipment and containers. Used to manufacture or construct liquid nitrogen and natural gas (Liquefied Natural Gas: LNG for short) storage tanks. For example, LNG ships for liquefied natural gas and storage tanks for storing liquefied natural gas will use a large amount of low-temperature steel 06Ni9DR. It has the characteristics of high yield strength and tensile strength, good low-temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/16C22C38/18C21D8/02
CPCC21D8/0226C21D8/0247C22C38/001C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/16C22C38/18
Inventor 康文举
Owner NANYANG HANYE SPECIAL STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap