Low-VOC polypropylene composite material and preparation method thereof

A composite material and polypropylene technology, applied in the field of low-VOC polypropylene composite materials, composite material preparation, and polypropylene composite materials, can solve the problems of high cost and less research on adsorption, and achieve cost reduction and easy batch production Good production and adsorption effect

Inactive Publication Date: 2016-10-26
SHANGHAI PRET COMPOSITES
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adsorption of organic volatiles in plastics is less studied.
[0005] Under the existing technology, the low-VOC modification of polypropylene is mostly achieved by adding the adsorption effect of synthetic molecular sieves, which is costly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-VOC polypropylene composite material and preparation method thereof
  • Low-VOC polypropylene composite material and preparation method thereof
  • Low-VOC polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Weigh 74.5% of polypropylene, 15% of talc, 5% of POE 8180, 5% of calcined diatomite, 0.1% of Irganox 1010, 0.1% of Igrafos 168, and 0.3% of Negonox DSTP in a high-speed mixer Medium-dry mixing for 5 minutes, the mixed raw materials are fed into the twin-screw extruder from the main feeding port at the end of the screw to melt and extrude to granulate. 220°C, 220°C in the fourth zone, 210°C in the head, and the speed of the twin-screw extruder is 500 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

Embodiment 2

[0034] Weigh 69.5% of polypropylene, 15% of talc, 5% of POE 8180, 10% of calcined diatomite, 0.1% of Irganox 1010, 0.1% of Igrafos 168, and 0.3% of Negonox DSTP in a high-speed mixer Medium-dry mixing for 5 minutes, the mixed raw materials are fed into the twin-screw extruder from the main feeding port at the end of the screw to melt and extrude to granulate. 220°C, 220°C in the fourth zone, 210°C in the head, and the speed of the twin-screw extruder is 500 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

Embodiment 3

[0036] Weigh 64.5% of polypropylene, 15% of talc, 5% of POE 8180, 15% of calcined diatomite, 0.1% of Irganox 1010, 0.1% of Igrafos 168, and 0.3% of Negonox DSTP in a high-speed mixer Medium-dry mixing for 5 minutes, the mixed raw materials are fed into the twin-screw extruder from the main feeding port at the end of the screw to melt and extrude to granulate. 220°C, 220°C in the fourth zone, 210°C in the head, and the speed of the twin-screw extruder is 500 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-VOC polypropylene composite material and a preparation method thereof. The low-VOC polypropylene composite material comprises the following raw materials by weight: 45 to 79.5% of polypropylene, 12 to 30% of an inorganic filling material, 3 to 7% of a flexibilizer, 5 to 15% of calcined diatomite, 0.2 to 2% of a stabilizing agent and 0 to 5% of other additives. The invention has the advantages that 1, since the calcined diatomite is used as a VOC adsorbent of the polypropylene composite material, emission of VOCs can be greatly reduced, and the preparation method is simple and can easily realize batch production; and 2, compared with other molecular-sieve synthetic adsorbents, the calcined diatomite is greatly reduced in cost and good in adsorption effect.

Description

technical field [0001] The invention relates to a polypropylene composite material, specifically a low-VOC polypropylene composite material, and a preparation method of the composite material, belonging to the field of polymer modification and processing. Background technique [0002] VOC refers to volatile organic compounds, VOC is volatile organic compounds, which have a huge impact on human health. When the VOC in the room reaches a certain concentration, people will feel headache, nausea, vomiting, fatigue, etc. in a short time. decline and other serious consequences. As people pay more attention to indoor and in-vehicle air quality, my country has issued indoor and in-vehicle air quality standards, mainly including the content limits of benzene and aldehydes and ketones. [0003] Polypropylene has good processing performance, physical and chemical properties, extremely low density, and relatively low price, and is widely used in household appliances, automobiles and o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/00C08L23/08C08K13/02C08K3/34
CPCC08L53/00
Inventor 陈勇张鹰张祥福周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap