Environment-friendly and flame-retardant waterproof agent for leather and preparation method for waterproof agent

A water-repellent and environmentally friendly technology, applied in leather surface treatment, small raw hide/big raw hide/leather/fur treatment, small raw hide/large raw hide/leather skin/fur chemical treatment, etc., can solve long reaction time and complicated manufacturing process and other problems, to achieve the effect of simple polymerization process, good waterproof performance and long-lasting waterproof performance

Inactive Publication Date: 2016-11-09
广州双桃精细化工有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With this preparation method, the manufacturing process is more complicated and requires a longer reaction time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly and flame-retardant waterproof agent for leather and preparation method for waterproof agent
  • Environment-friendly and flame-retardant waterproof agent for leather and preparation method for waterproof agent
  • Environment-friendly and flame-retardant waterproof agent for leather and preparation method for waterproof agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] In a four-necked flask equipped with a stirrer, a thermometer, and a reflux tube, mix 2g of BPO initiator, 5g of acrylamide, 20g of vinyl silicone oil (1000cp), 6g of vinyl chloride propylene, 40g of octadecyl acrylate with 100g of solvent (a blend of ethyl acetate 50g and butyl acetate 50g) mixed evenly, and added dropwise to the reaction vessel at 80°C for 4 hours, then added 29g of dodecafluoroheptyl acrylate dropwise for 1 hour, and finally mechanically stirred and kept for reaction After 5 hours, a uniform solution viscous substance was obtained, which was the environmentally friendly flame-retardant and water-repellent agent for leather. After standing for two months, the solution does not stratify and has good stability. Take the waterproofing agent and bake it at 100°C for 4 hours without yellowing. Ignite the dried waterproofing agent with an open flame and remove the fire source. It has a certain flame retardant performance. Apply the water repellent solution...

Embodiment 2

[0030] In a four-necked flask equipped with a stirrer, a thermometer, and a reflux tube, 1.5g AIBN initiator, 15g hydroxyethyl acrylate, 10g vinyl silicone oil (1500cp), 3g vinylidene chloride propylene monomer, 50g hexadecane acrylate Mix 100g solvent (butanone) and 100g solvent (butanone) evenly, add dropwise to the reaction vessel at 90°C for 2 hours, then add 22g dodecafluoroheptyl acrylate dropwise for 2 hours, and finally mechanically stir and keep warm for 3 hours to obtain a uniform The solution viscous is the environmentally friendly flame retardant waterproofing agent for leather. After standing for two months, the solution does not stratify and has good stability. Take the waterproofing agent and bake it at 100°C for 4 hours without yellowing. Ignite the dried waterproofing agent with an open flame and remove the fire source. It has a certain flame retardant performance. Apply the water repellent solution to the leather finishing agent 2060E, add 2 g of water repel...

Embodiment 3

[0032] In a four-necked flask equipped with a stirrer, a thermometer, and a reflux tube, mix 1.5g of BPO initiator, 6g of hydroxypropyl acrylate, 12g of vinyl silicone oil (500cp), 4g of vinyl chloride, 60g of dodecyl acrylate with 100g The solvent (a blend of butanone 50g and butyl acetate 50g) was mixed evenly, and added dropwise to the reaction vessel at 85°C for 3 hours, then 18g of hexafluorobutyl acrylate was added dropwise for 1.5 hours, and finally mechanically stirred and kept for 4 hours. Finally, obtain a uniform solution viscous substance, which is the environmentally friendly flame-retardant and water-repellent agent for leather. After standing for two months, the solution does not stratify and has good stability. Take the waterproofing agent and bake it at 100°C for 4 hours without yellowing. Ignite the dried waterproofing agent with an open flame and remove the fire source. It has a certain flame retardant performance. Apply the water repellent solution to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of leather finishing agents, and discloses an environment-friendly and flame-retardant waterproof agent for leather and a preparation method for the waterproof agent. The preparation method comprises the following steps: uniformly mixing an initiator, an acrylic ester monomer, vinyl silicone oil, a flame-retardant allyl vinyl monomer, a long-chain alkyl acrylate monomer and a solvent according to a proportion, adding dropwise a mixed solution into an 80 to 90 DEG C reactor for 2 to 4h, adding dropwise a fluorinated acrylate monomer for 1 to 2h, performing mechanical stirring and heat-preservation reaction for 3 to 5h, and performing cooling to obtain the environment-friendly and flame-retardant waterproof agent for the leather. The obtained waterproof agent is free of yellowing and demixing and high in stability; a formed waterproof agent film is flame-retardant, resistant to alcohol rubbing and persistent in waterproof performance, and has good application and environmental protection prospect, and a production process is simple.

Description

technical field [0001] The invention belongs to the field of leather finishing agents, and in particular relates to an environmentally friendly flame-retardant and water-repellent agent for leather and a preparation method thereof. Background technique [0002] With the improvement of people's consumption concept and consumption level, people place higher requirements on leather. In addition to keeping warm and covering the body, it should also be beautiful and comfortable. Environmental protection, flame retardancy and other functions. The current market waterproofing agents have problems such as poor stability and easy delamination. Some waterproofing agents contain PFOS / PFOA and other ingredients that are harmful to the human body and the environment, and are also bioaccumulative. Therefore, the new environmentally friendly and stable waterproofing agent has become a product with great development prospects in the current market. [0003] Fluorine-containing acrylate co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/07C09D5/18C14C11/00
CPCC09D183/04C09D5/18C14C11/003
Inventor 武慧玲唐强熊满军王刚欧建成
Owner 广州双桃精细化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap