Lubricating oil with modified graphene and good dispersibility and method for preparing lubricating oil

A dispersive performance, graphene technology, applied in the petroleum industry, lubricating compositions, additives, etc., can solve the problems of poor stability of lubricating oil and reduced lubricating performance of lubricating oil, and achieve lubricating performance improvement, performance improvement, and less addition Effect

Inactive Publication Date: 2016-12-07
CHONGQING DELING TECH
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although the use of graphene can improve the lubricating performance of the lubricating oil to a certain extent, the stability of the lubricating oil obtained is poor, and agglomerates will be formed after a long period of storage, which will reduce the lubricating performance of the lubricating oil.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lubricating oil with modified graphene and good dispersibility and method for preparing lubricating oil
  • Lubricating oil with modified graphene and good dispersibility and method for preparing lubricating oil
  • Lubricating oil with modified graphene and good dispersibility and method for preparing lubricating oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The modified graphene lubricating oil with good dispersibility comprises the following components in parts by weight: 0.3 part of 3-propylaminoethoxysilane graphene, 0.5 part of stearic acid and 100 parts of mineral base oil.

[0031] The preparation method of modified graphene lubricating oil with good dispersibility comprises the steps:

[0032] (1) 3-propylaminoethoxysilane graphene and stearic acid are added step by step in the mineral base oil according to the proportion, and stirred evenly to obtain the mixture;

[0033] (2) The mixture obtained in step (1) was mechanically stirred for 1 hour, and then treated with a rubber mill to obtain a modified graphene lubricating oil with good dispersibility.

[0034] In this embodiment, the particle size of the 3-propylaminoethoxysilane graphene is controlled to be 50-80 nm.

Embodiment 2

[0036] The modified graphene lubricating oil with good dispersibility comprises the following components in parts by weight: 1.5 parts of 3-propylaminomethoxysilane graphene, 0.3 parts of sodium dodecylbenzenesulfonate and 100 parts of synthetic base oil .

[0037] The preparation method of modified graphene lubricating oil with good dispersibility comprises the steps:

[0038] (1) 3-propylaminomethoxysilane graphene and sodium dodecylbenzenesulfonate are added step by step in the synthetic base oil according to the ratio, and stirred evenly to obtain a mixture;

[0039] (2) The mixture obtained in step (1) was mechanically stirred for 1.5 hours, and then treated with a rubber mill to obtain a modified graphene lubricating oil with good dispersibility.

[0040] In this embodiment, the particle size of the 3-propylaminomethoxysilane graphene is controlled to be 50-80 nm.

Embodiment 3

[0042] The modified graphene lubricating oil with good dispersibility comprises the following components in parts by weight: 0.5 parts of N-aminoethyl-3-aminopropyltrimethoxysilane graphene, 1.2 parts of fatty acid glycerides and vegetable oil base oil 100 copies.

[0043] The preparation method of modified graphene lubricating oil with good dispersibility comprises the steps:

[0044] (1) N-aminoethyl-3-aminopropyltrimethoxysilane graphene and fatty acid glyceride are added step by step in the vegetable oil base oil according to the ratio, and stirred evenly to obtain a mixture;

[0045] (2) The mixture obtained in step (1) was mechanically stirred for 3 hours, and then treated with a rubber mill to obtain a modified graphene lubricating oil with good dispersibility.

[0046] In this embodiment, the particle size of the N-aminoethyl-3-aminopropyltrimethoxysilane graphene is controlled to be 50-80 nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses lubricating oil with modified graphene and good dispersibility and a method for preparing the lubricating oil. The lubricating oil with the modified graphene comprises, by weight, 0.3-1.5 parts of modified graphene oxide, 0.3-1.5 parts of dispersing agents and 100 parts of base oil. The lubricating oil and the method have the advantages that formulas are reasonable, the method is simple, the prepared lubricating oil is good in stability and ultra-strong in lubricity and anti-attrition property, the lubricating properties can be enhanced, movement resistance can be reduced when the lubricating oil is used in mechanical movement, friction coefficients can be lowered, the service lives of mechanical components can be prolonged, and energy can be saved; the lubricating oil can be widely applied to various mechanical components, and accordingly the lubricating oil and the method have huge market potential and broad market prospects.

Description

technical field [0001] The invention belongs to the field of macromolecules and their applications, and in particular relates to a modified graphene lubricating oil with good dispersion performance, and also relates to a preparation method of the graphene lubricating oil. Background technique [0002] Friction and wear are ubiquitous in nature, causing more than 50% of the world's primary energy loss due to friction and wear, and wear is one of the main reasons for the scrapping of materials and equipment. In order to reduce friction and wear, people add lubricating oil between workpieces, but the economic loss of tens of billions of yuan is still caused to the country every year due to friction and wear. Therefore, reducing friction, reducing wear, reducing wear, and prolonging the life of parts are the goals that researchers in tribology, chemistry and materials are constantly pursuing. In order to improve the lubricating performance of lubricating oil, various anti-wear ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M125/02C10M139/04C10M169/04C10N10/02C10N10/04C10N30/06
CPCC10M125/02C10M139/04C10M169/04C10M2201/041C10M2207/024C10M2207/026C10M2207/126C10M2207/283C10M2209/104C10M2215/042C10M2219/044C10M2219/068C10M2227/04C10N2010/02C10N2010/04C10N2030/06C10N2030/72
Inventor 罗廷军
Owner CHONGQING DELING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products