Lithium-battery 8021 soft packaging aluminum foil and production method thereof

A production method and technology for lithium batteries, applied in the field of aluminum alloys, can solve problems such as poor product quality stability, difficult material manufacturing, and lithium battery fluid leakage, achieve good sealing, eliminate ingot component segregation, and improve grain structure. performance effect

Active Publication Date: 2016-12-07
HENAN MINGTAI AL INDUSTRIAL CO LTD
View PDF6 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the difficulty of material manufacturing and poor product quality stability, 8021 lithium battery soft pack products produced in Japan are currently mainly used in China. Domestic materials have defects such as high strength, low elongation, surface stripes, excessive pinholes, and low cup convexity. Eliminate quality problems such as lithium battery fluid leakage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium-battery 8021 soft packaging aluminum foil and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of 8021 soft package aluminum foil for lithium battery, the mass percent of each element in the described aluminum foil is as follows:

[0041] Si is 0.09%, Fe=1.4%, Cu is 0.04%, Mn is 0.04%, Mg is 0.04%, Cr is 0.04%, Zn is 0.03%, Ti=0.02%, and the rest is Al.

Embodiment 2

[0043] A kind of 8021 soft package aluminum foil for lithium battery, the mass percent of each element in the described aluminum foil is as follows:

[0044] Si is 0.08%, Fe=1.45%, Cu is 0.03%, Mn is 0.03%, Mg is 0.04%, Cr is 0.03%, Zn is 0.04%, Ti=0.025%, and the rest is Al.

Embodiment 3

[0046] A kind of 8021 soft package aluminum foil for lithium battery, the mass percent of each element in the described aluminum foil is as follows:

[0047] Si is 0.06%, Fe=1.5%, Cu is 0.02%, Mn is 0.02%, Mg is 0.03%, Cr is 0.02%, Zn is 0.02%, Ti=0.03%, and the rest is Al.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses lithium-battery 8021 soft packaging aluminum foil and a production method thereof. Aluminum alloy containing Si, Fe, Cu, Mn, Mg, Cr, Zn, Ti and the balance Al is smelted and subjected to ingot casting, then an ingot is subjected to surface milling and soaking treatment; and the lithium-battery 8021 soft packaging aluminum foil is obtained after the steps of hot rolling, cold rolling, annealing, foil rolling, roll combining, combined roll annealing and roll dividing. The lithium-battery 8021 soft packaging aluminum foil prepared through the good technological process is a finished product in the O state, the ductility reaches 18-20%, the cupping value is larger than or equal to 7 mm, and the fracture resistance, stamping resistance and the like of the soft packaging aluminum foil are effectively improved. The aluminum foil has no holes or pinholes completely, so that a lithium battery soft package prepared from the aluminum foil has good airtightness and is free of liquid leakage and safe to use. The lithium-battery 8021 soft packaging aluminum foil has good social and economical benefits and broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloys, and in particular relates to an 8021 soft-wrapped aluminum foil for lithium batteries and a production method thereof. technical background [0002] Aluminum foil has the characteristics of light material, high barrier property, shading, anti-ultraviolet, moisture-proof, anti-corrosion, heat insulation, long shelf life, clean and hygienic, etc. In deep processing and utilization, it has the characteristics of easy bending, excellent adhesion and heat sealing performance, and excellent surface printing performance and decorative effect. Therefore, aluminum foil is an excellent packaging material and has broad application prospects in the packaging industry. Moreover, the one-time consumption of aluminum foil is produced, and the market demand is large. [0003] According to statistics, more than 70% of aluminum foil in Europe is used in various packaging products. In the United States, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C1/06C22F1/04H01M2/02
CPCC22C1/06C22C21/00C22F1/04H01M50/116Y02E60/10
Inventor 李国锋何延武李发辉
Owner HENAN MINGTAI AL INDUSTRIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com