Preparation technology for one-component thermoplastic acrylic acid middle coating
A thermoplastic acrylic acid and preparation process technology, applied in the coating and other directions, can solve the problems of insufficient coating hardness, poor wear resistance and scratch resistance, etc., and achieve the effect of good wear resistance and scratch resistance and high hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0065] According to the mass ratio, the ingredients are as follows:
[0066] Thermoplastic Acrylic 72%
[0067] 15% polyamide wax paste 3%
[0068] Dispers610s dispersant 0.2%
[0069] EFKA-360 leveling agent 0.2%
[0070] EFKA-3033 leveling agent 0.3%
[0071] BYK-066N defoamer 0.3%
[0072] Trimethylbenzene 5%
[0074] n-Butyl acetate 0.5%
[0075] MIBK 3%
[0076] 1130 Light Stabilizer Light Stabilizer 1%
[0077] 292 light stabilizer 1%
[0078] n-Butyl acetate 10%.
[0079] In step C, the rotating speed is 600r / min; in step D, the rotating speed is 800r / min; in step E, the rotating speed is 1500r / min; in step F, the rotating speed is 1200r / min; 25°C.
Embodiment 2
[0081] According to the mass ratio, the ingredients are as follows:
[0082] Thermoplastic acrylic resin 81.75%
[0083] 15% polyamide wax paste 2%
[0084] Dispers610s dispersant 0.5%
[0085] EFKA-360 leveling agent 0.05%
[0086] EFKA-3033 leveling agent 0.1%
[0087] BYK-066N defoamer 0.1%
[0088] Trimethylbenzene 2%
[0090] n-Butyl acetate 0.5%
[0091] MIBK 1%
[0092] 1130 Light Stabilizer Light Stabilizer 0.5%
[0093] 292 light stabilizer 0.5%
[0094] n-Butyl acetate 9%.
[0095] In step C, the rotating speed is 800r / min, in step D, the rotating speed is 600r / min, in step E, the rotating speed is 1200r / min, in step F, the rotating speed is 800r / min, and the coating-4 cup viscosity: 20s / 25°C.
Embodiment 3
[0097] According to the mass ratio, the ingredients are as follows:
[0098] Thermoplastic Acrylic 77.5%
[0099] 15% polyamide wax paste 2.5%
[0100] Dispers610s dispersant 0.4%
[0101] EFKA-360 leveling agent 0.1%
[0102] EFKA-3033 leveling agent 0.2%
[0103] BYK-066N defoamer 0.2%
[0104] Trimethylbenzene 4%
[0106] n-Butyl acetate 0.5%
[0107] MIBK 2%
[0108] 1130 Light Stabilizer Light Stabilizer 0.8%
[0109] 292 light stabilizer 0.8%
[0110] n-Butyl acetate 8%.
[0111] In step C, the rotating speed is 700r / min; in step D, the rotating speed is 700r / min; in step E, the rotating speed is 1400r / min; in step F, the rotating speed is 1000r / min; 25°C.
[0112] The intermediate coating primer prepared by the above process is uniformly dispersed until the fineness is ≤35um, and the coating-4 cup viscosity: 20s~30s / 25℃. It has the characteristics of high hardness, good wear resistance and scratch resistance, and can better meet the...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com