High-carbon steel wire rod inclusion control method

A control method and inclusion technology, applied in the field of high-carbon steel, can solve the problems of damage to the processing performance of high-carbon steel wire rods, poor deformability, etc., and achieve the effect of improving processing performance and preventing the formation of micro-cracks

Inactive Publication Date: 2017-01-11
ANGANG STEEL CO LTD
View PDF7 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the processing performance of high-carbon steel, the invention has done work on the control of the structure of the wire rod and the control of inclusions, and it is mentioned that the control of the sulfide spacing is beneficial to the processing performance of the wire rod, but the invention obviously does not mention How to control the hazards of oxide inclusions, if there are oxide inclusions with large size and poor deformability in steel, it will inevitably greatly damage the processing performance of high carbon steel wire rods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-carbon steel wire rod inclusion control method
  • High-carbon steel wire rod inclusion control method
  • High-carbon steel wire rod inclusion control method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] Below by embodiment the present invention will be further described.

[0019] In the embodiment of the present invention, converter, LF refining, continuous casting and rolling are carried out according to the component distribution ratio of the technical solution. The chemical composition of the steel of the embodiment of the present invention is shown in Table 1. The main process parameters and inclusion detection results of the steel in the embodiment of the present invention are shown in Table 2.

[0020] The chemical composition of the high carbon steel wire rod applicable to the present invention is: [C]: 0.60%~0.95%, [Mn]: 0.30%~0.60%, [Si]: 0.10%~0.40%, [P]≤0.010%, 0.016%≤[S]≤0.025%, [Ti]≤0.0010%, full aluminum: 0.0005%-0.0020%, full oxygen: 0.0015%-0.0025%.

[0021] Table 1 The chemical composition (wt%) of the embodiment steel of the present invention

[0022] Example C，％ Si,% Mn, % P，％ S，％ All aluminum, % Total oxygen, % Ti, % 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-carbon steel wire rod inclusion control method. The method comprises converter treatment, refining, continuous casting, continuous rolling and wire rod rolling. In converter treatment, high-carbon steel is produced and after converter treatment, silicomanganese deoxidation is carried out. A LF refining temperature is in a range of 1550-1640 DEG C, refining time is in a range of 60-80min, sulfur content of a steel liquid at the refining finished point is in a range of 0.016-0.025%, oxygen activity is in a range of (10-30)*10<-6>, steel liquid acid-insoluble aluminum content is in a range of 0.0005-0.0025% and titanium content is less than or equal to 0.0010%. In continuous rolling and wire rod rolling, the steel wire rod diameter is in a range of 5-5.5mm, a spinning temperature is in a range of 880-910 DEG C and after spinning, a steel wire rod is fast cooled to 600-650 DEG C. The high-carbon steel wire rod obtained by the method contains fine oxide impurities. In steel wire rod drawing, the sulfide inclusion outside the oxide inclusion can cooperate with matrix deformation so that micro-cracks at two ends of the oxide impurity are prevented and finished product processing performances are improved.

Description

technical field [0001] The invention belongs to the field of high-carbon steel, and in particular relates to a method for controlling inclusions of high-carbon steel wire rods. Background technique [0002] With the rapid development of the automobile and other equipment manufacturing industries, and for weight reduction and safety considerations, wire products show an obvious trend of high strengthening. At present, the single filament strength can reach up to 4000MPa or more, but to obtain such a high strength, in addition to carrying out In addition to the composition adjustment, higher requirements are also placed on the processing performance of the wire rod. In order to improve the processing performance of high-carbon steel wire rod, the most common method is to take measures to refine the structure of the wire rod and modify the non-metallic inclusions in the steel to improve the deformability of the inclusions. In terms of inclusion control in high carbon steel for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/04C21C7/06C21C5/28
Inventor 高航郭大勇王秉喜马立国郭晓波王宁罗建华任玉辉其他发明人请求不公开姓名
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap