High strength abrasion-resistant concrete

A concrete and high-strength technology, applied in the field of concrete, can solve the problems of shortened service life and accelerated concrete failure, and achieve the effects of high wear-resistant service life, good water resistance and oil resistance

Inactive Publication Date: 2017-01-18
XINJIANG YUXIN CONCRETE
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing concrete is a heterogeneous porous material. Under the erosion of carbon dioxide, water, chloride ions, sulfate and other media, it will inevitably be corroded by external factors, and the concrete will be destroyed at an accelerated rate, and the service life will be greatly improved. To solve this problem, the applicant of this patent researched and developed a wear-resistant concrete with high hardness, high wear resistance and long service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Example 1: Steel slag is composed of steel slag with a particle size of 0.6mm, steel slag with a particle size of 0.28mm, steel slag with a particle size of 0.08mm and steel slag with a particle size of 0.07mm, and the mass ratio is 1:0.68:0.56:0.31 , The reason why such a gradation is used can minimize the porosity in the concrete, thereby improving the wear resistance of the concrete.

Embodiment 2

[0011] Example 2: Steel slag is composed of steel slag with a particle size of 0.58mm, steel slag with a particle size of 0.3mm, steel slag with a particle size of 0.076mm and steel slag with a particle size of 0.075mm, and the mass ratio is 1:0.68:0.56:0.31 .

Embodiment 3

[0012] Example 3: Steel slag is composed of steel slag with a particle size of 0.45mm, steel slag with a particle size of 0.3mm, steel slag with a particle size of 0.1mm and steel slag with a particle size of 0.065mm, and the mass ratio is 1:0.68:0.56:0.31

[0013] When the concrete of the present invention is made, the above-mentioned materials are firstly shaken and smoothed, then sprayed with a curing agent (or covered with film plastic), the process cycle is kept at about 2-3 days, and finally it is formed by stirring with a mixer Stirring time was kept at 45s / square.

[0014] The effects achieved by the present invention are as follows: 1. The formed floor has high hardness, good wear resistance, and can withstand heavy pressure and impact. 2. No sand, no dust, keep the floor clean. 3. The surface is smooth and bright, and the anti-slip effect is good. 4. Excellent water resistance and oil resistance, suitable for various dry and wet internal and external environments. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high strength abrasion-resistant concrete, in particular to a concrete for construction. The high strength abrasion-resistant concrete provided by the invention is composed of steel slag, a cementitious material, water and a water reducing agent, wherein the cementitious material consists of cement accounting for 45% of the mass of the cementitious material, mineral powder accounting for 20% of the mass of the cementitious material, and silicon carbide accounting for 5% of the mass of the cementitious material. The steel slag and the cementitious material are in a mass ratio of 1.67:1, and the water and the cementitious material are in a mass ratio of 0.2:1. The concrete made by the invention has the advantages of high hardness and high abrasion resistance, also has good water resistance and oil resistance, and is suitable for various dry and wet internal and external environments.

Description

technical field [0001] The invention relates to a concrete, especially a high-strength wear-resistant concrete. Background technique [0002] Concrete is a general term for engineering composite materials in which aggregates are cemented into a whole by cementitious materials. Generally speaking, the term concrete refers to the cement concrete obtained by using cement as the cementitious material, sand and stone as the aggregate; mixed with water (may contain admixtures and admixtures) in a certain proportion, and stirred. Concrete, which is widely used in civil engineering. However, the existing concrete is a heterogeneous porous material. Under the erosion of carbon dioxide, water, chloride ions, sulfate and other media, it will inevitably be corroded by external factors, and the concrete will be destroyed at an accelerated rate, and the service life will be greatly improved. To solve this problem, the applicant of this patent researched and developed a wear-resistant co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B111/20
Inventor 张建王建军
Owner XINJIANG YUXIN CONCRETE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com