A steel rolling production line that can realize the controlled cooling requirements of various alloy steel bars after rolling

An alloy steel bar and production line technology, applied in metal rolling, metal rolling, temperature control and other directions, can solve the problems of difficulty in meeting the production process requirements of various types of steel, difficulty in maintenance, and increasing the passing time of steel, and achieve equipment The structure is simple and reliable, and the effect of increasing the collection temperature and shortening the cooling time

Active Publication Date: 2018-03-06
BEIJING JINGCHENG RUIXINCHANGCAI ENG TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the layout of the post-rolling area of ​​the current long steel rolling workshop is relatively simple, and it is difficult to meet the production process requirements of various steel types. The main shortcomings are as follows:
[0003] 1. The existing steel rolling production line is equipped with a water cooling box 2, a cooling bed 5, a cut-to-length saw (including the first saw 6, the second saw 7, the third saw 8 and the fourth saw 9), and a collection table in the post-rolling area devices such as figure 1 As shown), the high-temperature slow-cooling material and the low-temperature slow-cooling material both adopt the same process route, but the process layout and equipment structure design are mainly to meet the requirements of cooling to low temperature, and it is difficult to take into account the requirements of high-temperature slow cooling temperature
[0004] 2. Some production lines have added a chain device that can move quickly across the cooling bed, but the structure of the cooling bed is complicated, the failure rate is high, and maintenance is difficult, and the actual utilization rate is not high in the end.
[0005] 3. In order to achieve a higher hourly output, 4 fixed-length saws are installed behind the cooling bed to cut to fixed lengths. However, the arrangement of the sawing area is too long, which increases the passage time of steel materials and cannot meet the requirements of high-temperature slow-cooled materials for collection temperature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A steel rolling production line that can realize the controlled cooling requirements of various alloy steel bars after rolling
  • A steel rolling production line that can realize the controlled cooling requirements of various alloy steel bars after rolling
  • A steel rolling production line that can realize the controlled cooling requirements of various alloy steel bars after rolling

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] It should be noted that, in the case of no conflict, the embodiments in the present application and the features in the embodiments can be combined with each other. The present invention will be described in detail below with reference to the accompanying drawings and examples.

[0040] A steel rolling production line that can realize the controlled cooling requirements after rolling of various alloy steel bars, including a rolling mill 1, a double-scale flying shear 3, a cooling bed 5, a first saw 6 and a second saw 7 connected in sequence, which can realize multiple The rolling production line required for controlled cooling after rolling of various alloy steel bars also includes a hot bed 4 for moving and cooling the rolled piece 12, and the temperature drop of the rolled piece 12 on the hot bed 4 is smaller than that of the rolled piece 12 on the cooling bed 5 Amplitude, the hot bed 4 contains input roller table 41, traverse trolley 44 and output roller table 47, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a rolled steel production line capable of meeting after-rolling cooling control requirements of multiple alloy steel bars. The rolled steel production line comprises a rolling mill (1), double-rule flying shears (3), a hot bed (4), a cold bed (5), a first saw (6) and a second saw (7); the temperature lowering amplitude of a rolled piece (12) on the hot bed (4) is smaller than that of the rolled piece (12) on the cold bed (5), the hot bed (4) comprises an input roller way (41), a transverse travel trolley (44) and an output roller way (47), the input roller way (41) of the hot bed (4) is located between the double-rule flying shears (3) and the cold bed (5), and the output roller way (47) of the hot bed (4) is located between the first saw (6) and the second saw (7). According to the rolled steel production line capable of meeting the after-rolling cooling control requirements of multiple alloy steel bars, not only can the requirements of a high-temperature slow cooling material on the high collecting temperature be met, but also the high-yield requirement of a low-temperature slow cooling material and the high-yield requirement of a conventional cooling material are both taken into account.

Description

technical field [0001] The invention relates to the field of steel rolling equipment, in particular to a steel rolling production line capable of realizing the requirements of controlled cooling after rolling of various alloy steel bars. Background technique [0002] Different alloy steel long products have completely different requirements on the controlled cooling process after rolling. For example, bearing steel and spring steel require rapid cooling and then slow cooling at low temperature after rolling, while gear steel requires rapid collection to achieve high temperature and slow cooling after rolling. Therefore, different processing methods should be used to produce different alloy steel grades. However, the layout of the post-rolling area of ​​the current long steel rolling workshop is relatively simple, and it is difficult to meet the production process requirements of various steel types. The main shortcomings are as follows: [0003] 1. The existing steel rollin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21B37/76B21B45/02
CPCB21B37/76B21B45/0209
Inventor 吕鹏王京瑶陈立坤马志勇丁玉龙杨勇强王任全刘炜黄衍林范思石
Owner BEIJING JINGCHENG RUIXINCHANGCAI ENG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products