Low-temperature lead-free glass powder for vehicle front windscreen laminated glass ink, and preparation method thereof

A technology for front windshield and lead-free glass powder, applied in the field of lead-free glass powder, can solve the problem of not mentioning the glass powder formulation and preparation method, and achieve the effects of good chemical stability and adhesion, and simple components

Inactive Publication Date: 2017-02-22
UNIV OF ELECTRONICS SCI & TECH OF CHINA ZHONGSHAN INST
View PDF10 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Application No. CN201110448979 of "Ink for Automobile Front Windshield and Its Preparation Method", Application No. CN201210429098 of "Ink Slurry for Environmentally Friendly Automobile Glass and Its Preparation Method" and "Ink and Preparation Method for Automobile Side Windshield" Its preparation method " the Chinese patent of application number CN201110444665 all discloses automobile glass ink and preparation method thereof, but does not mention the formula and preparation method of glass powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature lead-free glass powder for vehicle front windscreen laminated glass ink, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] In order to make the purpose, technical solutions and advantages of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. The described embodiments are some, but not all, embodiments of the invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0018] The formula of the lead-free glass powder that the embodiment of the present invention adopts is as shown in table 1 below:

[0019]

[0020] The preparation process adopted by the embodiments of the present invention 1, 2, 3, 4, 5 and 6 is as follows: each material is accurately weighed according to the mass percentage of the material set in the above table 1, and the above-mentioned materials are accu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses low-temperature lead-free glass powder for a vehicle front windscreen laminated glass ink, and a preparation method thereof, wherein the low-temperature lead-free glass powder contains, by mass, 15-25% of SiO2, 45-60% of Bi2O3, 4-12% of ZnO, 1.5-4.0% of Na2O, 0.5-2.5% of K2O, 0.3-1.0% of Al2O3, 5-10% of B2O3, 0.4-1.3% of F2, 0.5-1.0% of TiO2, and 2.5-3.8% of ZrO2. The low-temperature lead-free glass powder of the present invention has characteristics of low softening temperature, wide softening temperature range, suitable expansion coefficient, high acid resistance, high alkali resistance, high adhesion, and the like.

Description

technical field [0001] The invention belongs to the field of lead-free glass powder, and in particular relates to a low-temperature lead-free glass powder used for the ink of laminated glass on the front of the automobile glass. Background technique [0002] Automotive toughened glass ink is used on the edges of the toughened glass of the car to effectively reduce the UV transmittance, prevent the chemical change of the glue used to bond the glass and the car body, and at the same time cover the conductive silver paste, giving the appearance of the car a sense of beauty Action ink. Automotive tempered glass ink is mainly composed of glass powder, black glass pigment, varnish, additives, etc. and formulated according to a certain proportion. The mass ratio of glass powder can generally reach about 60%-80%. As a binder, glass powder plays an important role in glass ink. The glass powder softens and melts during sintering to produce a liquid state. When the organic components...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C12/00
Inventor 王悦辉
Owner UNIV OF ELECTRONICS SCI & TECH OF CHINA ZHONGSHAN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com