Quick-dry stone-like coating special for interior architecture wall surfaces

A technology of real stone paint and wall surface, applied in the direction of coating, etc., can solve the problems that the surface of real stone paint is easy to be stained with dust, not easy to dry, and slow to dry, so that it is not easy to get dusty and accelerates the drying speed Effect

Inactive Publication Date: 2017-03-22
ANHUI MEILIN BUILDING MATERIAL
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Many existing building walls usually need to be coated with real stone paint on the surface after the construction is completed, but the existing real stone paint is not easy to dry after coating, and the drying speed is slow, so that the surface of the real stone paint is easy to be stained with dust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A special quick-drying real stone paint for interior building walls, the real stone paint is composed of the following components by weight: 30 parts of pure acrylic emulsion, 6 parts of manganese naphthenate, 2 parts of hydroxyethyl cellulose, and 3 parts of ethylene glycol , 8 parts of quartz sand, 2 parts of hollow glass microspheres, 1 part of curing agent, 1 part of stabilizer, 2 parts of defoamer, 0.5 part of film-forming aid and 10 parts of deionized water.

[0013] The mesh of the quartz sand is 40 mesh.

[0014] The type of curing agent is vinyltriamine.

Embodiment 2

[0016] A special quick-drying real stone paint for interior building walls, the real stone paint is composed of the following components by weight: 50 parts of pure acrylic emulsion, 9 parts of manganese naphthenate, 4 parts of hydroxyethyl cellulose, and 5 parts of ethylene glycol , 9 parts of quartz sand, 5 parts of hollow glass beads, 3 parts of curing agent, 2 parts of stabilizer, 3 parts of defoamer, 1.5 parts of film-forming aid and 15 parts of deionized water.

[0017] The mesh of the quartz sand is 50 mesh.

[0018] The type of curing agent is methylenebiscyclohexylamine.

Embodiment 3

[0020] A special quick-drying real stone paint for interior building walls, the real stone paint is composed of the following components in parts by weight: 70 parts of pure acrylic emulsion, 12 parts of manganese naphthenate, 6 parts of hydroxyethyl cellulose, and 7 parts of ethylene glycol , 10 parts of quartz sand, 8 parts of hollow glass beads, 5 parts of curing agent, 3 parts of stabilizer, 4 parts of defoamer, 2.5 parts of film-forming aid and 20 parts of deionized water.

[0021] The mesh number of the quartz sand is 60 mesh.

[0022] The type of the curing agent is triethylenetetramine.

[0023] The real stone paint prepared by implementing the components of implementation 1, implementation 2 and implementation 3, compared with ordinary real stone paint, the real stone paint prepared by the present invention, by adding raw material components such as hollow glass beads, curing agent, stabilizer, etc., makes the present invention After the prepared real stone paint is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a quick-dry stone-like coating special for interior architecture wall surfaces. The stone-like coating is prepared from, by weight, 30-70 parts of pure acrylic emulsion, 6-12 parts of manganese naphthenate, 2-6 parts of hydroxyethyl cellulose, 3-7 parts of ethylene glycol, 8-10 parts of quartz sand, 2-8 parts of hollow glass microspheres, 1-5 parts of a curing agent, 1-3 parts of a stabilizing agent, 2-4 parts of an antifoaming agent, 0.5-2.5 parts of a film formation assistant and 10-20 parts of deionized water. According to the quick-dry stone-like coating, the ingredients of raw materials such as the hollow glass microspheres, the curing agent and the stabilizing agent are added, after the stone-like coating prepared with a method is coated, the drying speed is greatly quickened, and after the architecture wall surfaces are coated with the stone-like coating, the stone-like coating can be rapidly dried, and dust cannot be easily attached to the stone-like coating.

Description

technical field [0001] The invention relates to a real stone paint, in particular to a special quick-drying real stone paint for indoor building walls. Background technique [0002] Real stone paint is mainly made of natural stone powder of various colors. It is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. Real stone paint has the characteristics of fire prevention, waterproof, acid and alkali resistance, pollution resistance, non-toxic, tasteless, strong adhesion, and never fades. It can effectively prevent the harsh external environment from corroding buildings and prolong the life of buildings. Many existing building walls usually need to be coated with real stone paint on the surface after the construction is completed, but the existing real stone paint is not easy to dry after coating, and the drying speed is slow, so that the surface of the real stone paint is easy to be stained with dust. Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12
CPCC09D133/04C09D7/61C09D7/63C09D7/70C08L1/284C08K13/04C08K7/28C08K3/34C08K5/098
Inventor 周兴国
Owner ANHUI MEILIN BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com