Self-cleaning coating for aluminum alloy doors and windows
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of aluminum alloy doors and windows, self-cleaning technology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc. Strong adhesion effect
Inactive Publication Date: 2017-03-29
GUANGXI DEJUN DOOR & WINDOW CURTAIN WALL
View PDF0 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the photolysis of TiO2 will degrade the organic components of the coating film at the same time, so that the life of the coating film cannot be guaranteed
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] The self-cleaning paint for aluminum alloy doors and windows is prepared by reacting the following raw materials in parts by weight:
[0014] 45 parts of diphenyldimethoxysilane, 10 parts of vinyl, 1 part of methyl ethyl ketone, 5 parts of ethoxyethanol, 0.5 parts of iron oxide, 0.5 parts of catalyst, and 5 parts of dimethylpropane.
Embodiment 2
[0016] A self-cleaning coating for aluminum alloy doors and windows, which is prepared by reacting the following raw materials according to parts by weight:
[0017] 60 parts of diphenyldimethoxysilane, 15 parts of vinyl, 5 parts of methyl ethyl ketone, 8 parts of ethoxyethanol, 0.8 parts of iron oxide, 1 part of catalyst, and 15 parts of dimethylpropane.
Embodiment 3
[0019] A self-cleaning coating for aluminum alloy doors and windows, which is prepared by reacting the following raw materials according to parts by weight:
[0020] 55 parts of diphenyldimethoxysilane, 13 parts of vinyl, 3 parts of methyl ethyl ketone, 7 parts of ethoxyethanol, 0.6 parts of iron oxide, 0.8 parts of catalyst, and 11 parts of dimethylpropane.
[0021] The preparation method of above each embodiment:
[0022] (1) Add diphenyldimethoxysilane, vinyl, and methyl ethyl ketone to the kneader in order, and stir evenly;
[0023] (2) Continue to add dimethyl propane, heat up and vacuumize and stir, and it is worth the base material;
[0024] (3) Grinding the prepared base material into a powdery base material with a grinder;
[0025] (4) Add the powdery base material into the stirring tank, then add ethoxyethanol, catalyst and iron oxide, and stir evenly under vacuum to prepare the self-cleaning coating.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to self-cleaning coating, in particular to self-cleaning coating for aluminum alloydoors and windows. The self-cleaning coating for the aluminum alloydoors and windows is prepared from the following raw materials including, by weight, 20-30 parts of phenyltrimethoxysilane, 25-40 parts of methyl-ethyloxy silicone oil, 10-15 parts of fluorosilicone, 15-20 parts of methyl glyoxylate, 1-5 parts of oxalic acid, 0.1-0.5 part of cyclopentanol and 0.3-0.7 part of catalysts. According to the self-cleaning coating for the aluminum alloydoors and windows, material stability is good, adhesive force is strong, and the service life is long.
Description
technical field [0001] The invention relates to a self-cleaning paint, especially a self-cleaning paint for aluminum alloy doors and windows. Background technique [0002] Glass self-cleaning will be an important market for modern household hygiene needs. The traditional method of glass self-cleaning spraying construction is spraying. Its loss, equipment purchase, and operation difficulty are difficult for families to accept. We are looking for a convenient construction. Material saving, low-cost glass self-cleaning construction method is very necessary. [0003] Developing a transparent self-cleaning paint that can be applied to the glass surface to make the glass surface appear self-cleaning function is the pursuit goal of people in recent years. Most of the glass self-cleaning coatings available in the market are hydrophilic, and the TiO covered 2 Under the excitation of ultraviolet rays, the coating exhibits hydrophilicity and photolysis, so it can decompose and peel o...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 