Production technology of mirror surface black decoration film

A production process and decoration technology, applied in the direction of flat products, household appliances, other household appliances, etc., can solve the problems of strip borders, etc., achieve the effect of large blackness, solve the problem of strip borders, and evenly disperse

Inactive Publication Date: 2017-04-26
TIANJIN SUNRAY PLASTIC PROD
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The advantages and positive effects of the present invention are: the present invention provides a production process of mirror black decoration, compared with the prior art, the glass film in the technical solution of the present invention is more evenly dispersed, and the problem of striped borders is solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] (1) The step of preparing black masterbatch. The masterbatch base material adopts EVA resin with a melt index of 1.5g / 10min at 190°C. Add ultraviolet absorbers, antioxidants and ultrafine carbon black to the base material, and use polymer Wax is used as a dispersant, extruded on a twin-screw extruder, and the specific surface area of ​​ultra-fine carbon black is 2800㎡ / g;

[0011] (2) The step of mixing the black masterbatch with EVA resin and coupling agent uniformly, the melt index of EVA resin is 8g / 10min at 190°C;

[0012] (3) In the step of producing a mirror-surface black decorative film by casting a film-forming process, the extrusion temperature is controlled at 90° C.;

[0013] (4) In the step of embossing, the water temperature of the rubber rollers of the embossing forming equipment is controlled at 8°C, the rubber rollers are made of an integrated silicone material, the softness and hardness are controlled at 60A, and the grain size of the rubber rollers is 1...

Embodiment 2

[0016] (1) The step of preparing black masterbatch. The masterbatch base material adopts EVA resin with a melt index of 3.5g / 10min at 190°C. Add ultraviolet light absorbers, antioxidants and ultrafine carbon black to the base material, and use polymer Wax is used as a dispersant, extruded on a twin-screw extruder, and the specific surface area of ​​ultra-fine carbon black is 2900㎡ / g;

[0017] (2) The step of mixing the black masterbatch with EVA resin and coupling agent uniformly, the melt index of EVA resin is 12g / 10min at 190°C;

[0018] (3) The step of producing a mirror-surface black decorative film by casting a film-forming process, and the extrusion temperature is controlled at 100° C.;

[0019] (4) In the step of embossing forming, the water temperature of the rubber rollers of the embossing forming equipment is controlled at 10°C, the rubber rollers are made of integrated silicone material, the hardness is controlled at 70A, and the grain size of the rubber rollers is ...

Embodiment 3

[0022] (1) The step of preparing black masterbatch. The masterbatch base material adopts EVA resin with a melt index of 4.5g / 10min at 190°C. Add ultraviolet absorbers, antioxidants and ultrafine carbon black to the base material, and use macromolecule Wax is used as a dispersant, extruded on a twin-screw extruder, and the specific surface area of ​​ultra-fine carbon black is 3000㎡ / g;

[0023] (2) The step of mixing the black masterbatch with EVA resin and coupling agent uniformly, the melt index of EVA resin is 14g / 10min at 190°C;

[0024] (3) The step of producing a mirror-surface black decorative film by casting a film-forming process, and the extrusion temperature is controlled at 110° C.;

[0025] (4) In the step of embossing, the water temperature of the rubber rollers of the embossing forming equipment is controlled at 12°C, the rubber rollers are made of integrated silicone material, the hardness is controlled at 80A, and the grain size of the rubber rollers is 18 mesh;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the production technology of a mirror surface black decoration film. The production technology comprises the following steps that 1, black master batches are prepared, EVA resin with the melt index being 0.5 g / 10 min-5 g / 10 min at the temperature of 190 DEG C is adopted as a master batch base material, an ultraviolet absorber, an antioxidant and superfine carbon black are added into the base material, macromolecule wax is adopted as a dispersing agent and extruded and formed on a double-screw extruder, and the specific area of the superfine carbon black is 2500 m<2> / g-3000 m<2> / g; 2, the black master batches, the EVA resin and a coupling agent are mixed uniformly, and the melt index of the EVA resin ranges from 5 g / 10 min to 15 g / 10 min at the temperature of 190 DEG C; 3, the mirror surface black decoration film is generated, and the extrusion temperature is controlled to range from 90 DEG C to 110 DEG C; and 4, embossing forming is carried out, rubber roller water temperature of embossing forming equipment is controlled to range from 8 DEG C to 12 DEG C, a rubber roller is made of an integral silica gel material, hardness is controlled to range from 60 A to 80 A, roughness of sand meshes of the rubber roller is 14-18 meshes, steel roller water temperature is controlled to range from 10 DEG C to 15 DEG C, and the pattern depth ranges from 0.06 mm to 0.15 mm.

Description

technical field [0001] The invention relates to a production process of mirror black decoration. Background technique [0002] In the field of architectural decoration, laminated glass has been more and more widely used due to its excellent characteristics such as beauty and firmness. Laminated glass includes a glass film layer in the center and glass on both sides. The existing glass film is generally monochromatic, and the laminated glass produced is generally transparent and monochromatic. When it is necessary to show the combined color effect, laminated glass of multiple colors is generally used in combination. However, with the improvement and transformation of people's aesthetic ability, monochrome laminated glass can no longer meet people's aesthetic needs, and people are in urgent need of film products with mirror black effect. The above-mentioned production process does not exist in the prior art. There are many defects in the existing black decorative EVA film: (1...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C69/00B29C41/24B29C59/04B29B9/06B29L7/00
CPCB29C69/00B29B9/06B29C41/24B29C59/04B29L2007/00B29L2031/722
Inventor 崔九峰
Owner TIANJIN SUNRAY PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More