Super soft epoxy curing agent composition and preparation method thereof

A super-soft epoxy and curing agent technology, which is applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., can solve the problems of not meeting the requirements, not being environmentally friendly, and having a strong smell, and achieve a dense and soft combination with good effect good effect

Inactive Publication Date: 2017-04-26
江苏芯锐传感科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the curing temperature is high, and xylene must be added, which has a strong smell and is not environmentally f

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] This embodiment relates to a preparation method of a super soft epoxy curing agent composition, which includes the following steps:

[0056] According to 20 parts of diethylenetriamine, 30 parts of propylene carbonate, 20 parts of oleic acid, and 30 parts of castor oil, the ingredients are prepared;

[0057] Mix propylene carbonate, oleic acid and castor oil to obtain an oily turbid liquid;

[0058] Diethylenetriamine was added to the oily watery turbid liquid, and after mixing, the reaction was carried out at 100° C. to obtain the super soft epoxy curing agent composition.

Embodiment 2

[0060] This embodiment relates to a preparation method of a super soft epoxy curing agent composition, which includes the following steps:

[0061] According to 40 parts of diethylenetriamine, 10 parts of propylene carbonate, 30 parts of oleic acid, and 20 parts of castor oil;

[0062] Mix propylene carbonate, oleic acid and castor oil to obtain an oily turbid liquid;

[0063] Diethylenetriamine was added to the oily watery turbid liquid, and after mixing, the reaction was carried out at 100° C. to obtain the super soft epoxy curing agent composition.

Embodiment 3

[0065] This embodiment relates to a preparation method of a super soft epoxy curing agent composition, which includes the following steps:

[0066] According to 30 parts of diethylene triamine, 20 parts of propylene carbonate, 25 parts of oleic acid, and 25 parts of castor oil for ingredients;

[0067] Mix propylene carbonate, oleic acid and castor oil to obtain an oily turbid liquid;

[0068] Diethylenetriamine was added to the oily watery turbid liquid, and after mixing, the reaction was carried out at 100° C. to obtain the super soft epoxy curing agent composition.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a kind of super soft epoxy curing agent, which comprises the chemical reaction of combination with four chemicals of diethylenediamine, propylene carbonate, oleic acid, and castor oil. The curing agent is blended into super soft epoxy adhesive with epoxy resin and epoxy diluent. Finally, the super soft epoxy adhesive is used in the application of cloth cover, or widely used in bonding repair, house wall decoration and so on.

Description

Technical field [0001] The invention relates to a super soft epoxy curing agent composition and a preparation method thereof, and belongs to the technical field of curing agents. Background technique [0002] In order to make the thin cloth and epoxy glue adhere firmly, usually another layer of glue is applied to the thin cloth that has been coated with glue. At present, there are existing but single-component adhesives that can achieve the purpose of coating and bonding. But the adhesive needs 250°C to cure. Such curing conditions are too harsh, and now it is necessary to seek a flexible adhesive that can be cured at 80~100°C to achieve the purpose of coating and bonding. [0003] There are mainly the following types of low-temperature curing adhesives in the prior art: [0004] Hydroxy-terminated nitrile rubber modified epoxy adhesive. [0005] Epoxy resin (E-51) 100; [0006] Hydroxyl-terminated liquid nitrile rubber (HTBN) 16; [0007] Diethylenetriamine 10-15; [0008] Dioctyl se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G59/40C09J163/00
CPCC08G59/4014C09J163/00
Inventor 康健季婧立
Owner 江苏芯锐传感科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap