Wear-resistant cold-resistant modified polyvinyl chloride (PVC)/thermoplastic polyurethane elastomer (TPU) composite lightweight conveyor belt and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A lightweight conveyor belt, composite material technology, applied in conveyors, chemical instruments and methods, transportation and packaging, etc. problem, to achieve good compatibility, improve mechanical properties, improve wear resistance and low temperature resistance.
Inactive Publication Date: 2017-04-26
AA IND BELTING (SHANGHAI) CO LTD
View PDF8 Cites 12 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, during the use of light PVC conveyor belt, the wear resistance and low temperature resistance are poor, especially in the north, the surface of the conveyor belt will be brittle and worn, which will reduce the mechanical properties of the conveyor belt and affect its service life
The traditional coating method is used to prepare light PVC conveyor belts, and a large amount of plasticizer fumes will be generated during the preparation process, polluting the environment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 2
[0039] Present embodiment 2 is basically the same as embodiment 1, and its difference is:
[0040] In this embodiment 2, the composite cladding material includes the following components in parts by weight:
[0041] 100 parts of PVC powder;
[0042] 20 parts of TPU powder;
[0043] 60 parts of dioctyl phthalate;
[0044] 6 parts of epoxidized soybean oil;
[0045] 4 parts of calcium zinc composite heat stabilizer;
[0046] 10 parts of heavy calcium carbonate.
[0047] Performance testing was performed on the wear-resistant and cold-resistant modified PVC / TPU composite lightweight conveyor belt prepared in Example 2 above. The test results are shown in Table 1.
Embodiment 3
[0049] Present embodiment 3 is basically the same as embodiment 1, and its difference is:
[0050] In this embodiment 3, the composite cladding material includes the following components in parts by weight:
[0051] 100 parts of PVC powder;
[0052] 30 parts of TPU powder;
[0053] 60 parts of dioctyl phthalate;
[0054] 6 parts of epoxidized soybean oil;
[0055] 4 parts of calcium zinc composite heat stabilizer;
[0056] 10 parts of heavy calcium carbonate.
[0057] The wear-resistant and cold-resistant modified PVC / TPU composite lightweight conveyor belt prepared in Example 3 above was tested for performance, and the test results are shown in Table 1.
[0058] In order to detect the technical effect of the wear-resistant and cold-resistant modified PVC / TPU composite light conveyor belt prepared in the embodiment of the present invention, GB / T 531.1-2008, GB / T 1040.3-2006, GB / T 6035-1985, The method specified in ISO 5470-1-1999 was used for performance testing, and the...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
melting point
aaaaa
aaaaa
hardness
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a wear-resistant cold-resistant modified polyvinyl chloride (PVC) / thermoplastic polyurethane elastomer (TPU) composite lightweight conveyor belt. The conveyor belt is formed by pressing a fiber fabric and a PVC / TPU composite clad material, the PVC / TPU composite clad material comprises the following components in parts by weight: 100 parts of PVC powder, 10-40 parts of TPU powder, 60-70 parts of dioctyl phthalate, 4-6 parts of epoxidized soybean oil, 2-4 parts of calcium-zinc composite heat stabilizer and 5-10 parts of ground calcium carbonate, so as to prepare the wear-resistant cold-resistant modified polyvinyl chloride (PVC) / thermoplastic polyurethane elastomer (TPU) composite lightweight conveyor belt. Because the compatibility of the polyester type TPU and the suspension type PVC of the composite clad material is good, the TPU can be uniformly dispersed in the PVC, the wear resistance and the low temperature resistance of the clad layer of the conveyor belt can be improved, the mechanical property of the material can be improved, the wear-resistant and low-temperature-resistant performance is superior to that of a traditional PVC coating clad layer, and the lightweight conveyor belt can be used for a long term in a low-temperature environment at the temperature of 30 DEG C, and the technical problems that the lightweight conveyor belt is prone to brittle cracking, easy to wear and the like in a low-temperature environment can be effectively solved.
Description
technical field [0001] The invention relates to a wear-resistant and cold-resistant modified polyvinyl chloride (PVC) / thermoplastic polyurethane elastomer (TPU) composite light-duty conveyor belt and a preparation method thereof. Background technique [0002] Lightweight PVC conveyor belt is composed of single-layer or multi-layer reinforcement and covering rubber layer. It has the characteristics of light weight, good dimensional stability, high tension, bright color, safety and non-toxicity, etc. It is widely used in various industries, among which polyester The light PVC conveyor belt with fabric as the matrix and PVC resin as the matrix is often used in the production lines of various industries. However, during the use of light PVC conveyor belt, the wear resistance and low temperature resistance are poor, especially in the north, the surface of the conveyor belt will be brittle and worn, resulting in the reduction of the mechanical properties of the conveyor belt and...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.