Warm mix polymer modified asphalt mixture and preparation method thereof

A modified asphalt and polymer technology, applied in the direction of climate change adaptation, etc., can solve the problems of poor thermal stability and anti-aging performance of asphalt, environmental pollution, etc., and achieve improved anti-aging performance, shortened reaction time, and stable performance Effect

Active Publication Date: 2017-05-10
CHINA PETROLEUM & CHEM CORP +1
View PDF13 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] In order to solve the problem that the processing and use temperature of polymer modified asphalt mixture is high in the prior art, which may easily cause environmental pollution or the heat stability and anti-aging performance of the asphalt are not good even though the use temperature can be reduced after adding warm mix agent , the present invention provides a warm-mix polymer modified asphalt mixture. A self-made warm mix agent is added to the used asphalt, which can significantly reduce the use temperature of polymer-modified asphalt and reduce the use of polymer-modified asphalt. At the same time, it can improve the thermal stability of asphalt and improve the anti-aging performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Warm mix polymer modified asphalt mixture and preparation method thereof
  • Warm mix polymer modified asphalt mixture and preparation method thereof
  • Warm mix polymer modified asphalt mixture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] (1) Preparation of warm mix

[0061] Using Ni metal as a catalyst, the CO obtained after gasification of coal is combined with H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with a carbon number of 30 to 60 account for 90%.

[0062] ①Weigh 1000g of the above mixed alkane, about 1.2mol, put it in a closed container, heat it to 480℃, add 3g catalyst anhydrous CuCl 2 , keep introducing 0.89 mol of chlorine at this temperature, and feed nitrogen to keep the pressure of the reaction vessel at 3MPa, and react for 30min to obtain an intermediate;

[0063] ②Weigh 7000g of minus four-line extraction oil with an aromatic content of 70%, and add 441g of the complex [Cu(NH4)] to it. 3 ) 4 ]SO 4 , installed in another container and heated to 350 ° C, and stirred at a constant temperature for 180 min at this temperature to obtain an aromatic complex component;

[0064] 3. Introducing the aromatic hydrocarbon complex component into the above inte...

Embodiment 2

[0070] (1) Preparation of warm mix

[0071] Using Co metal as a catalyst, the CO obtained after gasification of coal is combined with H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with a carbon number of 30 to 130 account for 90%.

[0072] ①Weigh 3500g of the above mixed alkane, about 4.5mol, put it in a closed container, heat it to 400℃, add 31.5g catalyst anhydrous MnCl 2 , keep introducing 1.16mol of chlorine at this temperature, and feed nitrogen to keep the pressure of the reaction vessel at 5MPa, and react for 60min to obtain an intermediate;

[0073] ②Weigh 1000g of catalytic cracking oil slurry with an aromatic content of 63%, and add 19g of complex K to it 4 [Fe(CN) 6 ], installed in another container and heated to 270°C, and stirred at this temperature for 120min at a constant temperature to obtain an aromatic complex component;

[0074] 3. Introducing the aromatic hydrocarbon complex component into the above intermediate, kee...

Embodiment 3

[0080] (1) Preparation of warm mix

[0081] Using Fe metal as a catalyst, the CO obtained after gasification of coal is combined with H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with carbon numbers of 70 to 90 account for 90%.

[0082] ①Weigh 1000g of the above mixed alkane, about 0.8mol, put it in a closed container, heat it to 440℃, add 6g catalyst anhydrous NiCl 2 , keep introducing 0.31mol of fluorine at this temperature, and feed nitrogen to keep the pressure of the reaction vessel at 4MPa, and react for 45min to obtain an intermediate;

[0083] ②Weigh out 3500 g of phenol refined extract oil with an aromatic content of 78%, and add 164 g of the complex [Ni(CO) 4 ], placed in another container and heated to 310°C, and stirred at a constant temperature for 160min at this temperature to obtain an aromatic complex component;

[0084] 3. Introducing the aromatic complex component into the above intermediate, keeping the temperature at...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a warm mix polymer modified asphalt mixture and a preparation method thereof, wherein the mixture comprises 4.0-6.0 parts of a warm mix polymer modified asphalt, 1.0-3.0 parts of ore powder, and 91.0-95.0 parts of an aggregate, the warm mix polymer modified asphalt comprises 1-7 parts of a warm mix agent, 2-5 parts of a polymer, 88-97 parts of matrix asphalt, and sulfur, and the sulfur accounts for 0.01-0.07% of the total mass of the warm mix agent, the polymer and the matrix asphalt. The warm mix agent preparation method comprises: under the effect of a catalyst, carrying out a reaction on a macromolecule alkane and a halogen to obtain an intermediate; uniformly mixing aromatic hydrocarbon oil and a complexing compound to obtain an aromatic hydrocarbon complexing component; and carrying out a reaction on the aromatic hydrocarbon complexing component and the intermediate at a certain temperature to obtain the warm mix agent. According to the present invention, by adding the warm mix agent to the asphalt in the mixture, the warm mix effect is provided for the asphalt, the high temperature performance and the low temperature performance of the asphalt are considered, the thermal stability of the asphalt is improved, the aging resistance is improved, the thermal aging of the asphalt is reduced, and the harmful gas generation is reduced.

Description

technical field [0001] The invention relates to a warm-mixed polymer-modified asphalt mixture and a preparation method thereof, belonging to the fields of petroleum industry and basic material chemistry. Background technique [0002] Asphalt mixtures used in previous road projects are generally divided into two types according to the mixing construction temperature: cold mix asphalt mixture CMA (Cold Mix Asphalt) and hot mix asphalt mixture HMA (Hot Mix Asphalt). Cold mix asphalt is generally mixed and paved with emulsified asphalt or liquid asphalt and aggregates at room temperature without heating the aggregates and aggregates, which can save a lot of energy. However, the initial strength of cold mix asphalt mixture is low, and it is difficult to meet the requirements of important projects such as highways and heavy-duty traffic roads. Hot mix asphalt is widely used and has good road performance. However, in the production process of hot mix asphalt, asphalt and stone ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26
CPCY02A30/30
Inventor 陈保莲范思远张静宁爱民李志军程国香
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com