Manufacturing apparatus and method of microporous polyolefin resin sheet

A polyolefin resin, technology for manufacturing equipment, applied in flat products, applications, coatings, etc., can solve problems such as contamination, sheet defects, etc.

Active Publication Date: 2018-05-01
TORAY IND INC
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When a certain amount of liquid is stored, it will drip on the cooling and solidification device, pollute the cooling and solidification device where the sheets are tightly bonded, and cause defects in the sheets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing apparatus and method of microporous polyolefin resin sheet
  • Manufacturing apparatus and method of microporous polyolefin resin sheet
  • Manufacturing apparatus and method of microporous polyolefin resin sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] A specific sheet manufacturing method in this embodiment is as follows.

[0059] (1) Sheet material

[0060]·High-density polyethylene (HDPE): viscosity 1000Pa·s. Here, the viscosity is measured by the method of JISK7117-2 on conditions of a shear rate of 100 / s and a temperature of 200°C.

[0061] ·Liquid paraffin (LP): Dynamic viscosity 50cSt (at 40°C mm2 / s).

[0062] (2) Feeding

[0063] After the sheet material is dried, it is supplied to an extruder, and after passing through a gear pump and a filter, it is supplied to a die. In addition, the temperature of the device before reaching the die was set to 230°C.

[0064] (3) Die

[0065] The slit width was set to 300 mm, and the above-mentioned sheet material was discharged at a flow rate of 250 kg / hr. It should be noted that the concentration of LP in the polyolefin resin solution is 70% by mass, so 175kg / hr is LP. In addition, depending on the width of the sheet and the degree of decompression, 0.1% of the flo...

Embodiment 2

[0074] Film formation was performed with the same apparatus configuration and film formation conditions as in Example 1 except that the following rectifying plates were used.

[0075] (rectifier plate)

[0076] Make the rectifying plate of square column type without arc at the bottom. The opening of the lower surface of the rectifying plate facing the cooling and solidification device is set as a hole with a diameter of φ1mm and a pitch of 5mm, and is processed along the entire width with the same length as the width and length of the die lip. In addition, the gap between the rectifying plate and the back of the sheet is set to 5 mm, the gap between the lower surface of the die and the upper surface of the rectifying plate facing it is set to 5 mm, and the cooling and solidifying device and the gap below the rectifying plate facing it are set to 5 mm. The surface gap is set to 10 mm, and it is placed in the decompression chamber in this manner. In order to depressurize the i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for producing a microporous polyolefin resin sheet, in which a solution of a mixed polyolefin resin and a diluent discharged from a die is cooled while sucking air between the sheet and a cooling and solidification device using a suction chamber. The solidification device is discharged into flakes, and the flakes are cooled to prevent the liquefied products of low molecular weight components of polymers, diluents, and additives adhering to the rectifying plate arranged in the decompression chamber from dripping, and to prevent flake defects. produce. An apparatus for producing a microporous polyolefin resin sheet comprising a die for discharging a solution obtained by mixing a polyolefin resin and a diluent into a sheet is used. shape; the cooling and solidification device, the cooling and solidification device is used to cool the sheet discharged from the die; the decompression chamber, the decompression chamber is used to suck the air between the sheet and the cooling and solidification device, wherein the decompression The inside of the chamber is equipped with rectifying plates to attract the inside of the decompression chamber and the inside of the rectifying plate, and by keeping the pressure in the rectifying plate lower than the pressure of the decompression chamber, the polymer attached to the rectifying plate is reduced. Molecular weight components, diluents, and liquefied additives are forcibly sucked into the straightening plate and removed.

Description

technical field [0001] The present invention relates to a manufacturing device and method of a microporous polyolefin resin sheet. Background technique [0002] The outline of a general resin sheet manufacturing apparatus will be described below. Such as Image 6 As shown, the resin melted by the heat and shear force applied by the extruder 1 is discharged in a certain amount through the gear pump 2, and then the foreign matter and the like are filtered through the filter 3, and the resin is discharged from the die 4 with an arbitrary lip gap. For flakes. The discharged flaky molten resin is cooled and solidified by the cooling and solidification device 5 . Next, the cooled and solidified sheet 6 is stretched in an arbitrary direction at an arbitrary ratio by a stretching device 7 , and wound by a winder 8 . In addition, at this time, the thickness of the sheet in the width direction is measured by the thickness gauge 9, and based on the thickness measurement data, the li...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C47/88B29C41/24B29C41/34B29C47/08C08J9/28C08K5/00C08L23/00B29K23/00B29K105/04B29L7/00B29C48/08B29C48/28B29C48/305B29C48/355B29C48/885
CPCB29C41/24B29C41/34C08J9/28C08K5/00C08L23/00B29K2091/00B29K2105/0038B29K2023/06B29K2023/12B29K2025/06B29C2791/006B29K2105/041B29C48/92B29C48/022B29C48/08B29C48/0018B29C48/1472B29C48/25B29C48/27B29C48/272B29C48/274B29C48/28B29C48/302B29C48/355B29C48/387B29C48/69B29C48/768B29C48/914B29C48/916B29C2948/92152B29C2948/92514B29C2948/92647B29C2948/92923B29C2948/92961B29C48/885B29C48/88B29C48/30
Inventor 牧晃久北村理野村文保君岛康太郎
Owner TORAY IND INC