Continuous casting crystallizer function protection material special for high-oxygen enamel steel

A technology of continuous casting mold and protective material, applied in the field of metallurgical auxiliary materials, can solve the problems of various oxide inclusions, increase the brittleness of steel, etc., and achieve the effect of strong wear resistance and good anti-scale explosion performance.

Active Publication Date: 2017-05-31
HENAN XIBAO METALLURGICAL MATERIALS GROUP
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] 1. The oxygen content in molten steel is high, and oxygen will increase the brittleness of steel. Oxygen oft...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous casting crystallizer function protection material special for high-oxygen enamel steel
  • Continuous casting crystallizer function protection material special for high-oxygen enamel steel
  • Continuous casting crystallizer function protection material special for high-oxygen enamel steel

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] The preparation method of the special continuous casting crystallizer functional protection material for high-oxygen enamel steel of the present invention comprises the following steps:

[0045] Step S1: Weigh the above-mentioned raw materials for weighing and batching, put them into a mixer and mix for 40-50 minutes; then add them to a stirring mill, mix with water, grind, and sieve to obtain a slurry with a particle size of ≤1mm;

[0046] Step S2: The slurry is pumped through the slurry pipeline by the ceramic plunger slurry to the prilling tower for atomization and drying, and the slurry changes from liquid to solid to form hollow particles;

[0047] Step S3: Sieve the hollow particles to obtain qualified material, cool and pack.

[0048] The chemical composition of the premelt used in the present invention and its weight percentage are: SiO 2 25.0~35.0%, CaO35.0~46.0%, Al 2 o 3 2.0~7.0%, R 2 O4.0~15.0%, F ~ 2.0~8.0%, MgO2.0~6.0%, of which R 2 O=K 2 O+Na 2 O+...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a continuous casting crystallizer function protection material special for high-oxygen enamel steel and relates to metallurgical auxiliary materials. The continuous casting crystallizer function protection material comprises, by weight, 55.0%-62.5% of pre-molten materials, 4%-6% of lithium carbonate, 4%-6% of light-burned white alkali, 1%-3% of bentonite, 8%-10% of high fluorite powder, 1%-4% of high alumina, 4%-6% of cryolite, 3%-5% of sodium fluoride, 2%-4% of albite, 2%-4% of fine glass powder, 0-2% of imported carbon black and 0-2% of graphite, and the sum of the content of all the raw materials is 100%. The continuous casting crystallizer function protection material is special for the high-oxygen enamel steel and can be appropriately spread in a crystallizer, and no sintering and caking phenomenon occurs; melting is uniform, and a stable three-layer structure is achieved; the thickness of a liquid slag layer is 8-12 mm; the steel slag consumption quantity is 0.3-0.5 Kg/ton; and the surface quality, the subsurface quality and the inner quality of a casting blank are good.

Description

technical field [0001] The invention relates to metallurgical auxiliary materials, in particular to a special continuous casting crystallizer function protection material for high-oxygen enamel steel. Background technique [0002] On November 1, 2016, it was learned from the Ministry of Industry and Information Technology that the "Industrial Technology Innovation Capability Development Plan (2016~2020)" was officially released, aiming to break through common key technologies in key areas, strengthen the transformation of scientific and technological achievements into real productivity, and improve the performance of key links and key areas. Innovation capabilities, promote the deep integration of the two industries, stimulate the new kinetic energy of "mass innovation and mass innovation", and promote my country's transformation from a manufacturing power to a manufacturing power. The "Plan" also puts forward the key directions for the development of some industries in the i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D11/111
CPCB22D11/111
Inventor 李伟锋李书成周彬张鹏
Owner HENAN XIBAO METALLURGICAL MATERIALS GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap