Toughened, modified, low-temperature-cued and low-glossiness powder coating, preparation method and application

A low-gloss, toughening modification technology, used in low-temperature curing, impact-resistant powder coatings, high-toughness, preparation, low-gloss fields, can solve problems such as poor impact performance, and improve bending resistance and impact resistance. Effect

Inactive Publication Date: 2017-05-31
NIPPON PAINT TIANJIN
View PDF6 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the defects of poor impact properties of epoxy-polyester type low-temperature curing low-gloss products in the prior art, the first purpose of the present invention is to provide a toughened modified low-temperature curing low-gloss powder coating, so that the coating and base The adhesion of the material is the best, and the toughness of the coating is greatly improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Toughened, modified, low-temperature-cued and low-glossiness powder coating, preparation method and application
  • Toughened, modified, low-temperature-cued and low-glossiness powder coating, preparation method and application
  • Toughened, modified, low-temperature-cued and low-glossiness powder coating, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A toughened modified low-temperature curing low-gloss powder coating, comprising the following components by weight:

[0037]

[0038] First, accurately weigh the raw materials according to the formula composition of the coating components, and mix them evenly in the premixing tank through high-speed rotation (premixing time is 5-10 minutes), and then put the evenly mixed raw materials into the twin-screw extruder at a constant speed. The extruder is melted and extruded under the condition of 95-105°C, passed through the cooling roller and pressed into tablets, the tablets are cooled at natural temperature, and the flakes are roughly crushed by a pulverizer, and the obtained materials are ground by a pulverizer after cooling Fine grinding; in order to increase the dry powder fluidity of the powder and prevent powder agglomeration during the grinding process, add 0.1 part of desiccant AEROSIL Alu C, and then use a 180-mesh sieve to sieve, and finally get all the powder...

Embodiment 2

[0040] A toughened modified low-temperature curing low-gloss powder coating, comprising the following components by weight:

[0041]

[0042] First, accurately weigh the raw materials according to the formula composition of the coating components, and mix them evenly in the premixing tank through high-speed rotation (premixing time is 5-10 minutes), and then put the evenly mixed raw materials into the twin-screw extruder at a constant speed. The extruder is melted and extruded under the condition of 95-105°C, passed through the cooling roller and pressed into tablets, the tablets are cooled at natural temperature, and the flakes are roughly crushed by a pulverizer, and the obtained materials are ground by a pulverizer after cooling Fine grinding; in order to increase the dry powder fluidity of the powder and prevent powder agglomeration during the grinding process, add 0.1 part of desiccant AEROSIL Alu C, and then use a 180-mesh sieve to sieve, and finally get all the powder...

Embodiment 3

[0044] A toughened modified low-temperature curing low-gloss powder coating, comprising the following components by weight:

[0045]

[0046]

[0047]First, accurately weigh the raw materials according to the formula composition of the coating components, and mix them evenly in the premixing tank through high-speed rotation (premixing time is 5-10 minutes), and then put the evenly mixed raw materials into the twin-screw extruder at a constant speed. The extruder is melted and extruded under the condition of 95-105°C, passed through the cooling roller and pressed into tablets, the tablets are cooled at natural temperature, and the flakes are roughly crushed by a pulverizer, and the obtained materials are ground by a pulverizer after cooling Fine grinding; in order to increase the dry powder fluidity of the powder and prevent powder agglomeration during the grinding process, add 0.1 part of desiccant AEROSIL Alu C, and then use a 180-mesh sieve to sieve, and finally get all...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
softening pointaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a toughened, modified, low-temperature-cued and low-glossiness powder coating. The toughened, modified, low-temperature-cued and low-glossiness powder coating comprises the following components in parts by weight: 28-35 parts of polyester resin, 28-35 parts of epoxy resin, 3-5 parts of delustering agent, 3-5 parts of toughening agent, 1-10 parts of pigment, 15-27.5 parts of filler, 1-5 parts of levelling agent, and 0.3-0.5 part of benzoin. According to the toughened, modified, low-temperature-cued and low-glossiness powder coating, proper raw materials are selected, and a proper dosage range is set, so as to obtain the low-temperature-cued, low-glossiness, high-toughness and impact-resistant powder coating; the bending resistance and the impact resistance of the low-temperature-curing and low-glossiness product can be improved.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a powder coating with low-temperature curing, low gloss, high toughness and impact resistance, a preparation method and an application. Background technique [0002] Epoxy-polyester powder coatings are powder coatings that are rapidly developed and industrialized after epoxy powder coatings. The usual film-forming substances of epoxy-polyester powder coatings are carboxyl polyester resins and epoxy resins. [0003] Generally, epoxy-polyester powder coatings have the following advantages: 1) The selection of raw materials is very wide, and there are many brands and specifications of polyester and epoxy resins; Low melt viscosity, good leveling and decorative properties of the coating film; 3) Epoxy-polyester coating film has good acid and alkali resistance. However, epoxy-polyester powder coatings also have the following disadvantages: 1) the biggest disadvantage of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D163/00C09D5/03C09D7/12
CPCC09D167/00C08L2205/03C08L2207/53C09D5/031C09D5/033C09D163/00C08L63/00C08K13/02C08K2003/2241C08K3/04C08K2003/3045C08L67/00
Inventor 李景红王春方解晓雷潘高健
Owner NIPPON PAINT TIANJIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka