Water-based white pearly finish paint and preparation method thereof
A white and pearlescent technology, used in coatings, anti-corrosion coatings, etc., can solve the problems of low refractive index, yellow color, low weather resistance, etc., and achieve good acid and alkali resistance, weather resistance, and water resistance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] The preparation method of a kind of water-based white pearl finish paint described in the present embodiment 1 may further comprise the steps:
[0014] (1) Dilute 0.4 parts of thickener with 5% deionized water by weight to make a paste, add 0.1 parts of additives, stir evenly, and obtain mixed solution A;
[0015] (2) Add 0.3 parts of defoamer to 50 parts of water-based resin, stir at <1000r / min for 15 minutes, then add 0.1 part of pearlescent powder to obtain mixed solution B;
[0016] (3) Within 5 minutes, add 4 parts of solvent, deionized water, and 0.1 part of ammonia water dropwise to mixed solution B to obtain mixed solution C; the deionized water used in this step and the deionized water used in step (1) total 14 copies;
[0017] (4) Add the mixed solution A into the mixed solution C, and stir for 10 minutes at a rotation speed of 200 r / min to obtain the water-based white pearlescent topcoat.
Embodiment 2
[0019] A kind of preparation method of water-based white pearl finish paint described in present embodiment 2, comprises the following steps:
[0020] (1) Dilute 0.8 parts of thickener with 15% deionized water by weight to make a paste, add 0.4 parts of additives, stir well, and obtain mixed solution A;
[0021] (2) Add 0.7 parts of defoamer to 60 parts of water-based resin, stir at <1000r / min for 30 minutes, then add 0.5 parts of pearlescent powder to obtain mixed liquid B;
[0022] (3) Within 15 minutes, add 10 parts of solvent, deionized water, and 0.3 parts of ammonia water dropwise to mixed solution B to obtain mixed solution C; the deionized water used in this step and the deionized water used in step (1) total 28 copies;
[0023] (4) Add the mixed solution A into the mixed solution C, and stir for 30 minutes at a rotation speed of 400 r / min to obtain the water-based white pearlescent topcoat.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com