Processing process for collar points and sleeve caps of non-ironing shirt

A technology for processing technology and cuffs, which is applied in the field of clothing, can solve the problems of high friction, the influence of shirt strength, and the strength reduction of collar points and cuffs, so as to increase the number of times of washing resistance, ensure shape retention performance, and improve the quality of shirts. Effect

Inactive Publication Date: 2017-06-06
LUTAI TEXTILE
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even if the strength of the non-ironing fabric itself is qualified, after sewing, spraying resin, washing, pre-drying, flat pressing, ironing, baking and other processes, it will have a great impact on the strength of the shirt, especially the collar and sleeves of the shirt. There is a fusible interlining, which is relatively thick, and the absorbent resin is several times that of the shirt body. In addition, the friction of the industrial washing machine is large, and the collar and sleeves are angular, so the collar and sleeves are severely weakened, and appear Rubbing or fraying of the collar and cuffs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing process for collar points and sleeve caps of non-ironing shirt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1, concrete steps are as follows:

[0013] 1) The three-proof additive solution uses fluorine three-proof additive with a concentration of 10g / L. Before the shirt is finished without ironing, soak the shirt collar and sleeves in the three-proof additive solution for 30 seconds, and then wash the collar and sleeves with clean water. Sleeves, then dry at 30°C;

[0014] 2) Spray finishing solution: in the finishing solution, the concentration of Fusiping resin ELF is 120g / L, the concentration of Fusiping catalyst F-M is 30g / L, the concentration of organic silicon softener FMW is 40g / L, polyethylene protection The concentration of the agent HDP is 20g / L, the concentration of the surfactant MRZ is 3g / L, and the rest is water, and the shirt is sprayed to make the liquid-carrying rate 75%;

[0015] 3) Soak the collar and sleeves of the shirt in a phosphoric acid solution with a concentration of 5g / L for 20s, then wash the collar and sleeves with water, and then dry...

Embodiment 2

[0017] Embodiment 2, concrete steps are as follows:

[0018] 1) The three-proof auxiliary agent solution uses fluorine three-proof auxiliary agent with a concentration of 20g / L. Before finishing the shirt without ironing, soak the shirt collar and sleeves in the three-proof auxiliary agent solution for 25 seconds, and then wash the collar and sleeves with clean water. Sleeves, then dry at 40°C;

[0019] 2) Spray finishing liquid: in the finishing liquid, the concentration of Fusiping resin SW is 140g / L, the concentration of Fusiping catalyst F-M is 45g / L, the concentration of organic silicon softener NUP is 30g / L, and polyethylene protection The concentration of the agent CAN is 30g / L, the concentration of the surfactant MRZ is 5g / L, and the rest is water. Spray the shirt to make the liquid-carrying rate 80%;

[0020] 3) Soak the collar and sleeves of the shirt in a phosphoric acid solution with a concentration of 7g / L for 25s, then wash the collar and sleeves with water, and...

Embodiment 3

[0022] Embodiment 3, concrete steps are as follows:

[0023] 1) The three-proof additive solution uses fluorine three-proof additive with a concentration of 30g / L. Before finishing the shirt without ironing, soak the shirt collar and sleeves in the three-proof additive solution for 20 seconds, and then wash the collar and sleeves with clean water. Sleeves, then dry at 40°C;

[0024] 2) Spray finishing liquid: the concentration of F-AP Fusiping resin SW in the finishing liquid is 150g / L, the concentration of Fusiping catalyst F-M is 40g / L, the concentration of organic silicon softener NUP is 40g / L, poly The concentration of the vinyl protective agent CAN is 40g / L, the surfactant MRZ is 6g / L, and the rest is water. Spray the shirt to make the liquid carrying rate 80%;

[0025] 3) Soak the collar and sleeves of the shirt in a phosphoric acid solution with a concentration of 8g / L for 30s, then wash the collar and sleeves with water, and then dry them at 50°C;

[0026] 4) Pre-dry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention provides a processing process for collar points and sleeve caps of a non-ironing shirt. The processing process is characterized by comprising the following steps: (1) before the non-ironing finishing of the shirt, soaking the collar points and the sleeve caps of the shirt into a three-prevention aid solution, washing the collar points and the sleeve caps with clean water, and carrying out low-temperature drying; (2) spraying finishing liquid; (3) soaking the collar points and the sleeve caps of the shirt into a phosphoric acid solution, and washing with clean water; and (4) sequentially carrying out prebaking, pre-ironing, stereoscopic pressing, integral ironing and pressing and baking formation. According to the processing process, the collar points and the sleeve caps are subjected to aid isolation before the non-ironing finishing of the shirt, resin finishing liquid is sprayed to the shirt, and the resin at the collar points and the sleeve caps is peeled by virtue of the phosphoric acid solution, so that the shape maintenance performance of the non-ironing shirt is guaranteed, the washable number of times of the non-ironing shirt is increased, and the quality of the shirt can be greatly improved.

Description

technical field [0001] The invention relates to a treatment process for a non-ironing shirt collar and cuff, and belongs to the technical field of clothing. Background technique [0002] Shirts Non-ironing shirts have the advantages of good pleat effect, high appearance wrinkle level, strong three-dimensional effect, good softness, washability and wearability, etc., and are favored by customers. However, non-ironing shirt fabrics have undergone anti-wrinkle finishing such as mercerizing, open width, liquid ammonia moisture cross-linking, and pre-shrinking, and become fragile, lacking in stretchability, and low in strength. Even if the strength of the non-ironing fabric itself is qualified, after sewing, spraying resin, washing, pre-drying, flat pressing, ironing, baking and other processes, it will have a great impact on the strength of the shirt, especially the collar and sleeves of the shirt. There is a fusible interlining, which is relatively thick, and the absorbent res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/256D06M15/00D06M15/643D06M15/227D06M11/70
CPCD06M15/256D06M11/70D06M15/00D06M15/227D06M15/643D06M2200/20
Inventor 秦达刘红艳李凤霞
Owner LUTAI TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap