Production method of rolled thick-specification composite steel plate

A clad steel plate and production method technology, applied in the production of rolled clad plate with a thickness ≥ 50mm, and in the production field of rolled thick clad plate, can solve the problems such as difficulty in producing thick clad plate, and achieve a good and wide lamination effect The effect of applying the foreground

Inactive Publication Date: 2017-06-09
SHOUGANG CORPORATION
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a production method for rolling thick-gauge clad ste...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of rolled thick-specification composite steel plate
  • Production method of rolled thick-specification composite steel plate
  • Production method of rolled thick-specification composite steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] In this embodiment, Q345R is selected as the base layer material, and 316L is selected as the compound layer material. The specifications of the finished composite board are: (47+3)+(27+3) thickness×2040 width×12000 length mm, of which the thickness of Q345R is 47 and 27mm respectively, and the thickness of stainless steel is 3mm.

[0021] The production process includes billet assembly, heating, rolling, and water cooling, specifically:

[0022] (1) The steel billets designed and smelted according to the chemical composition are subjected to billet rolling; the thickness of the carbon steel Q345R billet is 247 and 142 mm respectively, and the thickness of the stainless steel intermediate billet is 16 mm. The surface cleaning of the composite surface is carried out by using a milling machine or an abrasive belt grinder. then follow figure 1 Combining the examples, adding a release agent between the stainless steels, and then welding and sealing the billet on four sides...

Embodiment 2

[0028] In this embodiment, A533B Class I is selected as the material of the base layer, and 304L is selected as the material of the multilayer. The finished product specifications of the composite board are: (62+7)+25 thickness×2040 width×12000 length mm, among which the thickness of A533B is 62 and 25mm respectively, and the thickness of stainless steel is 7mm.

[0029] The production process includes billet assembly, heating, rolling, and heat treatment, specifically:

[0030] (1) The steel billets designed and smelted according to the chemical composition are subjected to billet rolling; the carbon steel A533B billets have a thickness of 277 and 112mm, and the stainless steel intermediate billet has a thickness of 32mm. The surface of the composite surface is cleaned by a milling machine or an abrasive belt grinder. then follow figure 2 Example combination, stainless steel and thin-gauge carbon steel 112mm steel billet is added with a release agent, and the billet is then...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method of a rolled thick-specification composite steel plate, and belongs to the technical field of metal composite plate production. The composite steel plate is produced by surface treatment of a base plate and a composite plate, ply rolling, welding and vacuumizing of a matching board, wherein the vacuum degree is 10<-3> Pa to 10<-2> Pa; rolling and thermal treatment, wherein the rolling temperature is 1100-1200 DEG C, and the pressing rate for single time is 8-25%; separate cutting and flaw detection, detection, finishing and package. The production method has the advantages of realizing the production of the composite steel plate of which thickness is not less than 50 mm; the composite effect is good; the interface shearing intensity is 210 MPa or above; the performance of every layer can meet the standard requirement of corresponding materials.

Description

technical field [0001] The invention belongs to the technical field of metal composite plate production, and in particular relates to a production method for rolling thick-gauge composite steel plates. In particular, it relates to a production method for rolling a composite plate with a thickness greater than or equal to 50 mm. It is suitable for the production of thick-gauge stainless steel, nickel-based alloy and other clad steel plates for petroleum, chemical, nuclear power and other fields. Background technique [0002] As a new type of energy-saving and environmentally friendly functional materials, bimetallic clad steel plates such as stainless steel are widely used in petrochemical, water conservancy, salt production, nuclear power and other fields. At present, this kind of bimetallic composite panels is mainly produced by rolling method and explosion method in China. Among them, the explosion method is often used to produce thick specification composite panels in Ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B37/14B32B37/10B32B37/06B32B38/18B32B38/00
CPCB32B37/144B32B37/06B32B37/10B32B38/0012B32B38/1858B32B2038/0016
Inventor 王小勇王志勇孙启昆黄乐庆马长文罗家明白学军王东王华鹏王海宝秦丽晔
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap