Oil-soluble high molecular surfactant and preparation method thereof

A technology of surfactants and oil-soluble initiators, applied in the field of oil-soluble polymer surfactants and their preparation, can solve the problems of few reports, no effect, poor effect, etc., and achieve good product stability and stability Effect

Inactive Publication Date: 2017-06-09
山东鲁岳化工集团有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are few lipophilic polymer surfactants on the market, especially for inverse suspension polymerization. The effect is very poor or even ineffective; the mature oil-soluble polymer surfactant technology of foreign companies and colleges is top secret, and there are few reports in the literature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The embodiment of the present invention provides a kind of preparation method of oil-soluble polymer surfactant, and described method comprises the following steps:

[0024] S101: Stir 200 parts by weight of an organic hydrocarbon solvent and 0.01-0.1 parts by weight of an oil-soluble initiator evenly under air-isolated conditions, and then heat to 70-80°C to obtain a mixture A;

[0025] S102: Mix 1000 parts by weight of organic hydrocarbon solvent, 500-800 parts by weight of substance A, 500-800 parts by weight of substance B, and 50-80 parts by weight of substance C at 20-25°C, and then add 10 -20 parts by weight of the oil-soluble initiator, until completely dissolved, to obtain mixture B;

[0026] S103: adding the mixture B to the mixture A dropwise under the condition of cutting off the air, the dropping time is 6-8 hours, and keeping it warm for 1-2 hours after the dropping is completed, to obtain an oil-soluble polymer surfactant;

[0027] Wherein, the substance...

Embodiment 1

[0036] The present embodiment provides a kind of preparation method of oil-soluble polymer surfactant, described method is carried out according to the following steps:

[0037] S101: Add 2kg of gasoline and 0.1g of azobisisobutyronitrile into the reaction kettle, turn on the stirring device in the reaction kettle under the protection of nitrogen to stir evenly, and then heat to 70°C by using a water bath heating method to obtain a mixture A;

[0038] S102: Mix 10kg of gasoline, 5kg of lauryl methacrylate, 5kg of butyl methacrylate, and 0.5kg of dimethylaminoethyl methacrylate at 20°C, and then add 0.1kg of azobisisobutyronitrile to Dissolve completely to obtain mixture B;

[0039] S103: Add the mixture B into the reaction kettle through the dropping pump, finish the dropwise addition for 6 hours, and keep warm for 1 hour after the dropping, to obtain an oil-soluble polymer surfactant; the reaction kettle is continuously ventilated with nitrogen for protection during the dropp...

Embodiment 2

[0041] The present embodiment provides a kind of preparation method of oil-soluble polymer surfactant, described method is carried out according to the following steps:

[0042]S101: Add 2kg of kerosene and 1g of azobisisovaleronitrile into the reaction kettle, turn on the stirring device in the reaction kettle under the protection of nitrogen to stir evenly, and then heat it to 80°C by using a water bath heating method to obtain a mixture A;

[0043] S102: Mix 10kg of kerosene, 8kg of tetradecyl methacrylate, 8kg of methyl acrylate, and 0.8kg of dimethylaminoethyl acrylate at 25°C, then add 0.2kg of azobisisovaleronitrile until completely dissolved , to obtain mixture B;

[0044] S103: Add the mixture B into the reaction kettle through the dropping pump, finish the dropwise addition for 8 hours, and keep warm for 2 hours after the dropping, to obtain an oil-soluble polymer surfactant; the reaction kettle is continuously ventilated with nitrogen for protection during the dropp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an oil-soluble high molecular surfactant and a preparation method thereof. The preparation method comprises the following three steps: firstly, preparing a mixture A, preparing a mixture B, and dropping the mixture into the mixture A droplet by droplet, so as to obtain the oil-soluble high molecular surfactant. The oil-soluble high molecular surfactant prepared by using the method provided by the invention can be used as a stabilizer of a reversed phase suspension polymerization process, and has the advantages of being good in stability, good in high temperature resistance, acid-alkali resistance and uniform and stable in particle size of formed granular products.

Description

technical field [0001] The invention relates to the technical field of chemical additives, in particular to an oil-soluble polymer surfactant and a preparation method thereof. Background technique [0002] At present, there are few lipophilic polymer surfactants on the market, especially for inverse suspension polymerization. The effect is very poor or even has no effect; the mature oil-soluble polymer surfactant technology of foreign companies and colleges is top secret, and there are few reports in the literature. Contents of the invention [0003] The invention aims at the deficiencies of the prior art, and provides a preparation method of an oil-soluble high molecular surfactant used for reverse-phase suspension polymerization, so that the product of reverse-phase suspension polymerization has good stability. [0004] The present invention is achieved through the following technical solutions, providing a preparation method of an oil-soluble polymer surfactant, said m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F220/18C08F220/34C08F220/14C08F220/06C08F220/32C08F2/32
CPCC08F2/32C08F220/14C08F220/18C08F220/1812C08F220/1818C08F220/325C08F220/1804C08F220/34C08F220/06
Inventor 彭程刘培宝刘洪楼
Owner 山东鲁岳化工集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com