System and method for preparing ultra-high water filling materials with organic wastewater and industrial solid waste

A technology for organic waste water and filling materials, applied in cement production and other directions, can solve the problems of large investment in incineration method equipment, difficulty in applying incineration method to organic waste water, and high treatment costs, so as to achieve energy utilization, avoid occupation and pollution, and improve economy. effect of benefit

Active Publication Date: 2019-04-02
SHANDONG UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the incineration method has the disadvantages of large equipment investment and high treatment cost. Except for some special wastewater (such as hospital wastewater that needs to be disinfected and sterilized), this method must be used, and it is difficult to use the incineration method to treat general organic wastewater.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • System and method for preparing ultra-high water filling materials with organic wastewater and industrial solid waste
  • System and method for preparing ultra-high water filling materials with organic wastewater and industrial solid waste
  • System and method for preparing ultra-high water filling materials with organic wastewater and industrial solid waste

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0088] Prepare according to the above-mentioned system and the above-mentioned process, and its specific parameters are as follows: pulverize the coal gangue, and carry out batching with aluminum ash, carbide slag, and desulfurized gypsum. In terms of solid matter, the coal gangue accounts for 25 parts by weight, and the desulfurized gypsum accounts for 17 parts by weight. parts, calcium carbide slag accounts for 40 parts by weight, aluminum ash accounts for 18 parts by weight, and iron tailings accounts for 8 parts by weight. After the materials are blended, they are ground and homogenized. After being filtered, they are directly transported into the rotary kiln for calcination. The calcination temperature is 1270°C and the calcination time is 80 minutes. The main phases of the clinker after firing are calcium sulfoaluminate and dicalcium silicate. Take the above base material, add 1.0% of the mass of the base material as quick-setting agent, 1.5% of expansion agent, and 1.5%...

Embodiment 2

[0090] Prepare according to the above-mentioned system and the above-mentioned process, and its specific parameters are as follows: crush the coal gangue, and carry out batching with aluminum ash, carbide slag, and desulfurized gypsum. In terms of solid matter, the coal gangue is 23 parts by weight, and the desulfurized gypsum is 22 parts by weight. parts, calcium carbide slag is 35 parts by weight, aluminum ash is 20 parts by weight, and iron tailings is 11 parts by weight. After the materials are blended, they are ground and homogenized. After being filtered, they are directly transported into the rotary kiln for calcination. The calcination temperature is 1350°C and the calcination time is 80 minutes. Take the above base material, add 0.5% of the mass of the base material as quick-setting agent, 1.5% of expansion agent, and 1.0% of dispersant, and take another 97 parts of water, the quality of each 2 parts of water is the same as that of the above-mentioned base material, an...

Embodiment 3

[0092] Prepare according to the above-mentioned system and the above-mentioned process, and its specific parameters are as follows: crush the coal gangue, and carry out batching with aluminum ash, carbide slag, and desulfurized gypsum. In terms of solid matter, the coal gangue is 21 parts by weight, and the desulfurized gypsum is 20 parts by weight. parts, calcium carbide slag is 37 parts by weight, aluminum ash is 15 parts by weight, and iron tailings is 15 parts by weight. After the materials are blended, they are ground and homogenized. After being filtered, they are directly transported into the rotary kiln for calcination. The calcination temperature is 1350°C and the calcination time is 75 minutes. Take the above base material, add 1.0% quick-setting agent, 0.5% expansion agent, and 1.5% dispersant of the base material mass, and take another 97 parts of water, the quality of every 2 parts of water is the same as that of the above base material, and mix thoroughly Prepara...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
heating valueaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a system and a method for preparing ultra-high water filling materials by organic wastewater and industrial solid waste. The system comprises a wet pulverizer, a pressure filter, an equalizing basin, a rotary kiln and an indirect heat exchanger. Desulfurized gypsum, aluminum ash, carbide slag, coal gangue, iron tailings and part of the organic wastewater are mixed to obtain mixed solution, the water content of the mixed solution is 60%-70% (mass), the mixed solution is pulverized by a wet process, wet pulverized materials are equalized to obtain slurry, the slurry is mechanically pressed, filtered and dewatered to obtain paste, the other part of the organic wastewater is concentrated, then enters the rotary kiln together with the paste and calcined at high temperature to obtain base materials, pulverized coal is sprayed into the rotary kiln in the high-temperature calcining process, so that the pulverized coal and organic matters in the mixed paste are burnt, and finally, the base materials, accelerators, dispersants, expanding agents and water are prepared into the ultra-high water filling materials. The system and the method can be used for preparing the novel ultra-high water filling materials by reusing the industrial solid waste.

Description

technical field [0001] The invention relates to a system and a method for preparing ultra-high water filling materials by cooperating with organic waste water and industrial solid waste. Background technique [0002] The development of backfill technology in coal mines and other mined-out areas has been relatively lagging behind, which reduces the efficiency of mining, increases the cost of mining, and causes reduced safety hazards to society and the environment. As a new backfill material, ultra-high water filling material has attracted more and more attention. Ultra-high water filling materials must have good performance before they can be used in goaf filling replacement mining. Specifically, they should have the following basic properties: 1. The compressive strength of the solidified filling material should exceed 2MPa; 2. It must have good 3. Appropriate curing characteristics (mainly refers to the initial setting time and final setting time of the material); 4. Compa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/24
CPCC04B7/24Y02P40/10
Inventor 王文龙刘晓斌孙静宋占龙赵希强毛岩鹏
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com