Chemically-crosslinked mixed gelled electrolyte of lead-acid storage battery

A technology of colloidal electrolyte and lead-acid battery, which is applied in the direction of lead-acid battery, electrolyte immobilization/gelation, etc. It can solve the problems of unstable performance of organic glue, poor performance of inorganic glue, and little improvement in performance. It achieves the effects of fast charging and large current discharge performance, low production cost, and wide application range of battery temperature

Active Publication Date: 2017-06-20
JIANGSU AOXIN TECH DEV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] At present, the colloidal electrohydraulic used in lead-acid batteries uses organic glue or inorganic glue alone, but the single use of organic glue or inorganic glue will have certain disadvantages: the performance of inorganic glue is poor in the early stage, and the performance of organic glue is unstable in the later stage
Although organic and inorganic adhesives have been mixed mechanically and physically, the performance has not seen much improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chemically-crosslinked mixed gelled electrolyte of lead-acid storage battery
  • Chemically-crosslinked mixed gelled electrolyte of lead-acid storage battery
  • Chemically-crosslinked mixed gelled electrolyte of lead-acid storage battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0035] Example: A chemically cross-linked lead-acid storage battery mixed colloidal electrolyte, the specific process formula is: prepare 1050KG mixed gel, wherein organic glue 300KG, inorganic glue 600KG, succinic acid 50KG, adipic acid 100KG.

[0036] 1. Configure inorganic glue and organic glue first:

[0037] Inorganic glue including 10-20% SiO 2 , 70-85% water, 0.01%-0.1% stabilizer and 5-10% caustic soda, first cut SiO at a high speed with a high-speed shearing machine with a linear speed of about 4000 rpm 2 15min, forming gas phase SiO 2 ; Then mix the stabilizer and water uniformly at 1:200-1:1000, caustic soda and water at the ratio of 1:4-1:6 and add gas phase SiO 2 Among them, it is configured as inorganic glue.

[0038] Organic glue is made of SiCl 4 It is a high-molecular polymer in which the monomer undergoes high-temperature polymerization reaction at a high temperature of more than 1200°C, and when it reaches a molecular weight of 400-800, it forms a visco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a chemically-crosslinked mixed gelled electrolyte of a lead-acid storage battery. The chemically-crosslinked mixed gelled electrolyte is prepared from an original adhesive and sulfuric acid in a matching manner; the original adhesive is a chemically-crosslinked mixed adhesive, and specifically comprises an inorganic adhesive, an organic adhesive and a crosslinking agent; the crosslinking agent is butanedioic acid and adipic acid, wherein the organic adhesive accounts for 25-30% of the total weight of the adhesive; the inorganic adhesive accounts for 50-60% of the total weight of the adhesive; the butanedioic acid accounts for 4-8% of the total weight of the adhesive; and the adipic acid accounts for 8-16% of the total weight of the adhesive. The organic and inorganic mixed adhesive prepared by the chemical crosslinking method is taken as the electrolyte of the lead-acid storage battery; the chemically-crosslinked organic and inorganic mixed adhesive has the characteristic (relatively good post-period performance) of the inorganic adhesive as well as the characteristic (relatively stable front-period performance) of the organic adhesive, and is safe and reliable, not hydrolyzed within the life cycle and not degraded; and in addition, the electrolyte has low production cost, easy realization of industrialization, wide battery temperature applicable range, high rapid and high-current discharging performance and high capacity, and deep cycle life and discharging service life are both prolonged.

Description

technical field [0001] The invention relates to the technical field of lead-acid batteries, in particular to colloidal electrolytes for lead-acid batteries. Background technique [0002] colloid is a H 2 SO 4 A kind of electro-hydraulic fixed in colloidal materials that does not flow is beneficial to energy storage batteries used in deep-cycle power batteries and high-temperature environments. Colloidal electrolytes include inorganic glue and organic glue. [0003] Inorganic glue: generally refers to silicic acid colloid, SiO 2 It is silicic anhydride, which is acidic and can be written as H 4 SiO 4 , which is alkaline and can be written as Si(OH) 4 . [0004] Monomolecular silicic acid is uncharged, neutral molecule, small surface area and unstable. It is prone to polymerization at room temperature to form polysilicic acid. Generally, there are 4-12 monomers. In order to make SiO 2 The particles are stable and not polymerized. Stabilizers (such as polyamide, pectin, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/10
CPCH01M10/10H01M2300/0085Y02E60/10
Inventor 戴德兵李中奇王永陈云涛
Owner JIANGSU AOXIN TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products