A kind of photocrosslinkable hydrogel and preparation method thereof

A cross-linked hydrogel, photosensitive technology, applied in the field of hydrogel, can solve the problem of low mechanical strength of keratin hydrogel, which restricts the deep application of keratin hydrogel, and takes 10 or several hours Time and other issues, to achieve the effect of short gelation time, mild conditions and good biocompatibility

Active Publication Date: 2020-06-19
DONGHUA UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some of these methods have a long gelation time, which takes more than 10 hours or several days; the mechanical strength of keratin hydrogel obtained by some methods is low; some methods need to use toxic chemical cross-linking agents, such as glutaraldehyde, etc. , to form a three-dimensional cross-linked network structure
These problems have restricted the deep application of keratin hydrogels to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of photocrosslinkable hydrogel and preparation method thereof
  • A kind of photocrosslinkable hydrogel and preparation method thereof
  • A kind of photocrosslinkable hydrogel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Add 0.0005 g of cysteine ​​powder to 2 mL of PBS buffer, then add 0.02 g of Irgacure 2959, fully dissolve at 50° C., and then add 0.1 g of keratin powder. Stir to dissolve and then irradiate under ultraviolet light. The method resulted in the formation of keratin gels, i.e., photocrosslinkable hydrogels, within 4 days. For a physical picture of the gel, see figure 1 .

Embodiment 2

[0036] Add 0.003 g of dithiothreitol powder to 2 mL of PBS buffer, then add 0.01 g of Irgacure 2959, fully dissolve at 50° C., and then add 0.1 g of keratin powder. Stir to dissolve and then irradiate under ultraviolet light. The method can form a keratin gel within 50 minutes, that is, a photocrosslinkable hydrogel. For a physical picture of the gel, see figure 2 .

Embodiment 3

[0038] Add 0.003 g of glutathione powder to 2 mL of PBS buffer, then add 0.02 g of Irgacure 2959, fully dissolve at 50° C., and then add 0.2 g of keratin powder. Stir to dissolve and then irradiate under ultraviolet light. The method can form a keratin gel within 20 minutes, that is, a photocrosslinkable hydrogel. For a physical picture of the gel, see image 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to photo-crosslinkable hydrogel and a preparation method thereof. A matrix of the hydrogel comprises keratin; the keratin contains a plurality of free sulfhydryl groups. The preparation method comprises the following steps: dissolving the keratin into a buffering solution, and adding a photoinitiator; after sufficiently dissolving, illuminating under an ultraviolet lamp to form the photo-crosslinkable hydrogel. According to the hydrogel provided by the invention, the gelling time of materials is short, and the mechanical strength is high; the photo-crosslinkable hydrogel can be used for in-vivo injection and gelling, and has wide application value in the aspects of biomedicines, tissue engineering, medicine delivery and the like.

Description

technical field [0001] The invention belongs to the field of hydrogels, in particular to a photocrosslinkable hydrogel and a preparation method thereof. Background technique [0002] Hydrogel is a hydrophilic cross-linked three-dimensional polymer network material that can swell in water and retain a large amount of water without dissolving. Hydrogel has superior water absorption performance, and has good responsiveness to the external environment, storage stability, strength and softness, and exhibits good biocompatibility. It has great potential in biomedicine, tissue engineering and drug delivery. High application value. [0003] The crosslinking methods of hydrogel usually include chemical crosslinking, physical crosslinking, high energy radiation crosslinking, photocrosslinking and so on. The photocrosslinking method can be quickly formed within a few minutes under normal temperature and pressure, and the reaction conditions are mild, and the process is easy to contro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/075C08J3/28C08J3/24C08L89/00
CPCC08J3/075C08J3/24C08J3/28C08J2389/00
Inventor 杨光姚依茜曹禺李炎李颖
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap