A kind of natural color bamboo pulp for reconstituted tobacco additive and preparation method thereof

A technology of natural bamboo pulp and reconstituted tobacco, applied in the direction of tobacco, tobacco processing, application, etc., can solve the problems of reduced production cost, lack of forest resources, weakened dependence, etc.

Active Publication Date: 2018-10-26
SICHUAN UNIVERSITY OF SCIENCE AND ENGINEERING
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] People in the industry believe that the best raw material for "external fiber" is bleached coniferous wood fiber, while my country's wood and hemp as "external fiber" are constrained by factors such as planting area, growth cycle, ecological balance, production cost, and environmental protection. In addition, my country's forest resources are scarce, and the country attaches great importance to ecological protection, making it difficult for the domestic supply of wood fiber raw materials to meet the raw material needs of related industries for a long time in the future. Therefore, how to develop a new type of natural and regenerated cellulose fiber suitable for my country's national conditions to make up for the shortage of raw materials and meet the market's demand for reconstituted tobacco, on the one hand, there is a new kind of new product in the field of reconstituted tobacco production. New sustainable renewable raw materials can reduce the dependence of related enterprises on imported wood pulp, save foreign exchange expenses, promote the healthy and sustainable development of the industry, and greatly reduce production costs; on the other hand, through product differentiation, not only can the enterprise Profits can also stimulate the development of related industries and form a benign interactive development of forestry pulp integration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of natural color bamboo pulp for reconstituted tobacco additive and preparation method thereof
  • A kind of natural color bamboo pulp for reconstituted tobacco additive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] (1) Directly cut the bamboo into 10-50mm long and 5-20mm wide, adopt the dry method, remove impurities such as mud sand, knots and shavings by a dust collector, and send it to a cooking pot for alkaline cooking after dust removal. The liquid ratio is 1 : 6, relative to the absolute dry raw material quality, the amount of alkali used is 30% (Na 2 O meter), dihydroanthraquinone 0.5%, sodium dodecyl benzene sulfonate 0.1%, sulfurization degree 15%.

[0046] The cooking curve is: raise the temperature to 150°C within 90min, the corresponding pressure in the pot is about 0.48MPa, then put the pot until the pressure in the pot is 0MPa, then heat up to the maximum temperature of 150°C, and keep at this temperature for 80min until the end of cooking.

[0047] (2) Concentration: the slurry obtained in step (1) is put into the spraying pot, and is concentrated by waste liquid extraction, screening and concentrator, and the mass concentration of the concentrated slurry is 20%;

...

Embodiment 2

[0062] (1) directly cut bamboo into 10-50mm length, 5-20mm width, adopt wet method, wash off surface impurities and remove excess water after the grass washer, enter the digester to carry out alkaline cooking, and the liquid ratio is 1: 3. Relative to the absolute dry raw material quality, the amount of alkali used is 15% (calculated as Na2O), 0.6% of tetrahydroanthraquinone, 0.2% of xylene sulfonic acid, and 30% of sulfurization degree.

[0063] The cooking curve is: raise the temperature to 148°C within 90min, corresponding to a pressure of about 0.45MPa in the pot, then put the pot until the pressure in the pot is 0MPa, then heat up to a maximum temperature of 148°C, and keep at this temperature for 80min until the end of cooking.

[0064] (2) Concentration: the slurry obtained in step (1) is put into a spray pot, and is concentrated by waste liquid extraction, screening and concentrator, and the mass concentration of the concentrated slurry is 30%;

[0065] (3) Extrusion d...

Embodiment 3

[0075] (1) Directly cut the bamboo into 10-50mm long and 5-20mm wide, adopt the dry method, remove impurities such as mud sand, knots and shavings by a dust collector, and send it to a cooking pot for alkaline cooking after dust removal. The liquid ratio is 1 : 4, relative to the absolute dry raw material quality, the amount of alkali used is 20% (Na 2 O meter), dihydrodihydroxyanthraquinone 1.0%, alkylphenol polyoxyethylene ether sodium sulfate 0.1%, vulcanization degree 20%.

[0076] The cooking curve is as follows: the temperature is raised to 152°C within 90min, the corresponding pressure in the pot is about 0.50MPa, then the pot is placed in the pot until the pressure in the pot is 0MPa, then the temperature is raised to the maximum temperature of 152°C, and the temperature is kept for 80min until the end of cooking.

[0077] (2) Concentration: the slurry obtained in step (1) is put into a spray pot, and is concentrated by waste liquid extraction, screening and concentrat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of reconstituted tobacco, and specifically relates to natural-color bamboo pulp for a reconstituted tobacco additive and a preparation method thereof. The method is characterized in that bamboo is used as the raw material and subjected to preparing, stewing, squeezing extrusion, dipping, pulping and papermaking to obtain a high-purity product. The physical performance indexes of the natural-color bamboo pulp are that the tensile index is 35-45N-m / g; the burst index is 2.5-3.5kPa-m<2> / g; the tearing index is 6.5-9.5mN-m<2> / g; the intrinsic viscosity is 800-1000mL / g; the whiteness is 30-40% ISO; the pentosane is less than 8%; the ash content is less than 1.0%; the bulk is 5.0-8.5cm<3> / g. The prepared tobacco slices are added to finished cut tobacco based on ratio; the prepared cigarette is capable of supplying more air intake quantity while smoking, so that the cigarette can be promoted to completely burn, and the quantity of pyrolysis products under oxygen-poor condition can be effectively decreased, and as a result, the releasing quantity of harmful components such as tar and nicotine can be decreased.

Description

technical field [0001] The invention belongs to the technical field of reconstituted tobacco by a papermaking method, and particularly relates to a method for preparing natural bamboo pulp for tobacco additives by using bamboo as raw materials, in particular to a natural bamboo pulp for reconstituting tobacco additives and a preparation method thereof. Background technique [0002] Reconstituted tobacco is tobacco sheet, which is used in cigarette formulations in the form of an auxiliary material. It can reduce the consumption of tobacco leaves, reduce production costs, and effectively reduce the content of tar, nicotine, CO release and other harmful components in cigarettes. Cigarette safety, regulation of cigarette taste, etc. [0003] At present, the most widely used paper-making tobacco sheet production process in China is to use tobacco waste such as tobacco stems and tobacco chips as raw materials, extract and separate the water-soluble substances in the raw materials,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A24B15/18
CPCA24B15/18
Inventor 杨玲彭成高洪霞庞春霞李文俊于成龙王云凤肖林张豪王尧刘泽覃苏鹏杨睿婕
Owner SICHUAN UNIVERSITY OF SCIENCE AND ENGINEERING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products