Manufacturing method of microbubble type solid toilet soap

A manufacturing method and solid technology, applied in the direction of forming soap, chemical equipment and methods, alkali soap/ammonium soap composition, etc., can solve the problems of affecting carbon dioxide, low pressing efficiency, loss of organic acid, etc., and achieve enhanced foaming effect , Improve production efficiency and simplify production difficulty

Active Publication Date: 2020-03-24
深圳市启聆科技有限责任公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method involves pressing the organic acid into the porous silica. Since the porous silica has a microporous structure, the pore size is small, and the pressing efficiency is low.
Secondly, porous silica containing organic acids needs to be stored in microcapsules with a slow-release structure. Although the coexistence of organic acids and weak bases can be well achieved, it is also easy to cause the loss of organic acids during use, which affects the carbon dioxide production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The manufacture method of microfoam type solid toilet soap is as follows:

[0027] (1), raw materials such as soap base, bicarbonate and organic acid are equipped in proportion, in the present embodiment, by weight percentage, get 98% soap base, 1.14% bicarbonate, 0.86% organic acid, Divide the soap base into several parts of equal weight, and divide the bicarbonate and organic acid into several equal parts; among them, the bicarbonate can be any one of potassium bicarbonate, sodium bicarbonate and magnesium bicarbonate Or multiple, in the present embodiment, bicarbonate only selects sodium bicarbonate for use.

[0028] (2), spreading a portion of soap base on a thin-layered base layer in the mold, and drying it;

[0029] (3), evenly spread a portion of bicarbonate on the surface of the base layer and compact and dry;

[0030] (4), spread another portion of soap base on the surface of the layer formed through step (3), and carry out compaction and drying treatment;

...

Embodiment 2

[0037] (1), raw materials such as soap base, bicarbonate and organic acid are equipped in proportion, in the present embodiment, by weight percentage, get 87.0% soap base, 7.4% bicarbonate, 5.6% organic acid, Divide the soap base into several parts of equal weight, and divide the bicarbonate and organic acid into several parts with equal parts;

[0038] Wherein, the bicarbonate in the raw material can be selected bicarbonate can be selected any one or more in potassium bicarbonate, sodium bicarbonate and magnesium bicarbonate, and the soap base can adopt the soap base commonly used in the existing general solid toilet soap, Also can adopt the soap base among the embodiment 1, what organic acid adopted is malic acid.

[0039] Steps (2) to (5) are the same as in Example 1.

Embodiment 3

[0041] (1), raw materials such as soap base, bicarbonate and organic acid are equipped in proportion, in the present embodiment, by weight percentage, get 72% soap base, 15.9% bicarbonate, 12.1% organic acid, Divide the soap base into several parts of equal weight, and divide the bicarbonate and organic acid into several parts with equal parts;

[0042] Wherein, the bicarbonate in the raw material can be selected bicarbonate can be selected any one or more in potassium bicarbonate, sodium bicarbonate and magnesium bicarbonate, and the soap base can adopt the soap base commonly used in the existing general solid toilet soap, Also can adopt the soap base among the embodiment 1, what organic acid adopted is lactic acid.

[0043] Steps (2) to (5) are the same as in Example 1.

[0044] In Example 2 and Example 3, by increasing the content of bicarbonate and organic acid in the solid soap related to the present invention, the total content of the bubbles that the solid soap can pro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacture method of microbubble solid soap; as organic acids and bicarbonates are added into existing known soap base for solid soap, the solid soap can generate massive carbon dioxide in case of contact with water. The manufacture method has the advantages that the organic acid content in the solid soap can be increased with bubbling effect of the soap improved; the solid soap manufactured by the manufacture method can generate carbon dioxide bubbles when in contact with water, and deterging capacity of the soap can be enhanced through bursting force generated by breakage of bubbles.

Description

technical field [0001] The invention relates to a method for manufacturing solid soap, in particular to a method for manufacturing microfoam solid soap. Background technique [0002] In the use of solid soap, the foaming degree is one of the indicators that consumers pay close attention to. In the past soaps, a higher foaming degree was achieved by adding various foaming agents or adjusting different ratios. But this kind of bubble needs to be rubbed to produce, and because the internal and external air pressure is consistent, its rupture cannot bring higher cleaning ability. Later, solid soaps containing sodium bicarbonate to generate carbon dioxide appeared. [0003] The existing disclosed manufacturing method of solid soap that can generate carbon dioxide, such as publication number CN 106398923A discloses a manufacturing method of solid cosmetic soap that generates carbon dioxide, which uses the principle of acid-base reaction to release carbon dioxide gas to generate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C11D9/02C11D9/12C11D9/26C11D9/60C11D13/18
CPCC11D9/02C11D9/12C11D9/26C11D13/18
Inventor 钟柏华韩伟常青柳章
Owner 深圳市启聆科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap