Intumescent fireproof adhesive used for fireproof door and preparation method of adhesive

An intumescent, fire-resistant adhesive technology, applied in the direction of adhesives, adhesive types, natural rubber adhesives, etc., can solve the problems of unsatisfactory fire resistance and heat insulation, high preparation cost, small expansion coefficient, etc. Operating time, stable coating effect, and effect of improving flame retardancy

Inactive Publication Date: 2017-08-22
合肥市旺友门窗有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the main component of silicate inorganic fireproof adhesive is sodium silicate, so its water resistance is poor and its adhesion is small; while the composition of general polymer organic fireproof adhesive is complicated, which leads to cumbersome process and high production cost.
Since the silicate inorganic fireproof adhesive has a small expansion coefficient when heated, and the polymer organic fireproof adhesive is seriously carbonized and decomposed when heated, it has no filling effect on the gap left in the process of bonding the door core board, so their fireproof performance and poor thermal insulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] An intumescent fireproof adhesive for fire doors, comprising the following raw materials:

[0026] 65 parts of rubber;

[0027] 55 parts of flame retardant microcapsules;

[0028] 50 parts of liquid sodium silicate;

[0029] 47 parts of expanded graphite;

[0030] 40 parts of glycerin;

[0031] 36 parts of spherical closed-cell expanded perlite;

[0032] Hypophosphite 30 parts;

[0033] 15 parts of auxiliary agent;

[0034] 45 parts of water;

[0035] The flame retardant microcapsules include the following raw materials: 25 parts of phenolic resin, 20 parts of absolute ethanol and 15 parts of flame retardant;

[0036] The auxiliary agent includes the following raw materials: 3 parts of char-forming agent, 3 parts of water-retaining thickener, 2 parts of lubricant, 1 part of dispersant, 1 part of char-forming auxiliary agent, 0.2 parts of heat-resistant stabilizer and rheological 0.2 parts of the agent.

[0037] Wherein, the rubber is natural rubber.

[0038] W...

Embodiment 2

[0048] An intumescent fireproof adhesive for fire doors, comprising the following raw materials:

[0049] 75 parts of rubber;

[0050] 65 parts of flame retardant microcapsules;

[0051] 53 parts of liquid sodium silicate;

[0052] 49 parts of expanded graphite;

[0053] 45 parts of glycerin;

[0054] 38 parts of spherical closed-cell expanded perlite;

[0055] Hypophosphite 35 parts;

[0056] 20 parts of auxiliary agent;

[0057] 65 parts of water;

[0058] The flame retardant microcapsules include the following raw materials: 27 parts of phenolic resin, 23 parts of absolute ethanol and 17 parts of flame retardant;

[0059] The auxiliary agent includes the following raw materials: 6 parts of char-forming agent, 6 parts of water-retaining thickener, 3 parts of lubricant, 2 parts of dispersant, 2 parts of char-forming auxiliary agent, 1.2 parts of heat-resistant stabilizer and rheological 0.8 parts of the agent.

[0060] Wherein, the rubber is styrene-butadiene rubber....

Embodiment 3

[0071] An intumescent fireproof adhesive for fire doors, comprising the following raw materials:

[0072] 70 parts of rubber;

[0073] 60 parts of flame retardant microcapsules;

[0074] 51.5 parts of liquid sodium silicate;

[0075] 48 parts of expanded graphite;

[0076] 42.5 parts of glycerin;

[0077] 37 parts of spherical closed-cell expanded perlite;

[0078] Hypophosphite 32.5 parts;

[0079] 17.5 parts of auxiliary agent;

[0080] 55 parts of water;

[0081] The flame retardant microcapsules include the following raw materials: 26 parts of phenolic resin, 21.5 parts of absolute ethanol and 16 parts of flame retardant;

[0082] The auxiliary agent includes the following raw materials: 4.5 parts of char-forming agent, 4.5 parts of water-retaining thickener, 2.5 parts of lubricant, 1.5 parts of dispersant, 1.5 parts of char-forming auxiliary agent, 0.7 part of heat-resistant stabilizer and rheological 0.5 parts of the agent.

[0083] Wherein, the rubber is butadi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an intumescent fireproof glue for fireproof doors and a preparation method thereof, relates to the field of fireproof materials, and comprises the following raw materials in parts: 65~75 parts of rubber, 55~65 parts of flame retardant microcapsules, liquid silicon 50~53 parts of sodium bicarbonate, 47~49 parts of expanded graphite, 40~45 parts of glycerin, 36~38 parts of spherical closed-cell expanded perlite, 30~35 parts of hypophosphite, 15~20 parts of additives and 45~ 65 servings. The invention is easy to construct, and can expand violently under flame or high temperature to form a fire-resistant and heat-insulating layer to prevent flame and smoke from spreading and achieve ideal fireproof performance.

Description

technical field [0001] The invention relates to the field of fireproof materials, in particular to an intumescent fireproof adhesive for fireproof doors and a preparation method thereof. Background technique [0002] At present, the adhesives used in the fire door industry mainly fall into the following two categories: silicate inorganic fireproof adhesives and polymer organic fireproof adhesives. Among them, the main component of silicate inorganic fireproof adhesive is sodium silicate, so its water resistance is poor and its adhesion is small; while the composition of general polymer organic fireproof adhesive is complicated, which leads to cumbersome process and high production cost. Since the silicate inorganic fireproof adhesive has a small expansion coefficient when heated, and the polymer organic fireproof adhesive is severely carbonized and decomposed when heated, it has no filling effect on the gap left in the process of bonding the door core board, so their firepro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J107/00C09J109/06C09J109/00C09J11/04C09J11/06C09J11/08
CPCC09J107/00C08K2003/2224C08K2003/2227C08K2003/329C08K2201/014C08L2201/02C08L2205/035C09J11/04C09J11/06C09J11/08C09J109/00C09J109/06
Inventor 朱明超
Owner 合肥市旺友门窗有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap