Black-purple-color frosted glaze, preparation method and use method thereof

A frosted glaze and purple technology, which is applied in the field of black-purple frosted glaze and its preparation, can solve the problems of high cost and complicated glazing process, and achieve the effects of low preparation cost, improved appearance quality and stable effect

Inactive Publication Date: 2017-08-29
NORTHEASTERN UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing ceramic glazes need to add various pigments and additives, the cost of glaze preparation is high, and the glaze application process is relatively complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The preparation method of black purple frosted glaze, the steps are as follows: (1) get 39 parts of potassium feldspar, 25 parts of albite feldspar, 10 parts of talc, 10 parts of bentonite, 6 parts of dolomite, 6 parts of magnetite, 4 parts of black manganese ore; (2) after the potassium feldspar, albite, magnetite and black manganese ore in the above raw materials are uniformly mixed according to the proportion of ingredients, add 200 parts of water, and wet ball mill for 5-6 hours; after grinding, pass 200 Slurry 1 is obtained after mesh sieving; (3) After uniformly mixing talc, bentonite and dolomite in the above raw materials according to the proportion of ingredients, add 70 parts of water, and wet ball mill for 2-3 hours without sieving to obtain slurry Two; (4) the slurry one and the slurry two are evenly mixed and stirred, and finally adjusted into a glaze slurry of 50-60 Baume degree;

[0011] The method of using the black-purple frosted glaze is as follows: (1...

Embodiment 2

[0013] The preparation method of black purple frosted glaze, the steps are as follows: (1) get 40 parts of potassium feldspar, 22 parts of albite, 10 parts of talc, 10 parts of bentonite, 7 parts of dolomite, 6 parts of magnetite, 5 parts black manganese ore. (2) After uniformly mixing potassium feldspar, albite, magnetite and black manganese ore in the above raw materials according to the proportion of ingredients, add 200 parts of water, and wet ball mill for 5-6 hours; after grinding, pass through a 200-mesh sieve to obtain Slurry 1; (3) After uniformly mixing talc, bentonite and dolomite in the above raw materials according to the proportion of ingredients, add 70 parts of water, and wet ball mill for 2-3 hours without sieving to prepare Slurry 2; (4) Mix and stir the above slurry 1 and slurry 2 evenly, and finally adjust it to a glaze slurry of 50-60 Baume;

[0014] The method of using the black-purple frosted glaze is as follows: (1) take a body with a smooth surface, w...

Embodiment 3

[0016] The preparation method of black-purple frosted glaze, the steps are as follows: (1) get 40 parts of potassium feldspar, 23 parts of albite, 10 parts of talc, 9 parts of bentonite, 8 parts of dolomite, 5 parts of magnetite, 5 parts black manganese ore. (2) After uniformly mixing potassium feldspar, albite, magnetite and black manganese ore in the above raw materials according to the proportion of ingredients, add 200 parts of water, and wet ball mill for 5-6 hours; after grinding, pass through a 200-mesh sieve to obtain Slurry 1; (3) After uniformly mixing talc, bentonite and dolomite in the above raw materials according to the proportion of ingredients, add 80 parts of water, and wet ball mill for 2-3 hours without sieving to prepare Slurry 2; (4) Mix and stir the above slurry 1 and slurry 2 evenly, and finally adjust it to a glaze slurry of 50-60 Baume;

[0017] The method of using the black-purple frosted glaze is as follows: (1) take a body with a smooth surface, wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glaze, and particularly relates to a black-purple-color frosted glaze, a preparation method and a use method thereof. In a technical scheme, the black-purple-color frosted glaze is made from natural minerals including potassium feldspar, sodium feldspar, magnetite, hausmannite, talcum, bentonite and dolomite according to the following ratio, by weight: 35-40 parts of the potassium feldspar, 20-25 parts of the sodium feldspar, 8-10 parts of the talcum, 8-10 parts of the bentonite, 6-8 parts of the dolomite, 5-7 parts of the magnetite and 3-5 parts of the hausmannite. The black-purple-color frosted glaze is entirely prepared from natural minerals without addition of any pigments and additives, so that the glaze is low in cost, allows one-time shaping during a glazing process, is easy to apply, has stable effect, and has great market competitiveness.

Description

technical field [0001] The invention relates to a glaze, in particular to a black-purple frosted glaze and a preparation method and application method thereof. Background technique [0002] At present, my country is recognized as the largest country in the production and sales of ceramics. Glaze, as the most important ceramic raw material, plays a vital role in improving the quality of ceramic products and the level of decoration technology. Dark glazes have always been popular with the market and consumers because of their calm and robust feel. This black-purple glaze with frosted texture has an excellent tactility, and is more simple and low-key in style, which can effectively improve the quality and grade of ceramic products. Most of the existing ceramic glazes need to add various pigments and additives, the cost of glaze preparation is relatively high, and the glaze application process is relatively complicated. How to reduce the cost of glazing and simplify the proces...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B33/34C04B41/86
CPCC03C8/00C04B33/34C04B41/5022C04B41/86C04B2235/6567C04B2235/6583
Inventor 黄菲张志彬孟林邢苗苗任亚群黎永丽闫莹灿
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com