Antibacterial hot melt adhesive and preparation method thereof

An antibacterial heat and hot melt adhesive technology, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of moldy and odor of antibacterial hot melt adhesives, and achieve the effect of improving antibacterial ability

Active Publication Date: 2017-09-01
中山诚泰化工科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, most of the existing antibacterial hot melt adhesives still often have mildew and odor during use, and the viscosity of the hot melt adhesive is often sacrificed in order to obtain excellent antibacterial properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035]This embodiment provides a kind of antibacterial hot-melt adhesive and preparation method thereof, described hot-melt adhesive is prepared from the following components by weight: 85 parts of EVA, 45 parts of tackifying resin, 23 parts of polyamide resin, N, 14 parts of N-dimethylformamide, 14 parts of triethylvinylsilane, 17 parts of nano titanium dioxide, 15 parts of zinc oxide, 7 parts of naphthenic oil, 6 parts of antioxidant and 6 parts of plasticizer.

[0036] Its preparation method is:

[0037] (1) Add the formulated amount of N,N-dimethylformamide, triethylvinylsilane, nano-titanium dioxide, zinc oxide and naphthenic oil into the container, stir at 350r / min for 35min, and ultrasonically disperse at 65°C 25min, prepared mixed material A;

[0038] (2) Add the formulated amount of EVA, tackifying resin, polyamide resin, antioxidant and plasticizer into the reaction kettle and heat to 160°C, keep stirring during the heating process, stir for 1h to 2h, then add step ...

Embodiment 2

[0041] This embodiment provides an antibacterial hot-melt adhesive and a preparation method thereof, wherein the hot-melt adhesive is prepared from the following components in parts by weight:

[0042] 80 parts of EVA, 40 parts of tackifying resin, 20 parts of polyamide resin, 10 parts of N,N-dimethylformamide, 10 parts of triethylvinylsilane, 15 parts of nano titanium dioxide, 10 parts of zinc oxide, naphthenic oil 5 parts, 5 parts of antioxidant and 5 parts of plasticizer.

[0043] Its preparation method is:

[0044] (1) Add the formulated amount of N,N-dimethylformamide, triethylvinylsilane, nano-titanium dioxide, zinc oxide and naphthenic oil into the container, stir at 300r / min for 30min, and ultrasonically disperse at 60°C 20min, prepared mixed material A;

[0045] (2) Add the formulated amount of EVA, tackifying resin, polyamide resin, antioxidant and plasticizer into the reaction kettle and heat to 150°C, keep stirring during the heating process, stir for 1h to 2h, t...

Embodiment 3

[0048] This embodiment provides an antibacterial hot-melt adhesive and a preparation method thereof, wherein the hot-melt adhesive is prepared from the following components in parts by weight:

[0049] 100 parts of EVA, 50 parts of tackifying resin, 30 parts of polyamide resin, 20 parts of N,N-dimethylformamide, 20 parts of triethylvinylsilane, 20 parts of nano-titanium dioxide, 20 parts of zinc oxide, naphthenic oil 10 parts, 10 parts of antioxidant and 10 parts of plasticizer.

[0050] Its preparation method is:

[0051] (1) Add the formulated amount of N,N-dimethylformamide, triethylvinylsilane, nano-titanium dioxide, zinc oxide and naphthenic oil into the container, stir at 400r / min for 40min, and sonicate at 70°C Disperse for 30 minutes to prepare mixed material A;

[0052] (2) Add the formulated amount of EVA, tackifying resin, polyamide resin, antioxidant and plasticizer into the reaction kettle and heat to 170°C, keep stirring during the heating process, stir for 1h ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention provides an antibacterial hot melt adhesive and a preparation method thereof. The hot melt adhesive is prepared from the following components in parts by weight: 80-100 parts of EVA (Ethylene-Vinyl Acetate), 40-50 parts of a tackifying resin, 20-30 parts of a polyamide resin, 10-20 parts of N,N-dimethylformamide, 10-20 parts of vinyltriethylsilane, 15-20 parts of nanometer titania, 10-20 parts of zinc oxide, 5-10 parts of naphthenic oil, 5-10 parts of an antioxidant and 5-10 parts of a plasticizer. The composition and ratio of the raw materials are changed, N,N-dimethylformamide and vinyltriethylsilane are added to modify the adhesive in the preparation process, and zinc oxide and nanometer titania are added, so that the antibacterial ability of the adhesive is improved on the basis of guaranteeing the adhesiveness of the hot melt adhesive.

Description

technical field [0001] The invention belongs to the field of adhesives, and relates to an antibacterial hot-melt adhesive and a preparation method thereof. Background technique [0002] At present, hot melt adhesives can be widely used in the fields of footwear, clothing, leather goods and decorative materials due to the advantages of no solvent, no pollution, fast bonding speed, convenient compounding, simple use process, and high peel strength. They are also called green adhesives. [0003] The reason why hot melt adhesives develop rapidly is because of the stability and continuous improvement of the main material ethylene-vinyl acetate copolymer, and can be processed into film, rod, strip, and powder according to user requirements, especially different materials can be used Prepare different formulations to meet the needs of softening point, viscosity, embrittlement point and temperature. [0004] EVA hot melt adhesive is formulated from EVA resin, tackifier, plasticizer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J177/00C09J11/06C09J11/04
CPCC08K2003/2241C08K2003/2296C08K2201/011C08L2205/03C09J11/04C09J11/06C09J123/0853C08L77/00C08K13/02C08K5/20C08K5/5403C08K3/22
Inventor 过春明
Owner 中山诚泰化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com