Wood grain brick with negative ions

A negative ion and wood grain technology, applied in the field of negative ion wood grain tiles, can solve the problems of inability to purify the air, inability to release negative ions, unreasonable selection, etc., to achieve the effects of protecting the health of the whole family, stable product quality, and stable surface effects

Inactive Publication Date: 2017-09-22
谢传平
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, aiming at the above content, the present invention provides a kind of negative ion wood grain tile, which solves the problems that the floor tiles in the prior art cannot release negative ions and cannot purify the air due to the unreasonable selection of the formula.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A negative ion wood-grained brick, comprising the following raw materials in parts by weight:

[0024] Rare earth 3 parts

[0025] Silver ion 0.1 part

[0026] 15 parts of titanium dioxide

[0027] 10 parts clay

[0028] 10 parts feldspar

[0029] 5 copies of imitation wood grain paint

[0030] Quartz 5 parts.

Embodiment 2

[0032] A negative ion wood-grained brick, comprising the following raw materials in parts by weight:

[0033] Rare earth 5 parts

[0034] 2 parts of silver ion

[0035] 33 parts of titanium dioxide

[0036] 20 parts of the clay

[0037] 20 parts of feldspar

[0038] 10 copies of imitation wood grain paint

[0039] Quartz 10 parts.

Embodiment 3

[0041] A negative ion wood-grained brick, comprising the following raw materials in parts by weight:

[0042] Rare earth 10 parts

[0043] 3 parts of silver ion

[0044] 40 parts of titanium dioxide

[0045] Clay 20

[0046] Feldspar 20

[0047] Imitation wood grain paint 10

[0048] Quartz 10.

[0049] Wherein, the preparation method of the negative ion wood grain brick of the present invention is the same as the traditional one. The objects of the present invention can be achieved within the following parameter ranges of each material component: 3-10 parts of rare earth, 0.1-3 parts of silver ion, 15-40 parts of titanium dioxide, and 30-60 parts of basic glaze raw materials.

[0050] After testing, after the patented product has been polished and polished for a long time, its negative ion radioactivity is tested, and the negative ion radioactivity is between 20,000 and 30,000; the negative ion wood grain brick has passed the thermal stability test at 180 degrees for 5 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to brick, and provides a wood grain brick with negative ions, aiming at solving the problem that in the prior art, as the formula selection of a floor tile is unreasonable, the negative ions cannot be released, so that air cannot be purified and the like. The wood grain brick is prepared from the following raw materials in parts by weight: 3-10 parts of rare earth, 0.1-3 parts of silver ions, 15-40 parts of titanium dioxide and 30-60 parts of a raw material for parent glaze.

Description

technical field [0001] The invention relates to a brick, in particular to a negative ion wood grain brick. Background technique [0002] Traditional floor tiles are made of clay and other raw materials, which are then sold in warehouses after being pressed, fired, polished, graded and packaged. It has many specifications, strong quality, small bulk density, pressure resistance, wear resistance, and moisture resistance; some of them have been glazed and have decorative effects; they are mostly used on the ground and floors of public buildings and civil buildings. [0003] Traditional floor tiles are made of clay, feldspar and other raw materials in a certain proportion, and then put into a ball mill to grind into a slurry with a certain fineness. After the powder with particle size and particle ratio is transported to the press workshop for compression molding, the formed bricks are dried in a drying kiln and then enter the glaze line for glazing and inkjet, and then enter t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine