Preparation method for preparing wrap paper of mixed type cigarette cores which do not combust when being heated and cigarette cores

A technology of heat-not-burn and forming paper, which is applied in the fields of application, tobacco, and smoker's products, and can solve the problem of not developing hybrid heat-not-burn cigarette cores and related products, achieving good application prospects and improving smoke Quantity, the effect of simple preparation process

Active Publication Date: 2017-09-29
CHINA TOBACCO YUNAN NEW MATERIAL
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem that there are many related domestic heat-not-burn cigarettes, but no hybrid heat-not-burn cigarette core and related products suitable for the national conditions have been developed. Preparation method of forming paper for heat-not-burn cigarette core and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for preparing wrap paper of mixed type cigarette cores which do not combust when being heated and cigarette cores
  • Preparation method for preparing wrap paper of mixed type cigarette cores which do not combust when being heated and cigarette cores
  • Preparation method for preparing wrap paper of mixed type cigarette cores which do not combust when being heated and cigarette cores

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A preparation method for forming paper for preparing hybrid heat-not-burn cigarette cores, comprising the following steps:

[0052] Step (1), pretreatment: pretreat Burley tobacco stems with microwave expansion until the expansion rate is 200-260%, and then crush and sieve the obtained expanded Burley tobacco stems and the upper tobacco leaves of Burley tobacco To 80-120 mesh, obtain Burley tobacco expanded tobacco stem particles and Burley tobacco leaf particles;

[0053] Step (2), preparation of the first mixture: After mixing the Burley tobacco expanded tobacco stem particles and the Burley tobacco leaf particles according to the mass ratio of 6:4, add a smoking agent to it, stir until the mixture is uniform, and then statically Set for 0.5h to obtain the first mixture;

[0054] The added mass of the smoke-generating agent is 1 time of the total mass of the Burley tobacco expanded tobacco stem particles and the Burley tobacco leaf particles;

[0055] Described fumi...

Embodiment 2

[0073] A preparation method for forming paper for preparing hybrid heat-not-burn cigarette cores, comprising the following steps:

[0074] Step (1), pretreatment: pretreat Burley tobacco stems with microwave expansion until the expansion rate is 200-260%, and then crush and sieve the obtained expanded Burley tobacco stems and the upper tobacco leaves of Burley tobacco To 80-120 mesh, obtain Burley tobacco expanded tobacco stem particles and Burley tobacco leaf particles;

[0075] Step (2), preparation of the first mixture: After mixing the Burley tobacco expanded tobacco stem particles and the Burley tobacco leaf particles according to the mass ratio of 4:6, add a smoking agent to it, stir until the mixture is uniform, and then statically Set for 1.5h to obtain the first mixture;

[0076] The added quality of the smoke-generating agent is twice the total mass of the Burley tobacco expanded tobacco stem particles and the Burley tobacco leaf particles;

[0077] The fuming agen...

Embodiment 3

[0099] A preparation method for forming paper for preparing hybrid heat-not-burn cigarette cores, comprising the following steps:

[0100] Step (1), pretreatment: pretreat Burley tobacco stems with microwave expansion until the expansion rate is 200-260%, and then crush and sieve the obtained expanded Burley tobacco stems and the upper tobacco leaves of Burley tobacco To 80-120 mesh, obtain Burley tobacco expanded tobacco stem particles and Burley tobacco leaf particles;

[0101] The specific method for performing microwave expansion pretreatment on Burley tobacco stems to an expansion rate of 200-260% is as follows: put Burley tobacco stems with a moisture content of 14-16% into a microwave expansion device, and the microwave expansion parameters are The frequency is 2450MHz, the power is 900W, and the time is 20s; the expanded tobacco stems of the required Burley tobacco have no obvious carbonization;

[0102] Step (2), preparation of the first mixture: mix the Burley expan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method for preparing wrap paper of mixed type cigarette cores which do not combust when being heated and the cigarette cores and belongs to the technical field of cigarettes. The preparation method comprises the steps of preprocessing, preparing first mixtures, preparing mixed slurry, preparing spicing liquid, preparing coating and preparing the cigarette cores. The prepared wrap paper products are used for preparing the cigarette cores which do not combust when being heated, due to the fact that a large amount of burley tobacco particle materials are attached to the wrap paper, the smoke amount is adequate, the puff number can reach 20, and the smoke strength can be remarkably improved; the spicing materials can make the aroma and taste full and harmonious, no obvious stimulus exists in a nasal cavity, accordingly the suction quality of the cigarettes which do not combust when being heated is remarkably improved, and the prepared wrap paper products have good application prospects.

Description

technical field [0001] The invention belongs to the technical field of cigarettes, and in particular relates to a method for preparing a forming paper used for preparing a cigarette core of a hybrid heat-not-burn cigarette and a method for preparing the cigarette core. Background technique [0002] The new type of cigarette refers to not directly burning tobacco, but only heating (about 300°C) tobacco or its extracts, which releases less harmful components and is an important extension of mixed cigarettes. However, there has been no relevant report in this field in my country's tobacco industry. [0003] The current research hotspots of patent technology at home and abroad focus on heater system and sensor improvement, tobacco material formulation, cigarette structure molding, production process improvement, etc., and how to improve the sensory quality of cigarettes and reduce production costs. Philip Morris (Philip Morris for short) holds a systematic and comprehensive Elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A24F47/00
CPCA24F47/004
Inventor 王乃定徐艳群刘鑫吴雨松张强王涛魏杰夏启东刘燕王浩雅何嘉勋石银艳
Owner CHINA TOBACCO YUNAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com