Easily-cleaned protective glaze and preparation method therefor

A technology for protecting glaze and formula, applied in the field of ceramic glaze, can solve the problems of difficult surface cleaning, poor antifouling effect, blackening of products, etc., and achieves the effect of good gloss, easy cleaning, and not easy to hide dirt

Active Publication Date: 2017-10-20
GUANGDONG KITO CERAMICS GROUP CO LTD +2
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

No good solution has been found for existing ceramic products such as difficult surface cleaning, dirt storage, poor antifouling effect, and products turning black over time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easily-cleaned protective glaze and preparation method therefor
  • Easily-cleaned protective glaze and preparation method therefor

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] In a second aspect, the present invention provides a method for preparing an easy-to-clean protective glaze, comprising the following steps: (a) uniformly mixing a formula amount containing elements Si, Al, Fe, Ti, Na, K, Mg and Ca The silicate material is melted, then water-quenched and pulverized to obtain the easy-clean protective granules; (b) uniformly mixing the formulated amount of the easy-clean protective granules, ink and transparent glaze to obtain the easy-clean protective glaze.

[0044] The preparation method of the above-mentioned easy-clean protective glaze is simple and controllable, and the obtained easy-clean protective glaze has more uniform components and moderate fluidity. Therefore, the easy-clean protective glaze has better pollution resistance and easy-to-clean performance, and the easy-clean protective glaze Glaze has high transparency, gloss and good color development ability, which can ensure the clarity of the surface pattern and color of cer...

Embodiment 1

[0054]An Yijie protective glaze, which is mainly prepared from the following raw materials in parts by mass: 90 parts of Yijie protective particles, 230 parts of printing oil and 20 parts of transparent glaze;

[0055] Among them, Yijie protection particles are mainly composed of the following components by mass: SiO 2 60 parts, Al 2 o 3 15 parts, Fe 2 o 3 0.1 parts, TiO 2 0.01 parts, Na 2 O 4 parts, K 2 O 2 parts, MgO 0.05 parts, CaO 0.5 parts and ignition loss 0.05 parts;

[0056] The printing oil is mainly composed of the following components by mass: 5 parts of sodium carboxymethylcellulose, 20 parts of ethylene glycol, 1 part of bentonite and 60 parts of water;

[0057] The transparent glaze adopts the existing matt frit (the model is TC9071, produced by Zibo Tiancheng Glaze Co., Ltd.);

[0058] The particle gradation of Yijie protective granule is 80-120 mesh 45%, 120-200 mesh 40%, the rest is below 200 mesh; the specific gravity of Yijie protective glaze is 1...

Embodiment 2

[0060] An Yijie protective glaze, which is mainly prepared from the following raw materials in parts by mass: 95 parts of Yijie protective particles, 240 parts of printing oil and 25 parts of transparent glaze;

[0061] Among them, Yijie protection particles are mainly composed of the following components by mass: SiO 2 64 parts, Al 2 o 3 18 parts, Fe 2 o 3 0.15 parts, TiO 2 0.03 parts, Na 2 O 6 parts, K 2 4 parts of O, 0.1 part of MgO, 1 part of CaO and 0.1 part of loss on ignition;

[0062] The printing oil mainly consists of the following components by mass: 0.2 parts of sodium carboxymethyl cellulose, 25 parts of ethylene glycol, 2 parts of bentonite and 70 parts of water;

[0063] The transparent glaze adopts the existing matt frit (the model is TC9071, produced by Zibo Tiancheng Glaze Co., Ltd.);

[0064] The particle gradation of Yijie protective granule is 65% of 80-120 mesh, 10% of 120-200 mesh, and the rest is below 200 mesh; the specific gravity of Yijie ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of ceramic glaze and particularly provides easily-cleaned protective glaze and a preparation method therefor. The easily-cleaned protective glaze is mainly prepared from the following raw materials in parts by mass: 90-110 parts of easily-cleaned protective particles, 230-270 parts of squeegee oil and 20-40 parts of transparent glaze, wherein the easily-cleaned protective particles are mainly prepared from the following ingredients: SiO2, Al2O3, Fe2O3, TiO2, Na2O, K2O, MgO, CaO and ignition loss. According to the easily-cleaned protective glaze, all the raw materials and all the ingredients of the easily-cleaned protective particles are reasonably matched; after the easily-cleaned protective glaze is applied to surfaces of ceramic tiles, the easily-cleaned protective glaze can uniformly cover the surfaces of the ceramic tiles and effectively fill up gaps in the surfaces of the ceramic tiles; and the easily-cleaned protective glaze is good in stain resistance, not prone to dirt hiding and easy to clean.

Description

technical field [0001] The invention relates to the field of ceramic glazes, in particular to an easy-to-clean protective glaze and a preparation method thereof. Background technique [0002] With the rapid development of science and technology, people's lives are changing with each passing day. At the same time, an era of pursuing fashion and showing individuality has been created, and the field of building decoration materials is no exception. With its superior performance and decorative effect, ceramic tiles are favored by more and more consumers, and are widely used in people's daily life. Ceramic antique brick is a kind of building decoration material that has become popular in recent years. It has many advantages such as the magnificence of polished brick and the rich and colorful patterns of porcelain tiles, modern or retro charm, and personalization, and is very popular in the market. Consumer favorite. [0003] With the rapid development of architectural ceramics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/20
CPCC03C8/20
Inventor 喻劲军戴永刚钟礼丰李德英
Owner GUANGDONG KITO CERAMICS GROUP CO LTD