Method for preparing anti-bacteria cool graphene slubby yarn and application thereof to home textile products

A slub yarn, graphene technology, applied in textiles and papermaking, yarn, textile and other directions, can solve the problems of lack of affinity, difficult graphene processing, etc., to achieve a rich layered effect

Inactive Publication Date: 2017-10-20
IANGSU COLLEGE OF ENG & TECH
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the lack of affinity between graphene and textiles, it i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0024] A preparation method of graphene antibacterial and cool slub yarn, the yarn is composed of 30 parts by weight of graphene nylon composite fiber, 20 parts of bamboo fiber, and 10 parts of viscose fiber, and the above fiber is passed through a ring spindle The slub yarn is spun into slub yarn by the spinning machine spinning process; the process includes the following process steps: cotton blending, carding, drawing, spinning, winding, and the specific operations are as follows:

[0025] The cotton blending and carding process: use continuous weighing computer matching color blending process, manual proportioning and weighing→mixing→opening→carding, continuous weighing and quantitative feeding in the mixing warehouse, and suction through the negative pressure of the fan Soft opening. The main parameters of the carding process, the speed of the opening beater of the picker is 400rpm, the speed of the beater of the card opener is 800rpm, the speed of the coiling roller is 1...

specific Embodiment 2

[0029] A preparation method of graphene antibacterial and cool slub yarn, the yarn is composed of 60 parts by weight of graphene nylon composite fiber, 30 parts of bamboo fiber, and 20 parts of viscose fiber, and the above fiber is passed through a ring spindle The slub yarn is spun into slub yarn by the spinning machine spinning process; the process includes the following process steps: cotton blending, carding, drawing, spinning, winding, and the specific operations are as follows:

[0030] The cotton blending and carding process: use continuous weighing computer matching color blending process, manual proportioning and weighing→mixing→opening→carding, continuous weighing and quantitative feeding in the mixing warehouse, and suction through the negative pressure of the fan Soft opening. The main parameters of the carding process, the speed of the opening beater of the picker is 500rpm, the speed of the beater of the card opener is 1000rpm, the speed of the coiling roller is ...

specific Embodiment 3

[0034]A kind of preparation method of graphene antibacterial cool slub yarn, this yarn is made up of the graphene nylon composite fiber that is 40 parts by weight, the bamboo fiber of 27 parts, the viscose fiber of 13 parts, and above-mentioned fiber is passed through ring spinning The slub yarn is spun into slub yarn by the spinning machine spinning process; the process includes the following process steps: cotton blending, carding, drawing, spinning, winding, and the specific operations are as follows:

[0035] The cotton blending and carding process: use continuous weighing computer matching color blending process, manual proportioning and weighing→mixing→opening→carding, continuous weighing and quantitative feeding in the mixing warehouse, and suction through the negative pressure of the fan Soft opening. The main parameters of the carding process, the speed of the opening beater of the picker is 460rpm, the speed of the beater of the card opener is 900rpm, the speed of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing anti-bacteria cool graphene slubby yarn. The yarn is composed of, by weight parts, 30-60 parts of graphene chinlon composite fiber, 20-30 parts of bamboo fiber and 10-20 parts of viscose fiber. The fibers are spun into the slubby yarn through a ring spinning frame spinning process. The process comprises the steps of cotton blending, cotton carding, drawing, spinning and spooling. The obtained anti-bacteria cool graphene slubby yarn is formed by blending of various function fibers and integrates the advantages of the used fibers. Compared with conventional cotton yarn, the anti-bacteria cool graphene slubby yarn has viscose glue, is more excellent than natural cotton fiber in softness, moisture absorption and light self-weight and has anti-bacteria and cool performances of the bamboo fiber; the novel graphene chinlon composite fiber is adopted to intensify anti-static anti-bacteria, cool, comfortable and conformable performance and the like. The prepared yarn is applied to home textiles, and the finished home textiles are rich in layering sense and third dimension and have multiple functions.

Description

technical field [0001] The invention belongs to the field of new material blended yarns, and in particular relates to a preparation method of graphene antibacterial and cool slub yarn and its application in home textile products. Background technique [0002] Graphene composite fiber materials have become a research hotspot in recent years. At present, there have been a lot of research on the potential applications of graphene composite fiber materials, such as energy storage materials, conversion devices, sensors, wires, etc. Graphene has excellent antibacterial properties and thermal conductivity. Antibacterial fabrics can be prepared by finishing graphene on fabrics. Compared with traditional inorganic and organic antibacterial agents, graphene has basically no cytotoxicity and is more suitable for direct contact with human skin. However, due to the lack of affinity between graphene and textiles, it is difficult to process graphene onto textiles through conventional proce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/34D02G3/04D03D15/00
CPCD02G3/04D02G3/34D02G3/346D03D15/00D10B2401/13D10B2331/02D10B2201/24D10B2201/10D03D15/283D03D15/217D03D15/225D03D15/50
Inventor 陈志华
Owner IANGSU COLLEGE OF ENG & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap