A kind of orange-red glass and its preparation method and application
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An orange-red, glass technology, applied in the field of glass preparation, can solve problems such as easy film release, and achieve the effect of reasonable formula, bright color and low cost
Inactive Publication Date: 2019-08-16
LUOYANG INST OF SCI & TECH
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The former has better color and brightness, but it is easy to remove the film
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1-5
[0027] Embodiments 1-5 have different glass composition ratios, and the preparation method is the same, and the glass compositions of 5 embodiments are prepared according to Table 1:
[0028] Table 1. Basic composition of orange-red glass
[0029] components Na 2 o
Rb 2 o
CaO BeO SiO 2
C Se Na 2 SO 4
Example 1 8.20% 4.50% 9.8% 3.00% 64% 0 9.50% 1% Example 2 12.00% 1.40% 8.5% 2.00% 65% 3.50% 5.50% 1% Example 3 11.50% 2.50% 7.5% 2.60% 62% 6.10% 6.80% 1% Example 4 7.60% 1.50% 6.5% 2.40% 61% 8.00% 12% 1% Example 5 11.00% 4.40% 9.9% 2.20% 65% 6.50% 0 1%
[0030] According to Table 1. The design composition is converted into the quality of sodium carbonate, rubidium chloride, limestone, beryllium hydroxide, silica sand, carbon powder, selenium powder, sodium sulfate respectively, and different amounts of sodium carbonate, rubidium chloride, limestone, Beryllium hydroxide, ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to orangered glass and a production method and application thereof; the orangered glass is made from, by weight, 5-13.0% of Na2O, 1-4.5% of Rb2O, 6.4-10.0% of CaO, 2.0-3.0% of BeO, 60-65% of SiO2, 1% of Na2SO4, 4.5% of C, and 5.6% of Se; the above components are introduced in the forms of sodium carbonate, rubidium chloride, limestone, beryllium hydroxide, silica sand, sodium sulfate, carbon powder, and selenium powder respectively. The above materials are mixed well, the mixture is melted at 1485+ / -5 DEG C, the temperature is held for 90 min, the glass melt is poured into a mold that is preheated to 580 DEG C, the mold is placed a resistance furnace held at 580 DEG C for the purpose of annealing, and the temperature is held for 60 min before natural cooling to room temperature. Carbon and selenium are mixed for coloring; as carbon and selenium are used together under controlled usage, the orangered glass can be produced which has bright appearance and full color, never fades and is a novel material for making ornaments.
Description
technical field [0001] The invention relates to the technical field of glass preparation, in particular to an orange-red glass and its preparation method and application. Background technique [0002] Glass substrates can exhibit aesthetic properties that allow one to imagine it as gemstones, nephrite, and topaz, among others. There are two ways to make the glass substrate achieve the desired color effect. One is to coat the surface of the colorless glass, and coat the film of the corresponding color according to the desired color. Another method is to directly produce colored glass, and add some colorants to the glass batch to make the melted glass itself have color. The former has better color and brightness, but it is easy to remove the film. The present invention belongs to the latter. Adding selenium and carbon to the glass batch material at the same time, and controlling a certain amount, can produce brightly colored orange-red glass. This color glass is used to pro...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.