Epoxy resin curing agent
A technology of epoxy resin curing and aluminum oxide, which is applied in the field of epoxy resin curing agent, can solve the problems of long curing time and affecting work efficiency, and achieve the effect of fast curing reaction rate
Inactive Publication Date: 2017-10-27
吴丹
View PDF3 Cites 1 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, due to the long curing time of epoxy resin at room temperature (28°C), it usually takes 8-12 hours to fully cure, which seriously affects work efficiency.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0009] The epoxy resin curing agent is composed of 20-30 parts of acid anhydride mixture, 15-18 parts of aluminum oxide, 12-14 parts of isoprene, 6-9 parts of n-butanol hydroglyceryl ether, asbestos Composed of 5-7 parts of fiber, 8-9 parts of polypropylene glycol dicondensate, and 1 part of glyceryl ether.
[0010] . The epoxy resin curing agent provided by the invention has a fast curing reaction rate and can reduce the complete curing time of the epoxy resin to 6 hours.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention discloses an epoxy resin curing agent which consists of the following components in parts by weight: 20-30 parts of an acid anhydride mixture, 15-18 parts of aluminum oxide, 12-14 parts of isoprene, 6-9 parts of n-butyl alcohol phenyl glycidyl ether, 5-7 parts of an asbestos fiber, 8-9 parts of polypropylene glycol diglycidyl ether and 1 part of phenyl glycidyl ether. The epoxy resin curing agent disclosed by the invention is rapid in curing reaction velocity, and the complete curing time of an epoxy resin can be shortened to 6 hours.
Description
technical field [0001] The invention relates to an epoxy resin curing agent. Background technique [0002] Epoxy resin is an amorphous viscous liquid, which becomes plastic when heated, has no obvious melting point, becomes soft when heated, gradually melts and becomes sticky, insoluble in water, and will not harden itself, so it has almost no independent use value. Epoxy resin curing agent is an additive that chemically reacts with epoxy resin to form a network-like three-dimensional polymer, envelops the composite material in the network, and makes the linear resin into a tough body-shaped solid. When a certain amount of curing agent is added to the epoxy resin, it will gradually cure. Due to the good mechanical strength and insulation properties of epoxy resin after curing, epoxy resin is widely used as an adhesive in the manufacture of electronic products. For example, epoxy resin is needed to glue and cure some electrical components on circuit boards. Together. Howev...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/42C08G59/40C08L71/02C08K13/04C08K7/12C08K5/01C08K3/22C08K5/1515
CPCC08G59/42C08G59/4007C08K3/22C08K5/01C08K5/1515C08K7/12C08K13/04C08K2003/2227C08L71/02
Inventor 吴丹
Owner 吴丹
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap