Mold-proof desulfurization gypsum mortar and preparation method thereof

A technology for desulfurizing gypsum and mortar, which is applied in the field of comprehensive utilization of building materials and solid waste, can solve problems such as mildew, erosion, and damage to finishes, and achieve the effects of preventing mildew over time, saving resources and protecting the natural environment.

Active Publication Date: 2017-11-03
上海漕源建材贸易有限公司 +1
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing cement mortar has strong alkalinity, so it has anti-mildew and antibacterial properties within a certain period of time. However, as time goes by, the surface of the mortar is affected by CO in the air. 2 It is gradually acidified by the action of mold, etc., and its gaps are prone to mildew, erosion and damage to the finish, which affects the appearance and use of the building.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] In this embodiment, to prepare 100kg of anti-mildew desulfurization gypsum mortar, the raw materials are weighed as follows, and the composition and mass percentage of the raw materials are:

[0027] Desulfurization gypsum 70kg;

[0028] Fly ash 19kg;

[0029] quicklime 4kg;

[0030] Inorganic gel 4kg;

[0031] Antifungal agent 1kg;

[0032] Anti-crack agent 2kg. The method for preparing 100kg of mildew-resistant desulfurized gypsum mortar is to put the above-mentioned raw materials into a mixer in sequence, and after fully stirring evenly, the mildew-proof desulfurized gypsum mortar is obtained, which can be mixed evenly by adding an appropriate amount of water before use.

Embodiment 2

[0034] In this embodiment, to prepare 100kg of anti-mildew desulfurization gypsum mortar, the raw materials are weighed as follows, and the composition and mass percentage of the raw materials are:

[0035] Desulfurization gypsum 66kg;

[0036] Fly ash 22kg;

[0037] Quicklime 5kg

[0038] Inorganic gel 4kg;

[0039] Antifungal agent 1kg;

[0040] The method of preparing 100kg of anti-mildew desulfurization gypsum mortar with 2kg of anti-cracking agent is to put the above-mentioned raw materials into the mixer in turn, and after fully stirring, the anti-mildew desulfurization gypsum mortar is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses mold-proof desulfurization gypsum mortar and a preparation method thereof. The mortar is prepared from, by mass, 65%-75% of desulfurization gypsum, 15%-25% of pulverized fuel ash, 4%-5% of quick lime, 3%-5% of inorganic gel, 0.8%-1.2% of mold-proof agent and 1%-3% of anti-cracking agent. The preparation method of the mold-proof desulfurization gypsum mortar comprises the steps that weighing is performed according to raw material composition and mass percentage content, the desulfurization gypsum, the quick lime, the pulverized fuel ash, the inorganic gel, the mold-proof agent and the anti-cracking agent are sequentially added into a mixing machine for full and even mixing to prepare the mold-proof desulfurization gypsum mortar. The mortar prepared by adopting the method uses the desulfurization gypsum to replace natural gypsum. Due to high calcium sulphate dihydrate content in the desulfurization gypsum and adding of the quick lime and the pulverized fuel ash, and the alkalinity of the mortar is improved. In addition, the mold-proof agent and the anti-cracking agent are mixed in the mortar, molding with the passing of time is prevented, meanwhile a new way is opened for resourceful utilization of the desulfurization gypsum in industrial solid waste, resources are saved, and the natural environment is protected.

Description

technical field [0001] The invention belongs to the technical field of comprehensive utilization of building materials and solid waste, and in particular relates to a mildew-resistant desulfurized gypsum mortar and a preparation method thereof. Background technique [0002] The existing cement mortar has strong alkalinity, so it has anti-mildew and antibacterial properties within a certain period of time. However, as time goes by, the surface of the mortar is affected by CO in the air. 2 It is gradually acidified by the action of mold, etc., and its gaps are prone to mildew, erosion and damage to the finish, which affects the appearance and use of the building. [0003] At present, desulfurization gypsum is a by-product of flue gas desulfurization by wet lime / limestone-gypsum method in coal-fired power plants, and its main component is calcium sulfate dihydrate (CaSO 4 2H 2 O), the color is light yellow, neutral or slightly alkaline, and its content of calcium sulfate dihy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14
CPCC04B28/144C04B2111/2092C04B18/08C04B22/064C04B24/124C04B14/104C04B18/26
Inventor 刘玉林陆文雄张欢党俐刘鸿鹏张雪冰
Owner 上海漕源建材贸易有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products