Energy-saving and environment-friendly seal primer and preparation method thereof

A sealing primer, energy saving and environmental protection technology, applied in coatings, anti-corrosion coatings, etc., can solve the problems of low environmental protection efficiency and single function, and achieve the effect of ensuring environmental protection, good corrosion resistance, and large-scale industrialization promotion value.

Inactive Publication Date: 2017-11-17
重庆卡美伦科技有限公司合川分公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the function of the water-based paint in the prior art is comparatively single, and the efficiency of environmental protection is lower

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] A preparation method for an energy-saving and environment-friendly sealing primer, comprising the following steps:

[0036] Firstly, 1-9 parts by weight of auxiliary agents are dissolved in 100-150 parts of deionized water to form a first mixed solution.

[0037] Secondly, 17-43 parts by weight of acrylic acid, 24-39 parts of vinyl acetate and 0.1-0.3 parts of n-butyl acrylate are added to the first mixed solution and mixed uniformly to form a second mixed solution.

[0038] Then, pour the second mixed solution into the reactor and heat to prepare the copolymer resin, and the heating temperature is 60-70°C.

[0039] Then, after cooling the copolymerized resin, 100-240 parts by weight of zinc powder are added and stirred evenly with a stirrer.

[0040] As a preferred solution, the preparation method of the energy-saving and environment-friendly sealing primer also includes adding 100-240 parts by weight of zinc powder after cooling the copolymer resin, stirring evenly w...

Embodiment 1

[0043] This embodiment provides an energy-saving and environment-friendly sealing primer, which is prepared by the following preparation method of an energy-saving and environment-friendly sealing primer. The method includes the following steps:

[0044] First, 1 part by weight of benzoyl peroxide, dimethylaniline and dimethyl phthalate in a weight ratio of 0.1:0.1:2 is dissolved in 100 parts of deionized water to form the first mixture.

[0045] Secondly, 43 parts by weight of acrylic acid, 24 parts of vinyl acetate and 0.1 part of n-butyl acrylate were added to the first mixed solution and mixed uniformly to form a second mixed solution.

[0046] Then, the second mixed solution was poured into the reactor and heated to obtain a copolymer resin, and the heating temperature was 60°C.

[0047] Then, after cooling the copolymer resin, 100 parts by weight of zinc powder and 3 parts of bentonite were added and stirred evenly with a mixer.

Embodiment 2

[0049] This embodiment provides an energy-saving and environment-friendly sealing primer, the difference between its preparation method and the preparation method of the energy-saving and environment-friendly primer provided in Example 1 is that the method comprises the following steps:

[0050] First, 5 parts by weight of benzoyl peroxide, dimethylaniline and dimethyl phthalate in a weight ratio of 0.1:0.1:2.5 are dissolved in 100 parts of deionized water to form the first mixture.

[0051] Secondly, 30 parts by weight of acrylic acid, 25 parts of vinyl acetate and 0.2 part of n-butyl acrylate were added to the first mixed solution and mixed evenly to form a second mixed solution.

[0052] Then, the second mixed solution was poured into the reactor and heated to obtain a copolymer resin, and the heating temperature was 65°C.

[0053] Then, after the copolymer resin is cooled, 150 parts by weight of zinc powder and 8 parts of natural clay are added and stirred evenly with a m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention provides an energy-saving and environment-friendly seal primer and a preparation method thereof and relates to the field of coatings. The primer is prepared from the following components: 24-39 parts of vinyl acetate, 17-43 parts of acrylic acid, 100-150 parts of industrial deionized water, 0.1-0.3 part of n-butyl acrylate, 3-8 parts of an adsorbent, 1-9 parts of an assistant and 100-240 parts of zinc powder. The seal primer is good in environment-friendliness. The preparation method of the energy-saving and environment-friendly seal primer comprises the following steps of: dissolving the assistant in the industrial deionized water to form a first mixed solution; adding acrylic acid, vinyl acetate and n-butyl acrylate into the first mixed solution to be uniformly mixed to form a second mixed solution; pouring the second mixed solution into a reaction kettle and heating the reaction kettle to prepare copolymerized resin; and successively adding a zinc powder adsorbent into the cooled copolymerized resin and uniformly stirring the mixture. The method is simple and convenient and high in operability, and has relatively great industrial promotional value.

Description

technical field [0001] The invention relates to the field of coatings, and in particular to an energy-saving and environment-friendly sealing primer and a preparation method thereof. Background technique [0002] Coatings play an important role in the national economy and are indispensable in modern society. However, there are 10 million tons of volatile organic compounds (VOC) emitted into the atmosphere from coatings in the world every year, which are the main source of air pollution. With the continuous improvement of people's awareness of environmental protection and the promulgation of relevant regulations to limit VOC emissions, it has become the consensus of the entire society that environmentally friendly green coating products, with their characteristics of non-polluting and safe, can replace traditional heavily polluting solvent-based coatings. [0003] In recent years, with the progress of modern economy and the rapid development of science and technology, people...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/02C09D131/04C09D5/10C09D7/12C08F220/06C08F218/08C08F220/18
CPCC08F218/08C08F220/06C08K3/346C08K3/36C08K5/12C08K7/24C08K2003/0893C08K2003/2227C08K2201/011C08K2201/014C09D5/106C09D131/04C09D133/02C08F220/1804
Inventor 张占华关雪松
Owner 重庆卡美伦科技有限公司合川分公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap