TPV for vehicle air conditioner pipe members

A low-odor and mixture technology, applied in the TPV field of automotive air-conditioning pipe fittings, can solve problems such as unsatisfactory mechanical properties, and achieve the effects of reducing odor and TVOC content, using environmentally friendly materials, and excellent mechanical properties.

Inactive Publication Date: 2017-11-24
ANHUI XIONGYA PLASTIC TECH
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this type of thermoplastic elastomer has obtained the physical properties and processing properties of elastomers and thermoplastics, its mechanical properties are not satisfactory, so it has not been widely used.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TPV for vehicle air conditioner pipe members
  • TPV for vehicle air conditioner pipe members
  • TPV for vehicle air conditioner pipe members

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] 100 parts by weight of vulcanizable elastomer (U.S. DuPont NDR 2744), 70 thermoplastic polyolefin (ExxonMobil PP 7032KN), 1 part by weight of MAH graft modified polypropylene (ExxonMobil PP7032KN, grafting ratio 3wt%), weighed and poured into a blender, stirring evenly. Then add 3 parts by weight of cross-linking agent, 1.5 parts by weight of stannous chloride, 1 part by weight of zinc oxide, 0.5 parts by weight of stabilizer, 2 parts by weight of zinc stearate, pour into a stirrer and stir evenly. The mixed material is added in the hopper of the twin-screw extruder, the extender oil of 100 parts by weight, the plasticizer trioctyl trimellitate of 5 parts by weight, the bis(trimethylsilyl) of 0.02 parts by weight The carbodiimide mixture is fed into the extruder from the plasticizing section of the extruder through a liquid metering pump, melted and blended, extruded and granulated to form a composite material. Among them, the temperature settings of each heating zone ...

Embodiment 2

[0048] 100 parts by weight of vulcanizable elastomer (U.S. DuPont NDR 2744), 70 thermoplastic polyolefins (ExxonMobil PP 7032KN), 1 part by weight of acrylic acid graft modified polypropylene (ExxonMobil PP 7032KN, grafted Rate 2wt%), weighed and poured into a blender, stirred evenly. Then add 3 parts by weight of cross-linking agent, 1.5 parts by weight of stannous chloride, 1 part by weight of zinc oxide, 0.5 parts by weight of stabilizer, 2 parts by weight of zinc stearate, pour into a stirrer and stir evenly. The mixed material is added in the hopper of the twin-screw extruder, the extender oil of 100 parts by weight, the plasticizer trioctyl trimellitate of 5 parts by weight, the bis(trimethylsilyl) of 0.03 parts by weight The carbodiimide mixture is fed into the extruder from the plasticizing section of the extruder through a liquid metering pump, melted and blended, extruded and granulated to form a composite material. Among them, the temperature settings of each heati...

Embodiment 3

[0050] 100 parts by weight of vulcanizable elastomer (U.S. DuPont NDR 2744), 70 thermoplastic polyolefin (ExxonMobil PP 7032KN), 1 part by weight of MAH graft modified polypropylene (ExxonMobil PP7032KN, grafting ratio 5wt%), weighed and poured into a blender, stirring evenly. Then add 3 parts by weight of cross-linking agent, 1.5 parts by weight of stannous chloride, 1 part by weight of zinc oxide, 0.5 parts by weight of stabilizer, 2 parts by weight of zinc stearate, pour into a stirrer and stir evenly. The mixed material is added in the hopper of twin-screw extruder, the extender oil of 100 parts by weight, the plasticizer trioctyl trimellitate of 5 parts by weight, the two (trimethylsilyl) of 0.08 parts by weight The carbodiimide mixture is fed into the extruder from the plasticizing section of the extruder through a liquid metering pump, melted and blended, extruded and granulated to form a composite material. Among them, the temperature settings of each heating zone of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a low-odor TPV for vehicle air conditioner pipe members, wherein the low-odor TPV is prepared from a vulcanized mixture through a dynamic vulcanization process, and the vulcanized mixture comprises, by weight, 100 parts of a vulcanizable elastomer, 50-200 parts of a thermoplastic polyolefin, 0.01-10 parts of a cross-linking agent, 10-100 parts of filling oil, 0.1-5 parts of an olefinic acid compound-modified thermoplastic polyolefin, and 0.01-0.1 part of a carbodiimide compound. The TPV of the present invention meets the requirements of the national vehicle interior air-related standards.

Description

technical field [0001] The invention relates to the field of low-odor thermoplastic vulcanizate (TPV), and also relates to the TPV applied to automobile air-conditioning pipe fittings. Background technique [0002] At present, a class of polyolefin thermoplastic elastomers (TPOs) is prepared by blending a semi-crystalline plastic (such as PP) with an amorphous rubber (such as EPDM) using rubber-plastic blending technology, creating a new class of The first of its kind in thermoplastic elastomers. Although such thermoplastic elastomers have obtained the physical properties and processing properties of elastomers and thermoplastics, their mechanical properties are not satisfactory, so they have not been widely used. [0003] For this reason, the development of these blending technologies in recent years has mainly focused on dynamic vulcanization. Dynamic vulcanization is the process of elastic vulcanization and crosslinking at the same time of melting and mixing under high ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/00C08L51/06C08L61/06C08K13/02C08K3/16C08K3/22C08K5/098C08K5/12C08K5/5445
CPCC08K2003/2296C08L23/16C08L2205/02C08L2205/035C08L23/00C08L51/06C08L61/06C08K13/02C08K3/16C08K3/22C08K5/098C08K5/12C08K5/544
Inventor 葛军马访中
Owner ANHUI XIONGYA PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products