Once-forming, fully-glazing and support pin type firing method of small fully-glazed porcelain

A technology for porcelain and glaze, applied in the field of porcelain support firing, can solve the problems of low yield and high cost

Active Publication Date: 2017-12-01
汝州市荣华汝瓷开发有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cost of repeated firing is extremely high, and the yield is extremely low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Once-forming, fully-glazing and support pin type firing method of small fully-glazed porcelain
  • Once-forming, fully-glazing and support pin type firing method of small fully-glazed porcelain

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The adhesive uses starch as the main ingredient. Pseudo-boehmite powder accounting for 20% of its weight, 20% aluminum powder and 90% water are sequentially added to the starch and mixed and stirred evenly, wherein the starch It is a mixture of one or more of white flour, corn flour, mung bean flour or sorghum flour, and the particle diameter of the pseudo-boehmite powder and aluminum powder is 80 mesh.

[0029] The adhesive also contains montmorillonite powder with a particle size of 80-120 meshes accounting for 3% of the total weight of the starch.

[0030] The adhesive also contains 1% allophane by the total weight of the starch.

Embodiment 2

[0032] The adhesive is mainly made of starch, and 30% of the weight of the pseudoboehmite powder, 40% of the aluminum powder and 110% of the water are sequentially added to the starch and then mixed and stirred evenly, wherein the starch It is a mixture of one or more of white flour, corn flour, mung bean flour or sorghum flour, and the particle diameter of the pseudo-boehmite powder and aluminum powder is 80-120 mesh.

[0033] The binder also contains montmorillonite powder with a particle size of 80-120 meshes accounting for 5% of the total weight of the starch.

[0034] The adhesive also contains allophane accounting for 3% of the total weight of the starch.

Embodiment 3

[0036] The adhesive is mainly made of starch, and 25% of the weight of the pseudoboehmite powder, 30% of the aluminum powder and 100% of the water are sequentially added to the starch and then mixed and stirred evenly, wherein the starch It is a mixture of one or more of white flour, corn flour, mung bean flour or sorghum flour, and the particle diameter of the pseudo-boehmite powder and aluminum powder is 80-120 mesh.

[0037] The binder also contains montmorillonite powder with a particle size of 80-120 meshes accounting for 4% of the total weight of the starch.

[0038] The binder also contains allophane accounting for 2% of the total weight of the starch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a once-forming, fully-glazing and support pin type firing method of small fully-glazed porcelain. A seal is carved in the center of the bottom of the small porcelain related in the method. The fully-glazing and support pin type firing method comprises steps as follows: the part, excluding the seal, of the surface of the porcelain is uniformly dipped with glaze, the seal is taken as a support point, a support seat is used for a support, the porcelain fully dipped with the glaze and the support seat are put into a kiln together to be fired by the aid of support pins, the support seat is a seat plate which is as large as the porcelain and is used for supporting the porcelain, and a trapezoid support bulge matched with the seal is arranged at the center of the top of the seat plate. The method is simple and practical, and the small fully-glazed porcelain can be formed and fired once.

Description

technical field [0001] The invention relates to the technical field of branch firing of porcelain, in particular to a full glaze branch firing method for one-time molding of small vessel type full glazed porcelain. Background technique [0002] China is the hometown of porcelain, and porcelain is an important creation of the ancient working people. Colorful porcelain is one of the great inventions in ancient China. "Porcelain" and "China" are the same word in English, which fully shows that the exquisiteness of Chinese porcelain can be used as a representative of China. High-grade porcelain is much more difficult than ordinary porcelain, so there is no shortage of exquisite porcelain collections in the ancient royal family. As one of the special luxury products of ancient China, porcelain was spread to various countries through various trade channels, and exquisite ancient porcelain was collected by a large number of collectors as antiques with collection value. In order t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/86C04B26/28
CPCC04B26/285C04B41/5022C04B41/86C04B2111/00482C04B41/4535C04B14/303C04B14/34C04B22/002C04B14/104C04B14/041
Inventor 韩琴任一昊
Owner 汝州市荣华汝瓷开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com