Composite material, preparation method thereof and air conditioner workpieces

A technology of composite materials and mixed materials, applied in the field of plastics, can solve problems such as noise pollution, and achieve the effect of avoiding noise, excellent dimensional stability, good impact strength and high modulus

Active Publication Date: 2017-12-22
GD MIDEA AIR-CONDITIONING EQUIP CO LTD +1
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's living standards, air conditioners have become a must-have for family life. They have the functions of adjusting indoor temperature and humidity and purifying the air. While bringing comfort to people, there are also noise pollution problems.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material, preparation method thereof and air conditioner workpieces

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The preparation steps of the composite material are as follows:

[0058] The weight ratio of raw materials is: 50 parts of copolymerized polypropylene, 10 parts of homopolypropylene, 10 parts of talcum powder, 5 parts of barium sulfate, 10 parts of mica, 5 parts of graft compatibilizer, 0.5 parts of antioxidant, lubricant PE 0.5 parts of wax, 0.5 parts of nucleating agent, rare earth oxide Nd 2 o 3 1.0 servings.

[0059] (1) Add the above-mentioned raw materials in proportion to the high-speed mixer, and mix for 3 minutes;

[0060] (2) Put the mixed components into a parallel twin-screw extruder for melting, and simultaneously feed 10 parts of chopped glass fibers side by side, extrude and granulate, so as to obtain a composite material, wherein the barrel temperature of the extruder is: 220°C, the screw speed is 100r / min, the melt pressure is 1.5~2.5MPa, and the vacuum degree is -0.04~-0.1MPa.

Embodiment 2

[0062] The preparation steps of the composite material are as follows:

[0063] The weight ratio of raw materials is: 50 parts of copolymerized polypropylene, 10 parts of homopolypropylene, 5 parts of talcum powder, 10 parts of barium sulfate, 10 parts of mica, 5 parts of graft compatibilizer, 0.5 parts of antioxidant, lubricant PE 0.5 parts of wax, 0.5 parts of nucleating agent, rare earth oxide Nd 2 o 3 1.0 servings.

[0064] (1) Add the above-mentioned raw materials in proportion to the high-speed mixer, and mix for 3 minutes;

[0065] (2) Put the mixed components into a parallel twin-screw extruder for melting, and simultaneously feed 10 parts of chopped glass fibers side by side, extrude and granulate, so as to obtain a composite material, wherein the barrel temperature of the extruder is: 220°C, the screw speed is 100r / min, the melt pressure is 1.5~2.5MPa, and the vacuum degree is -0.04~-0.1MPa.

Embodiment 3

[0067] The preparation steps of the composite material are as follows:

[0068] The weight ratio of raw materials is: 40 parts of copolymerized polypropylene, 20 parts of homopolypropylene, 10 parts of talcum powder, 10 parts of barium sulfate, 5 parts of mica, 5 parts of graft compatibilizer, 0.5 parts of antioxidant, lubricant B 0.5 part of bisstearic acid amide (EBS), 0.5 part of nucleating agent, rare earth oxide Nd 2 o 3 1.0 servings.

[0069] (1) Add the above-mentioned raw materials in proportion to the high-speed mixer, and mix for 3 minutes;

[0070] (2) Put the mixed components into a parallel twin-screw extruder for melting, and simultaneously feed 10 parts of chopped glass fibers side by side, extrude and granulate, so as to obtain a composite material, wherein the barrel temperature of the extruder is: 220°C, the screw speed is 100r / min, the melt pressure is 1.5~2.5MPa, and the vacuum degree is -0.04~-0.1MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite material, a preparation method thereof and air conditioner workpieces. The composite material comprises the following materials, in parts by weight: 50-70 parts of polypropylene, 10-20 parts of chopped glass fibers, 20-30 parts of an inorganic filler, 5-10 parts of a graft compatilizer, 0.2-0.8 part of an antioxidant, 0.5-2.0 parts of a lubricant, 0.1-1.0 part of a nucleating agent, and 0.5-2.0 parts of a rare earth oxide. The composite material has a low linear expansion coefficient and excellent dimensional stability, when the air conditioner workpieces are prepared by adopting the composite material, noise caused by thermal expansion and cold contraction in an air conditioner usage process can be effectively avoided.

Description

technical field [0001] The invention relates to the technical field of plastics, in particular, the invention relates to a composite material, a preparation method thereof and an air conditioner. Background technique [0002] With the improvement of people's living standards, air conditioners have become a must-have for family life. They have the functions of adjusting indoor temperature and humidity and purifying the air. While bringing comfort to people, they also have the problem of noise pollution. [0003] Therefore, existing air-conditioning still needs to be improved. Contents of the invention [0004] The present invention proposes based on the inventor's discovery of the following problems and facts: [0005] The root cause of the noise of the indoor unit of the air conditioner is that the air conditioner parts (such as the chassis of the split machine, the volute tongue, the air outlet frame, the air duct assembly of the cabinet machine, the inner air outlet fra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L23/12C08L51/06C08L23/06C08K13/04C08K3/34C08K3/30C08K3/22C08K7/14C08K5/20
CPCC08L23/14C08L2205/02C08L2205/035C08L23/12C08L51/06C08L23/06C08K13/04C08K3/34C08K3/30C08K3/22C08K7/14C08K5/20
Inventor 麦剑章林勇强
Owner GD MIDEA AIR-CONDITIONING EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com