Environment-friendly anti-flaming fabric compound for motor vehicle interior and preparation method thereof

A technology for flame-retardant fabrics and motor vehicles, which is applied in the field of flame-retardant materials, can solve the problems such as the difficult limit oxygen index of polyurethane soft foam sponges, and achieve the effect of wide application and improvement of flame-retardant performance.

Active Publication Date: 2018-01-09
HANGZHOU XIANGJUN TEXTILE FLAME RETARDANT TECH
View PDF11 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In the case of increasingly severe fire safety situation, stricter requirements for flame retardant and environmental protection, and higher and higher raw material prices, especially when the prices of TDI and MDI raw materials for the preparation of polyurethane sponge fluctuate sharply and the safety and environmental protection situation of hazardous chemical isocyanate is severe Under the circumstances that it is difficult for the polyurethane soft foam sponge to greatly increase the limiting oxygen index and reduce the odor, the present invention is based on reducing the dependence on the polyurethane sponge, and provides an environmentally friendly flame-retardant fabric compound for motor vehicle interior decoration and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly anti-flaming fabric compound for motor vehicle interior and preparation method thereof
  • Environment-friendly anti-flaming fabric compound for motor vehicle interior and preparation method thereof
  • Environment-friendly anti-flaming fabric compound for motor vehicle interior and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] With 50 kilograms of fineness at 3 denier macromolecule main chain phosphorus-containing essential flame-retardant polyester copolyester staple fiber (permanent flame-retardant staple fiber product of Hangzhou Xiangjun Flame Retardant Technology Co., Ltd., phosphorus content is 0.65wt% , the limiting oxygen index is 31.9%) and 50 kg of PET staple fibers with a fineness of 3 deniers (the conventional polyester staple fiber products of Yizheng Chemical Fiber) are opened, carded, and laid into a fiber web, and then the fiber web is reinforced by a needle. Cloth, manufactured by needle-punching process, and pressed to produce a flame-retardant non-woven fabric with a thickness of 4.0 mm, an area density of 230 g / m2, and a bulk density of 57.5 kg / m3. The lining is The phosphorus content of the flame-retardant non-woven fabric is 0.325wt%, and the limiting oxygen index of the flame-retardant non-woven fabric, that is, the flame-retardant lining 2, is 26.7%;

[0053] 50 kg of ...

Embodiment 2

[0057] With 70 kilograms of fineness at 2 denier macromolecule backbone phosphorus-containing essential flame-retardant polyester copolyester staple fiber (permanent flame-retardant staple fiber product of Hangzhou Xiangjun Flame Retardant Technology Co., Ltd., phosphorus content is 0.70wt% , the limiting oxygen index is 32.9%) and 30 kg of PET fiber staple fibers with a fineness of 4 deniers (Yizheng Chemical Fiber’s conventional polyester staple fiber products) are opened, carded, and laid into a fiber web, and then the fiber web is reinforced by a needle Finished cloth, manufactured by needle-punching process, and pressed to produce a flame-retardant non-woven fabric with a thickness of 3.3 mm, an area density of 250 g / m2, and a bulk density of 72.0 kg / m3. The phosphorus content of the cloth is 0.49wt%, and the limiting oxygen index of the flame-retardant non-woven fabric, that is, the flame-retardant lining 2, is 29.1%;

[0058] 50 kg of flame-retardant lining 2 is placed ...

Embodiment 3

[0062]With 70 kilograms of fineness at 5 denier macromolecule main chain phosphorus-containing essential flame-retardant polyester copolyester staple fiber (permanent flame-retardant staple fiber product of Hangzhou Xiangjun Flame Retardant Technology Co., Ltd., phosphorus content is 0.68wt% , the limiting oxygen index is 32.5%) and 30 kg of PET fiber staple fibers with a fineness of 4 deniers (Yizheng Chemical Fiber’s conventional polyester staple fiber products) are opened, carded, laid into a fiber web, and then the fiber web is reinforced by a needle Finished cloth, manufactured by needle-punching process, and pressed to produce a flame-retardant non-woven fabric with a thickness of 3.3 mm, an area density of 250 g / m2, and a bulk density of 72.0 kg / m3. The phosphorus content of the cloth is 0.476wt%, and the limiting oxygen index of the flame-retardant non-woven fabric, that is, the flame-retardant lining 2, is 29.2%;

[0063] 50 kg of flame-retardant lining 2 is placed on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Basis weightaaaaaaaaaa
power levelaaaaaaaaaa
Login to view more

Abstract

The invention discloses an environmentally friendly flame-retardant fabric compound for motor vehicle interior decoration and a preparation method thereof, comprising a motor vehicle interior environment-friendly flame-retardant fabric and a flame-retardant lining, the two are compounded by flame, flame-retardant glue or flame-retardant heat Melt-adhesive compounding achieves tight bonding. The environmentally friendly flame-retardant composite fabric for motor vehicle interiors has dry cloth surface, green environmental protection, low smoke and less toxicity, low VOC, low atomization value, no peculiar smell, soft hand feeling, excellent flame-retardant performance, high peel strength, good resilience, Good antistatic performance and other characteristics, can be widely used in seats, safety seats, ceilings, door panels, handrails, etc.

Description

technical field [0001] The invention relates to the field of flame-retardant materials, in particular to an environmentally friendly flame-retardant fabric composite for motor vehicle interior decoration and a preparation method thereof. Background technique [0002] In recent years, motor vehicle combustion accidents have occurred frequently. Relevant national ministries and commissions issued a document pointing out that the combustion test standard of motor vehicle interior materials is one of the important factors to ensure the safety of motor vehicles. All countries have clear regulations on the flammability of automotive interior fabrics. my country has proposed new standards on the flame retardant performance requirements of school bus, passenger car and train interior fabrics. The horizontal combustion test index is changed from the original burning speed ≤ 100mm / min is reduced to ≤70mm / min. The flame retardant requirements of passenger car interior materials only r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B5/02B32B5/26D01F6/92D01F1/07D03D15/00D04H1/4382D04H1/46
Inventor 曾军蒋小云陈忠刚蒋义赏孟凡超吕佩佩刘清华唐俊毅
Owner HANGZHOU XIANGJUN TEXTILE FLAME RETARDANT TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap