Large bar induction tempering technology and large bar induction tempering production line

A bar induction and production line technology, applied in the field of steel bar production, can solve problems such as low strength of steel bars

Inactive Publication Date: 2018-01-16
江苏南钢通恒特材科技有限公司
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The first purpose of the present invention is to provide a large bar induction quenching a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Large bar induction tempering technology and large bar induction tempering production line
  • Large bar induction tempering technology and large bar induction tempering production line
  • Large bar induction tempering technology and large bar induction tempering production line

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] The technical solutions of the present invention will be clearly and completely described below in conjunction with the accompanying drawings. Obviously, the described embodiments are part of the embodiments of the present invention, rather than all of them. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative work shall fall within the protection scope of the present invention.

[0040] In the description of the present invention, it should be noted that the terms "center", "upper", "lower", "left", "right", "vertical", "horizontal", "inner", "outer", etc. The indicated orientation or positional relationship is based on the orientation or positional relationship shown in the drawings, and is only for the convenience of describing the present invention and simplifying the description, rather than indicating or implying that the pointed device or element must have a specific orientation or a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of steel bar production, in particular to a large bar induction tempering technology and a large bar induction tempering production line. The large bar induction tempering technology comprises the steps as follows: the curvature of a raw material of rolled steel bars is inspected, the raw material of the steel bars is continuously moved on a conveying roller table and conveyed to a multi-stage induction heating zone, the steel bars subjected to multi-stage induction heating are conveyed to a quenching device for quenching, the quenched steel bars are conveyed to a multi-stage tempering induction heating zone, the tempered steel bars are conveyed to a blanking cold bed for natural cooling, and the cooled steel bars are packaged and stored. The steel bars are driven by the conveying roller table to move forwards continuously, so that the steel bars are gradually heated stage by stage, the induction heating tempering quality of the steel bars is improved, bending deformation is small, the steel bars are moved slowly while being treated, the steel bars are uniformly heated and cooled and has uniform hardness, metallographic structure and mechanical performance and small scattering difference. The large bar induction tempering production line has the advantages as compared with the prior art.

Description

Technical field [0001] The present invention relates to the technical field of steel rod production, in particular to a large-bar induction quenching and tempering process and a large-bar induction quenching and tempering production line. Background technique [0002] In the current material 4141MOD-1, steel bar with diameter 61 quenching and tempering process, general manufacturers adopt flame furnace, box furnace, pit furnace as quenching and tempering process, due to the heating method of flame furnace, box furnace and pit furnace The limitations of this method cannot fully meet the performance requirements of 10.9 high-strength fasteners; this causes premature failure of parts during use and reduces the service life of high-strength fasteners. [0003] Therefore, providing a large-bar induction quenching and tempering process and a large-bar induction quenching and tempering production line with high strength of steel bars has become an important technical problem to be solved ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D9/00C21D1/25C21D1/42C21D1/62
CPCY02P10/25
Inventor 鲍新城门强蒋振
Owner 江苏南钢通恒特材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap