Duplex-phase golf club head titanium alloy

A technology for golf club heads and titanium alloys, which is applied in the field of titanium alloys for duplex golf club heads, and can solve problems affecting the characteristics of the ball head

Active Publication Date: 2018-01-30
O TA PRECISION IND
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] Therefore, different microstructures will affect the characteristics of the ball head

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Duplex-phase golf club head titanium alloy
  • Duplex-phase golf club head titanium alloy
  • Duplex-phase golf club head titanium alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033]In order to make the above-mentioned and other objects, features and advantages of the present invention more obvious and easy to understand, the preferred embodiments of the present invention will be exemplified below and described in detail in conjunction with the accompanying drawings. Furthermore, the directional terms mentioned in the present invention, such as up, down, top, bottom, front, rear, left, right, inner, outer, side, surrounding, center, horizontal, lateral, vertical, longitudinal, axial, Radial, uppermost or lowermost, etc., are only directions with reference to the attached drawings. Also, references to the singular forms "a", "an" and "the" herein include plural references unless the context clearly dictates otherwise. The numerical range (such as 10% to 11% of A) includes upper and lower limits unless otherwise specified (ie 10%≦A≦11%); if the numerical range does not define the lower limit (such as B below 0.2%) , or B) below 0.2%, it means that th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a duplex-phase golf club head titanium alloy, which contains 6.0-7.5 wt% of aluminum, 1.5-2.5 wt% of vanadium, 1.5-2.5 wt% of chromium, 0.1-0.5 wt% of iron, 1.5-2.5 wt%of tin, 1.5-2.5 wt% of zirconium, 0.1-0.5 wt% of silicon, and other trace elements inevitable in an alloy material manufacturing process and with the ratio by using titanium as a base material. According to the present invention, after the duplex-phase golf club head titanium alloy is subjected to 780-840 DEG C plastic processing and heat treatment, the alloy structure with the alpha phase and the beta phase can be obtained; and due to the combination of the multiple alloying elements, the subgrain and high-density differential arrangement structure is generated in the alloy matrix, and the trace amount of the fine omega-phase precipitate can be formed, such that the duplex-phase golf ball bar head titanium alloy can have the tensile strength of 1300-1450 MPa, have the yield strength of 1250-1400 MPa, and the elongation of 6-12% so as to improve the design space of the golf club head structure.

Description

technical field [0001] The present invention relates to a duplex phase golf club head titanium alloy comprising: 6.0 to 7.0 wt % aluminum, 1.5 to 2.5 wt % tin, 1.5 to 2.5 wt % zirconium, 1.5 to 2.5 wt % % vanadium, 1.5 to 2.5 wt % chromium, 0.1 to 0.5 wt % iron, 0.05 to 0.20 wt % silicon. After proper plastic working and heat treatment, the basic microstructure of the alloy is bimodal, with the characteristics of secondary grains and high density dislocation, as well as a small amount of ω-phase precipitates. Background technique [0002] In golf equipment, several clubs for different purposes are classified into wooden clubs, irons and putters according to their functions. The clubs for different uses are made of various alloy materials. Among them, 3-5 wood heads, 7-8 iron heads, 1 pitching head (PW), 1 sand pit head (SW), and 1 putter 1 putter. It is described as follows: [0003] 1. Wood head: The wood head is mainly based on the driver, which is required to play far...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C14/00C22F1/18
Inventor 常传贤赵志烨曲湾湾
Owner O TA PRECISION IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com