Material used for preparing brush for motor of treadmill

A treadmill and brush technology, applied in circuits, current collectors, electrical components, etc., can solve the problems of inability to meet the lifespan of treadmill brushes, poor stability, and high noise, and achieve low electrical noise, high stability, and noise. low effect

Inactive Publication Date: 2018-02-06
SUZHOU DONSUN CARBONWARE CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, at present, domestic brushes generally have high electrical noise and poor stability in operation, and domestic carbon brush factories cannot meet the requirements of long life, low noise and stability of treadmill motor brushes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material used for preparing brush for motor of treadmill
  • Material used for preparing brush for motor of treadmill
  • Material used for preparing brush for motor of treadmill

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] 1. Prepare materials (parts) according to the following proportions by weight:

[0047]

[0048] Wherein, the additive is one or a combination of molybdenum disulfide, tungsten disulfide, and aluminum phosphate; the binder is selected from bisphenol A epoxy resin, and its epoxy value is 0.25-0.45; the curing agent is selected from epoxy resin Latent curing agent T-31 curing agent (Changzhou Shanfeng Chemical Co., Ltd.).

[0049] 2. Prepare the raw material mixture by electric brush

[0050] Put natural graphite, artificial graphite, flexible graphite, talcum powder, graphene, additives, and curing agent in the kneading pot, turn on the rotating device of the kneading pot, and stop mixing at room temperature for 1.5 hours to obtain matrix powder; Dissolve phenol A type epoxy resin in acetone, stir and mix evenly to dissolve, and prepare binder solution; add binder solution to matrix powder and stir, mix well, stir for 1.5h, mix well and take out The materials are pl...

Embodiment 2

[0060] 1. Prepare materials according to the following proportions by weight (parts):

[0061]

[0062] Wherein, the additive is one or a combination of molybdenum disulfide, tungsten disulfide, and aluminum phosphate; the binder is selected from bisphenol A epoxy resin, and its epoxy value is 0.25-0.45; the curing agent is selected from epoxy resin Latent curing agent T-31 curing agent (Changzhou Shanfeng Chemical Co., Ltd.).

[0063] 2. Prepare the raw material mixture by electric brush

[0064] Put natural graphite, artificial graphite, flexible graphite, talcum powder, graphene, additives, and curing agent in the kneading pot, turn on the rotating device of the kneading pot, and stop mixing at room temperature for 1.5 hours to obtain matrix powder; Dissolve phenol A type epoxy resin in acetone, stir and mix evenly to dissolve, and prepare binder solution; add binder solution to matrix powder and stir, mix well, stir for 1.5h, mix well and take out The materials are pl...

Embodiment 3

[0074] 1. Prepare materials according to the following proportions by weight (parts):

[0075]

[0076]

[0077] Wherein, the additive is one or a combination of molybdenum disulfide, tungsten disulfide, and aluminum phosphate; the binder is selected from bisphenol A epoxy resin, and its epoxy value is 0.25-0.45; the curing agent is selected from epoxy resin Latent curing agent T-31 curing agent (Changzhou Shanfeng Chemical Co., Ltd.).

[0078] 2. Prepare the raw material mixture by electric brush

[0079] Put natural graphite, artificial graphite, flexible graphite, talcum powder, graphene, additives, and curing agent in the kneading pot, turn on the rotating device of the kneading pot, and stop mixing at room temperature for 1.5 hours to obtain matrix powder; Dissolve phenol A type epoxy resin in acetone, stir and mix evenly to dissolve, and prepare binder solution; add binder solution to matrix powder and stir, mix well, stir for 1.5h, mix well and take out The mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Bulk densityaaaaaaaaaa
Wear rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a material used for preparing a brush for a motor of a treadmill. The brush comprises a matrix powder material and a binder, the ratio of the parts by weight of the matrix powder material to the binder is 5-7.5:1-2, the matrix powder material comprises graphite, flexible graphite powder, talcum powder and graphene, the ratio of the parts by weight of the graphite to the flexible graphite powder to the talcum powder to the graphene is 70-95:1-3:2-4:0.5-2, and the matrix powder material also comprises additives and curing agents. According to the brush prepared by employing the material, the resistivity is moderate, the wear resistance is good, the commutation performance is good, and the spark grade is low; and more importantly, the noise is low, and the product stability is good.

Description

technical field [0001] The invention relates to a material used for preparing electric brushes for treadmill motors, in particular to a material for preparing electric brushes for low-noise treadmill motors, belonging to the field of motors. Background technique [0002] The brush is a conductive part used in the motor to contact the commutator or slip ring, and is one of the important components of the motor. As a sliding contact body that imports and exports current, it has good electrical, thermal and lubricating properties, and has a certain mechanical strength and the instinct to suppress commutation sparks. Almost all DC motors, as well as commutated motors, use brushes. [0003] With the development of science and technology, the types of motors and the working conditions of use are becoming more and more diverse, so various types of brushes are required to meet the various requirements of the motor, so the types of brushes also follow the motor industry. developmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More