A clean and glazed technology, applied in the field of high-clean glaze, can solve the problems of threatening the health of operators, long clarifying time, polluting the environment, etc., and achieve the effect of improving rigidity, improving performance and service life, and good cleanliness

Inactive Publication Date: 2018-02-09
新沂市港发商贸有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Currently commonly used clarifiers include cerium dioxide, white arsenic, etc., but white arsenic is a highly toxic substance that threatens the health of operators and se

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example: A high-clean glass made of the following raw materials by weight: 40-50 parts of quartz sand, 10-20 parts of co-solvent, 5-10 parts of oxidizing agent, 15-20 parts of clarifying agent, and 5-10 parts of coloring agent Parts, 2-3 parts of fluorescent whitening agent, 5-8 parts of enhancer, 2-5 parts of binder, 1-2 parts of suspending agent and 1-2 parts of coloring auxiliary;

[0019] The sum of the three addition proportions of the quartz sand, the co-solvent and the clarifying agent accounts for 55-70% of the total weight parts, the colorant, the fluorescent whitening agent, the enhancer and the The addition ratio of the four binders accounts for 15-20% of the total mass parts;

[0020] The binder includes 2-5 parts by weight of amino acids, 2-5 parts by weight of phenolic resin, and 2-3 parts by weight of organic bentonite.

[0021] The colorant includes: 1-2 parts by weight of copper oxide, 2-3 parts by weight of cuprous oxide, and 3-6 parts by weight of dicobalt ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-clean glass, which is made of the following raw materials in parts by weight: 40-50 parts of quartz sand, 10-20 parts of cosolvent, 5-10 parts of oxidizing agent, 15-20 parts of clarifying agent, and 5-20 parts of coloring agent 10 parts, 2-3 parts of fluorescent whitening agent, 5-8 parts of reinforcing agent, 2-5 parts of binder, 1-2 parts of suspending agent and 1-2 parts of coloring aid; quartz sand, co-solvent and clarifying agent The sum of the three addition ratios accounts for 55-70% of the total parts by weight, and the sum of the four addition ratios of the coloring agent, fluorescent whitening agent, reinforcing agent and binder accounts for 15-20% of the total parts by weight; The agent comprises 2-5 parts by weight of amino acid, 2-5 parts by weight of phenolic resin and 2-3 parts by weight of organic bentonite. The invention is not only non-toxic and harmless, but also has good cleanliness, and the glaze has high rigidity, stability and strength, and long practical life.

Description

technical field [0001] The invention belongs to the technical field of colored glaze, in particular to a kind of high-clean colored glaze. Background technique [0002] Glass is a silicate product with a long history. Its quality is crystal clear, which fully reflects the delicacy, delicacy and subtlety of the oriental people. The main components of glass are silica, alumina, flux and pigments. [0003] Glass has excellent characteristics such as low softening point and long material properties, so it is easy to manufacture and suitable for glass forming. The quality of glass products is reflected in good luster, less air bubbles, streaks, and stones. The softening point and material properties of colored glaze mainly depend on the types and proportions of the ingredients in the colored glaze formula, and adding clarifiers to the basic components of colored glaze can reduce the melting temperature of colored glaze, improve the melting quality, and avoid defects such as bubbl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C1/00C03C1/04C03C4/02C03C14/00C03C6/04
CPCC03C4/02C03C1/00C03C1/004C03C1/04C03C14/002
Inventor 张永志
Owner 新沂市港发商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap