White carbon black adsorption environment-friendly waterborne polyurethane mat

A water-based polyurethane, silica technology, applied in polyurea/polyurethane coatings, coatings, textiles and papermaking, etc., to achieve the effect of good air permeability, high production efficiency and good hand feeling

Inactive Publication Date: 2018-02-09
遂昌玄乐炭复合材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] "Nanchang University" 2011 master's thesis "Exploration of Aqueous Polyurethane Acid Bath Coagulation Film Formation" paper discloses the use of acetic acid to foam water-based polyurethane emulsion to prepare synthetic leather, but also discloses that the surface and cross-section of WPU acid bath demulsification method have There are many microporous structures, among which the microporous structure without wood powder is richer than that with added wood powder, but no matter which one, compared with the solvent-based PU wet method, the microporous structure is still quite different. Therefore, WPU acid bath demulsification method needs further research from theory to practice

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White carbon black adsorption environment-friendly waterborne polyurethane mat

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

margin

[0044] A kind of production method of environment-friendly type imitation leather water-based polyurethane cushion, this method comprises the following steps:

[0045] 1) Soak the polar fleece cloth with bamboo vinegar solution before scraping, the pH of the bamboo vinegar solution is 3.5, soak the polar fleece cloth with bamboo vinegar solution, and then squeeze dry;

[0046] 2) Scratch the above-mentioned water-based polyurethane coating on the fleece cloth, solidify on the surface of the fleece cloth to form a water-based polyurethane layer, and squeeze it dry;

[0047] 3) After being squeezed dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2, and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0048] 4) After foaming, wash with water and dry to obtain the water-based polyurethane mat.

[0049] Adopt the above-mentioned...

Embodiment 2

margin

[0096] A kind of production method of environment-friendly type imitation leather water-based polyurethane cushion, this method comprises the following steps:

[0097] 1) Soak the polar fleece cloth with bamboo vinegar solution before scraping, the pH of the bamboo vinegar solution is 3.5, soak the polar fleece cloth with bamboo vinegar solution, and then squeeze dry;

[0098] 2) Scratch the above-mentioned water-based polyurethane coating on the fleece cloth, solidify on the surface of the fleece cloth to form a water-based polyurethane layer, and squeeze it dry;

[0099] 3) After being squeezed dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2, and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0100] 4) After foaming, wash with water and dry to obtain the water-based polyurethane mat.

[0101] The water-based polyureth...

Embodiment 3

margin

[0111] A kind of production method of environment-friendly type imitation leather water-based polyurethane cushion, this method comprises the following steps:

[0112] 1) Soak the polar fleece cloth with bamboo vinegar solution before scraping, the pH of the bamboo vinegar solution is 3.5, soak the polar fleece cloth with bamboo vinegar solution, and then squeeze dry;

[0113] 2) Scratch the above-mentioned water-based polyurethane coating on the fleece cloth, solidify on the surface of the fleece cloth to form a water-based polyurethane layer, and squeeze it dry;

[0114] 3) After being squeezed dry, enter the bamboo vinegar solution for foaming. The pH of the bamboo vinegar solution is 3.2, and the foaming time is 2 minutes to form a porous polyurethane coating. The coating amount of the water-based polyurethane layer is 40g / m 2 ;

[0115] 4) After foaming, wash with water and dry to obtain the water-based polyurethane mat.

[0116] The water-based polyureth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of mat, and especially relates to a white carbon black adsorption environment-friendly waterborne polyurethane mat. The white carbon black adsorption environment-friendly waterborne polyurethane mat is prepared via foaming with bamboo vinegar; tensile strength, tearing strength, and wear resistance are capable of reaching that of DMF wet foaming method; and obtained finished products possess advantages such as excellent handfeel, fine texture, and excellent permeability. No DMP is used in the whole production process; water is adopted as a solvent; flame resistance, safety, environment-friendly performance, and low cost are achieved. No formaldehyde or DMF is detected in the obtained white carbon black adsorption environment-friendly waterborne polyurethane mat, and requirement on environment-friendly waterborne polyurethane mats is satisfied.

Description

technical field [0001] The invention relates to the field of mats, in particular to a white carbon black adsorption and environment-friendly water-based polyurethane mat. Background technique [0002] Most of the existing high molecular polymer mats (or pads, gaskets) are made of plastic (such as PVC) and rubber materials. They are generally made by one-time integral injection molding or vulcanization, and the products made are resistant to low temperature. Poor performance, easy to harden and crack, feel astringent; production process of finished products is more, easy to cause dirty production environment, heavy odor, some raw materials (such as PVC) long-term close contact with human body will also affect human health, and, due to plastic The nature of the product determines that the product is easy to age, has poor wear resistance, and has a short service life. [0003] Polyurethane synthetic leather has soft and natural luster, soft hand feeling and strong genuine leat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/14C09D7/61C09D175/04D06M15/01
CPCD06N3/004C08K2003/2241C08K2003/265C08K2201/011C08L2205/035C09D175/04D06M15/01D06N3/0059D06N3/0063D06N3/14D06N2209/1671C08L97/02C08K13/02C08K3/36C08K3/26C08K3/22
Inventor 管宁章管玄谢永水
Owner 遂昌玄乐炭复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap