Pearlescent PVC (Polyvinyl Chloride) thin film and preparation method thereof

A PVC film and pearlescent technology, applied in the field of pearlescent PVC film and its preparation, can solve the problems of low high-end market competitiveness, poor dispersion of raw materials, and difficult to control product quality, and achieve the effect of improving matte effect and low cost

Inactive Publication Date: 2018-02-16
FOSHAN WEIMING PLASTICS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, the production process of pearlescent PVC film is to add pearlescent powder, but this method is not environmentally friendly, and the dispersion of raw materials is poor, the product quality is difficult to control, and the high-end market competitiveness is not strong

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A pearlescent PVC film, specifically prepared by the following components in parts by mass: 60 parts of Type 5 PVC, 10 parts of Type 7 PVC, 8 parts of fiber powder, 2 parts of ESO, 3 parts of calcium carbonate, 1.5 parts of BS-105 1 part, 0.5 part of 1203, 0.1 part of 8775, 0.05 part of 2147, 0.2 part of 736A, 1 part of titanate, 1 part of ACR-401, 1 part of CPE; among them, ESO is a non-toxic plasticizer and stabilizer for polyvinyl chloride, BS -105 is thermoplastic acrylic resin, 1203, 8775 and 2147 are pigments, 736A is powder stabilizer, ACR-401 is acrylate processing aid, CPE is chlorinated polyethylene resin.

[0016] The preparation method specifically includes the following steps: mixing and stirring-filtering and extruding-calendering forming-cooling and shaping-finished product winding;

[0017] Further, the fiber powder, its preparation method, specifically the following steps:

[0018] (1) In terms of parts by mass, take 5 parts of bagasse and 15 parts of ...

Embodiment 2

[0024] A pearlescent PVC film, specifically prepared by the following components in parts by mass: 80 parts of Type 5 PVC, 30 parts of Type 7 PVC, 10 parts of fiber powder, 3 parts of ESO, 5 parts of calcium carbonate, 2.5 parts of BS-105 1 part, 1 part of 1203, 0.2 part of 8775, 0.01 part of 2147, 0.4 part of 736A, 2 parts of titanate, 2 parts of ACR-401, 3 parts of CPE; the preparation method is as follows: mixing and stirring-filtering and extruding- Calendering - cooling and shaping - finished product winding;

[0025] Further, the fiber powder, its preparation method, specifically the following steps:

[0026] (1) In terms of parts by mass, 8 parts of bagasse and 20 parts of rice straw were dried and crushed, then 120 parts of aqueous sodium hydroxide solution with a mass fraction of 15% was added, heated to 80-90° C., and soaked in heat for 60 minutes;

[0027] (2) Filtrate to obtain the filter residue A, wash the filter residue A with clear water, add 5 times the water...

Embodiment 3

[0032] A pearlescent PVC film, specifically prepared by the following components in parts by mass: 70 parts of Type 5 PVC, 20 parts of Type 7 PVC, 9 parts of fiber powder, 2.5 parts of ESO, 4 parts of calcium carbonate, 2 parts of BS-105 Part, 0.8 part of 1203, 0.15 part of 8775, 0.008 part of 2147, 0.3 part of 736A, 1.5 parts of titanate, 1.5 parts of ACR-401, 2 parts of CPE; the preparation method is as follows: mixing and stirring-filtering and extruding- Calendering - cooling and shaping - finished product winding;

[0033] Further, the fiber powder, its preparation method, specifically the following steps:

[0034] (1) In terms of parts by mass, take 6 parts of bagasse and 18 parts of rice straw, dry them and break them into pieces, add 110 parts of aqueous sodium hydroxide solution with a mass fraction of 15%, heat to 80-90° C., and heat-preserve and soak for 50 minutes;

[0035] (2) Filtrate to obtain the filter residue A, wash the filter residue A with clear water, ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a pearlescent PVC (Polyvinyl Chloride) thin film. The pearlescent PVC thin film is prepared from the following components in parts by mass: 60 to 80 parts of 5 type PVC, 10 to30 parts of 7 type PVC, 8 to 10 parts of fiber powder, 2 to 3 parts of ESO, 3 to 5 parts of calcium carbonate, 1.5 to 2.5 parts of BS-105, 0.5 to 1 part of 1203, 0.1 to 0.2 part of 8775, 0.005 to 0.01 part of 2147, 0.2 to 0.4 part of 736A, 1 to 2 parts of titanate, 1 to 2 parts of ACR-401 and 1 to 3 parts of CPE. According to the preparation method of the pearlescent PVC thin film disclosed by the invention, by adding the fiber powder, the pearlescent PVC thin film has the advantages of environment friendliness, health, low cost and capability of effectively improving the matte effect of thePVC thin film, so that the product is more upscale and beautiful; in addition, the pearlescent PVC thin film cooperates with a pearlescent material, so that the reflection of the pearlescent materialunder light irradiation is more dazzling; and furthermore, the pearlescent PVC thin film is worthy of being promoted.

Description

technical field [0001] The invention belongs to the technical field of polymer compounds, and in particular relates to a pearlescent PVC film and a preparation method thereof. Background technique [0002] The main component of PVC film is polyvinyl chloride, and other components are added to enhance its heat resistance, toughness, ductility, etc. PVC film is a kind of synthetic material that is loved, popular and widely used in the world today. The global usage of PVC film ranks second among various synthetic materials. Among the materials that can produce three-dimensional surface films, PVC is the most suitable material. [0003] In the prior art, the production process of pearlescent PVC film is to add pearlescent powder, but this method is not environmentally friendly, and the dispersion of raw materials is poor, the product quality is difficult to control, and the high-end market competitiveness is not strong. Contents of the invention [0004] In order to solve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L1/02C08L33/04C08L23/28C08K13/02C08K3/26C08J5/18
CPCC08L27/06C08J5/18C08J2327/06C08J2427/06C08K2003/265C08L2203/16C08L2205/025C08L2205/035C08L1/02C08L33/04C08L23/286C08K13/02C08K3/26
Inventor 李永平
Owner FOSHAN WEIMING PLASTICS
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com