Bridge support mortar foundation material taking cement and gypsum as bottom materials and preparation method thereof

A technology for bridge bearing mortar and basic materials, applied in the field of building materials, can solve the problems of complex materials and high cost, and achieve the effect of simple materials and low cost

Inactive Publication Date: 2018-03-13
芜湖铁路桥梁制造有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1:

[0024] A bridge bearing mortar base material with cement as the base material, the total weight of the bridge bearing base material is 1000kg, and the weight ratio of each component is cement: gypsum: expansion agent: water reducing agent: water retention agent: early strength type Admixture: retarder: defoamer = 20:5:2:0.1:0.1:0.01:0.2:0.01.

[0025] Among them, cement is Portland cement; expansion agent is concrete expansion agent; water reducer is conventional lignosulfonate water reducer; water retention agent is polyacrylamide; early strength admixture is nitrite; The agent is a conventional retarder; the defoamer is polydimethylsiloxane.

Example Embodiment

[0026] Example 2:

[0027] A bridge bearing mortar base material with cement as the base material, the total weight of the bridge bearing base material is 1500kg, and the weight ratio of each component is cement: gypsum: expansion agent: water reducing agent: water retention agent: early strength type Admixture: retarder: defoamer = 40:8:10:0.8:0.8:0.08:1:0.05.

[0028] Cement is aluminate cement; expansion agent is concrete expansion agent; water reducing agent is naphthalene series superplasticizer; water retention agent is sodium polyacrylate; early strength admixture is chromate; defoamer is polyoxyethylene Glyceryl ether.

Example Embodiment

[0029] Example 3:

[0030] A bridge bearing mortar base material with cement as the base material, the total weight of the bridge bearing base material is 2000kg, and the weight ratio of each component is cement: gypsum: expansion agent: water reducing agent: water retention agent: early strength type Admixture: retarder: defoamer = 30:10:8:0.5:0.5:0.05:0.8:0.03.

[0031] Cement is phosphate cement; expansion agent is concrete expansion agent; water reducer is polycarboxylate superplasticizer; water retention agent is starch grafted acrylate; early strength admixture is calcium formate; Oxyethylene polyoxypropylene pentaerythritol ether.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bridge support mortar foundation material taking cement and gypsum as bottom materials and a preparation method thereof. The bridge support foundation material is prepared from the following components in parts by weight: 20 to 40 parts of the cement, 5 to 10 parts of the gypsum, 2 to 10 parts of an expanding agent, 0.1 to 0.8 part of a water reducing agent, 0.1 to 0.8 part of a water retaining agent, 0.01 to 0.08 part of an early strength type additive, 0.2 to 1 part of a retarder and 0.01 to 0.05 part of a de-foaming agent. In the second aspect, the preparation method of the bridge support mortar foundation material, provided by the invention, comprises the step of uniformly mixing all the components according to the formula. The bridge support mortar foundationmaterial disclosed by the invention has the beneficial effects of simple materials and low cost.

Description

technical field [0001] The invention belongs to the field of building materials, and more specifically relates to a bridge support mortar base material with cement and gypsum as base materials and a preparation method thereof. Background technique [0002] Bridge bearings are important structural components connecting the bridge superstructure and substructure. It can reliably transmit the reaction force and deformation (displacement and rotation angle) of the bridge superstructure to the bridge substructure, so that the actual stress of the structure is consistent with the calculated theoretical diagram. [0003] Chinese patent CN 104370511 B discloses bridge support mortar and its production method. The bridge support mortar includes the following raw materials in parts by weight: 45-60 parts of graded quartz sand, 30-40 parts of 42.5 sulfoaluminate cement , 5-15 parts of 42.5 ordinary silicon cement, 1-10 parts of U-type expansion agent, 0.1-1 part of water-reducing agen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/34C04B28/04C04B28/06
CPCC04B28/04C04B28/06C04B28/34C04B22/143C04B2103/302C04B2103/465C04B2103/22C04B2103/50C04B2103/12
Inventor 陈辰杨明黄海峰
Owner 芜湖铁路桥梁制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap